An approach to measure infill matric suction of irregular infilled rock joints under constant normal stiffness shearing

Rock joints infilled with sediments can strongly influence the strength of rock mass. As infilled joints often exist under unsaturated condition, this study investigated the influence of matric suction of infill on the overall joint shear strength. A novel technique that allows direct measurement of matric suction of infill using high capacity tensiometers (HCTs) during direct shear of infilled joints under constant normal stiffness (CNS) is described. The CNS apparatus was modified to accommodate the HCT and the procedure is explained in detail. Joint specimens were simulated by gypsum plaster using three-dimensional (3D) printed surface moulds, and filled with kaolin and sand mixture prepared at different water contents. Shear behaviours of both planar infilled joints and rough joints having joint roughness coefficients (JRCs) of 8–10 and 18–20 with the ratios of infill thickness to asperity height (t/a) equal to 0.5 were investigated. Matric suction shows predominantly unimodal behaviour during shearing of both planar and rough joints, which is closely associated with the variation of unloading rate and volumetric changes of the infill material. As expected, two-peak behaviour was observed for the rough joints and both peaks increased with the increase of infill matric suction. The results suggest that the contribution of matric suction of infill on the joint peak normalised shear stress is relatively independent of the joint roughness.     

Research on hydrophobicity of electrospun Fe3O4/PVDF nanofiber membranes under different preparation conditions

Abstract

Preparation condition can affect the structure and the properties of nanofiber membrane. In order to explore suitable conditions to prepare the Fe₃O₄/PVDF nanofiber membrane with good hydrophobicity, the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes obtained by electrospinning was investigated by changing preparation conditions like weight percentage of Fe₃O₄ nanoparticles, blending quality concentration of poly (vinylidene fluoride) (PVDF) and Fe₃O₄ nanoparticles, and positive voltage. And the variations of hydrophobicity of Fe₃O₄/PVDF nanofiber membranes modified by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane were studied. The results show that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has changed under different preparation conditions. The contact angles of samples increased after a modification by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane, which indicates that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has been enhanced.     

Novel thermal-sensitive properties of NBT-BZT composite ceramics for high-temperature NTC thermistors

We found for the first time that (1 − x) Na_0.5Bi_0.5TiO₃-xBiZn_0.5Ti_0.5O₃ (NBT–BZT) composite ceramics showed negative temperature coefficient (NTC) at a high temperature. The NBT–BZT nanopowders were successfully prepared by Pechini method. Their ceramics were sintered at 1100°C. The NBT–BZT ceramic exhibited a good linear relationship between logarithm of electrical resistivity (Inρ) and reciprocal of absolute temperature (1000/T) at 250°C–1050°C. The obtained ρ₆₀₀, ρ₉₀₀, and B_600/900 constants of the NBT–ZBT NTC thermistors are approximately 5.92 × 10⁶ to 3.01 × 10⁴ Ω cm, 7.03 × 10³ to 7.60 × 10² Ω cm and 2.3 × 10⁴-1.3 × 10⁴ K, respectively. The electrical characteristics can be tuned to the desired value by changing the Na_0.5Bi_0.5TiO₃ content in the compound. The electrical conductivity in these compounds is due to the electron jumps between Ti³⁺ and Ti⁴⁺ and oxygen-ion conductivity. Results demonstrate a tremendous potential of the studied system for perovskite materials with NTC performance.     

铝碳质长水口用低铝抗氧化涂层的研制

为抑制铝碳质长水口使用过程中石墨的氧化，其表面会涂覆含 20%~30%Al₂O₃的抗氧化涂层，但切割丝钢等特种钢冶炼过程必须严格控制钢液中夹杂的 Al₂O₃的含量，因此需要制备低氧化铝含量的抗氧化涂层。本文通过调节涂料组成、加水量和水玻璃加入量制备了低铝抗氧化涂层，并利用扫描电镜分析了抗氧化实验后试样断口的显微结构。结果表明：以粘土粉、钾长石粉和硅砂为主要原料，添加 10%硼砂的涂料可在 800 ℃形成良好的釉层，此时涂料中 A12O3的含量可降至 12%，得到了低铝涂料；当加入占涂料质量 80%的水和 40%的水玻璃时，涂层具有最佳的涂覆性能和抗氧化性能，涂层和长水口基体结合致密，保护了长水口中的石墨不被氧化。     

X70配套埋弧焊丝用H08D盘条的研制

介绍了北营公司X70配套埋弧焊丝用H08D盘条的开发研制情况.其生产工艺的关键点为:转炉采用“双渣法除磷”,脱氧合金化在转炉和LF炉两个阶段完成,连铸采用结晶器电磁搅拌及末端电磁搅拌、恒定拉速;盘条采用控冷控轧及轧后延迟型斯太尔摩冷却工艺等措施.生产的成品盘条成分、力学性能、金相组织等指标均满足客户拉拔工艺要求.     

A facile method for preparation of PGS@ZB‐N and gas‐sol alternating synergistic effect for fire resistance of EVA

Through the simple precipitation of palygorskite (PGS) by zinc borate (ZB) (to make PGS@ZB) and the decoration of PGS@ZB by dodecylamine (N), a novel organic‐inorganic@inorganic hybrid flame retardant of PGS@ZB‐N was prepared and was incorporated with ethylene vinyl acetate copolymer (EVA) to improve its flame retardance. The structure and morphology of PGS@ZB‐N were characterized by Fourier transform infrared (FTIR) spectroscopy, X‐ray diffraction (XRD), and scanning electron microscopy (SEM), and it was confirmed that the PGS@ZB‐N hybrid had been successfully prepared. The flame retardancy and burning behavior of EVA/PGS@ZB‐N/EG (EG = expandable graphite) composite were studied through thermogravimetric analysis (TGA), limiting oxygen index (LOI), UL‐94 (by the vertical burning test), and cone calorimeter test (CCT) characterizations. The prepared EVA/PGS@ZB‐N/EG composite obtained an LOI value of 41.2% with the addition of 30 wt% PGS@ZB‐N/EG. It was found that EVA/PGS@ZB‐N/EG was protected through a gas phase and condensed phase alternating synergistic effect mechanism.     

面向过程装备工程师培养的O2O课程体系构建

过程装备与控制工程专业的人才培养方案及课程体系可以划分为线上和线下两块。线上课程侧重于新知识传授,有助于学生开阔眼界,活跃思维,启迪智慧;线下课程侧重于基本知识传授,有助于学生夯实专业基础,培养专业素养,锻炼工程技能。研究线上和线下课程的主辅关系及交互模式,形成具有鲜明流程工业装备特征的“线上+线下”一体化课程群,建立培养效果(达成度)的评价方法与持续改进机制,有利于培养掌握综合知识、善于设计计算、了解制造检验的优秀过程装备工程师。