Cyclic oxidation behaviors of MoSi<Subscript>2</Subscript> with different relative density

The influence of different relative density on the cyclic oxidation behaviors of MoSi2 at 1 273 K were studied. ＂Pesting＂ was not found in all MoSi2 materials after being oxidized for 480 h. All samples exhibited continuous mass gain during the oxidation process. The mass gains of MoSi2 with the lowest relative density （78.6%） and the highest relative density （94.8%） are increased by 8.15 mg·cm^-2 and 3.48 mg·cm^-2, respectively. The surface of the material with lower relative density formed a loose, porous and discontinuous oxidation scale, which accelerated oxygen diffusion and aggravated the oxidation process. However, a dense scale in the material with higher relative density is formed, which acts a diffusion barrier to the oxygen atoms penetrating into the matrix. The high temperature oxidation resistance of MoSi2 can be improved by increasing its relative density.     

油润滑下MoSi2材料的摩擦磨损性能

运用M-200型摩擦磨损试验机测定了油润滑条件下MoSi2与45调质钢、45淬火钢和CrWMn钢配对时的摩擦磨损性能，采用扫描电镜和微探针分析了摩擦副表面的形貌，探讨了磨损机理：结果表明：采用20号机械油润滑可有效地降低MoSi2材料的磨损率及摩擦因数；与低硬度的45调质钢和45淬火钢对摩时，MoSi2材料的主要磨损机制为晶间断裂、疲劳断裂、轻微粘着磨损和磨粒磨损；MoSi2材料与高硬度的CrWMn钢对摩时，主要磨损机制表现为粘着磨损、微犁削式磨粒磨损，并在偶件表面材料凸点的前端形成楔块。     

45号钢表面化学镀镍磷合金

在45号钢表面化学镀镍磷合金，获得含磷10％（质量分数）的镍磷合金镀层，比较了其与2Cr13不锈钢的耐磨性及在不同腐蚀介质中的耐蚀性，结果表明，含磷10％的镍磷合金层的耐磨，耐蚀性均优于2Cr13不锈钢。     

微量镁对Mo-Si混合粉末机械合金化的影响

采用X射线衍射(XRD) 和扫描电子显微镜(SEM)测试方法研究了Mg含量为6%和12%的Mo-Si-Mg混合粉末在球磨过程中相的演变规律、组织形貌以及热处理对球磨粉末的影响. 结果表明: 在球料比30:1, 转速304 r·min-1条件下, Mo-Si-Mg粉末球磨40 h时才生成亚稳态β-MoSi2, 球磨180 h仍有残留的单质Mo. Mg对MoSi2的合成有阻碍作用, 其合成机制是一种缓慢的反应模式, 不是类自蔓延模式. 球磨后得到粉末的形状近似球形, 并发生了团聚现象. 球磨粉末在900和1000 ℃退火处理1 h后, 亚稳态β-MoSi2全部转变为稳态α-MoSi2, 并且产生了Mo5Si3新相.     

喷涂粉末对MoSi_2涂层结构的影响

以自蔓延合成MoSi2粉末和团聚体MoSi2粉末为喷涂原料,采用大气等离子喷涂技术,在K403镍基合金表面制备了二硅化钼涂层,考察了两种喷涂用粉末对MoSi2涂层的相组成和微观组织的影响。结果表明,自蔓延合成粉末制备的MoSi2涂层含有较多的Mo5Si3和Mo相,不利于涂层的抗氧化性能;采用团聚体粉末为喷涂原料,可制备出含有少量的Mo5Si3相和Mo相且致密性较好的MoSi2涂层。     

等离子喷涂距离和氩气流量对MoSi_2 涂层结构的影响

以MoSi_2粉末为喷涂原料,采用大气等离子喷涂技术,在K403镍基合金表面制备了二硅化钼涂层,考察了不同喷涂距离和氩气流量对MoSi_2涂层的相组成和微观组织的影响.结果表明,随喷涂距离的增加,涂层的相组成由富硅相向富钼相演变;氩气流量的增大可减少涂层中的富钼相,但若流量过大,则会降低涂层的致密性;采用喷涂功率为30 kW、喷涂距离为100 mm和氩气流量为50 L/min的喷涂工艺可制备出以MoSi_2为主相且致密性较高的涂层,明显提高了基体的高温抗氧化性.     

矿用钛合金钻杆表面复合强化与摩擦性能研究*

为提高矿用钛合金钻杆的耐磨性能,以低成本粉末冶金Ti-Al-Fe-Mo合金为研究对象,采用表面机械碾磨与固相渗碳相结合的创新方式对其表面进行复合强化处理,研究不同表面碾磨道次加渗碳处理的钛合金表面的微观组织及其显微硬度。以氮化硅球为摩擦对偶,对表面复合强化钛合金样品进行往复式滑动摩擦试验,研究钛合金表面强化层对其磨损量、摩擦因数、表面磨痕微观组织的影响规律。结果表明：表面机械碾磨方法可以在粉末钛合金表面形成梯度纳米晶结构;钛合金经过表面机械碾磨处理后可显著提高表面渗碳的深度和均匀度;经表面机械碾磨与固相渗碳复合强化处理的钛合金,其磨损量相比于单一表面渗碳的钛合金降低了近58%。表面复合强化的钛合金摩擦磨损机制以疲劳磨损、黏着磨损、氧化磨损和少量的磨粒磨损为主。     

金属间化合物NiAl涂层的制备及耐腐蚀性

采用自蔓延高温合成法制备了适合大气等离子喷涂用的NiAl粉末,在45钢基体上制备NiAl涂层,研究了涂层在800℃的高温氧化特性和室温下浸泡在4wt%NaCl溶液中的耐腐蚀性,利用XRD、SEM技术分析了涂层的高温氧化和耐腐蚀机理。结果表明,自蔓延高温合成法制得的NiAl粉末主要由主相NiAl和少量Al3Ni相组成,制备的NiAl涂层致密且与基体结合良好;NiAl涂层在800℃氧化168 h增重13.8 mg.cm-2,约为45钢的1/10,提高了基体的高温抗氧化性,归因于高温氧化过程中涂层表面变成了一层薄薄的Al2O3保护膜;45钢和NiAl涂层在4wt%NaCl溶液中浸泡腐蚀42天后质量损失分别为5.34、1.23 mg.cm-2,这表明NiAl涂层具有较好的耐腐蚀性。     

块体金属玻璃剪切带相关压缩塑性形成机制研究

研究了Vit1块体金属玻璃在不同压缩载荷下的塑性变形行为和对应的剪切带斑图演化规律。基于机械约束模型,采用高分辨透射电子显微镜对约束载荷下金属玻璃剪切带斑图的形成及演化规律和压缩塑性形成机制进行了分析。结果表明,压缩载荷下机械约束是多重剪切带形成的诱因,纳米晶粒的形成进一步增强了多重剪切带的形成,进而增强金属玻璃的压缩塑性变形能力,对理解块体金属玻璃在约束载荷下剪切带斑图的演化规律、塑性变形行为和进行压力加工提供了有价值的参考。     

稀土元素在铝合金阳极氧化后处理中的应用

研究了将稀土盐（如铈盐）用于铝合金阳极氧化后处理，测量了氧化膜在酸、碱介质中的耐蚀性。结果表明，经铈盐处理后，铝氧化膜的耐酸性明显提高，优于常温封闭处理，耐碱性却降低。这可能是由于氧化膜孔中的稀土化合物在碱性介质中优先溶解。