Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

某矿快速掘进最优炮孔间距的选择

山西某矿5308底抽巷在掘进过程中速度慢、效率低，直接影响工作面的瓦斯抽采，为了改善上述情形，对炮孔间距进行研究。通过使用ANSYS软件对不同炮孔间距下快速掘进效果的模拟分析，并经现场验证，得出了适应该矿的最佳炮孔间距。结果表明：炮孔间距为500 mm时，爆破产生裂隙发育范围和岩石损伤区域都最大，快速掘进的效果最好。     

低温水等离子体活化和表面接枝DMAE聚氯乙烯中空纤维膜研究

采用低温水等离子体技术，在三通道聚氯乙烯(PVC)膜表面接枝了甲基丙烯氧基苄基二甲基氯化铵(DMAE)单体，增强了膜亲水和抗菌性能。通过红外分析，表明DMAE成功接枝到了PVC膜上，水通量提高两倍，PVC-ir-H₂O膜(通过水等离子体处理的膜)对牛血清蛋白(BSA)的吸附能力下降67%，对BSA溶液的通量从7.7提高至40 kg?m^-2?h^-1，并且对BSA的截留能力不变。通过静态及动态抗菌实验，接枝后的PVC膜（PVC-g-PMAE膜）抗菌率达到100%，膜组件运行中的抗菌率也达到82%以上。在保证细菌截留率100%的同时，其渗透通量提高三倍。该膜表面修饰工程技术能实现膜表面的均一化改性，且绿色环保、操作简便、成本低，改性膜在饮用水处理领域，尤其是家用净水器中展现了很好的应用前景。     

关于加强员工考勤管理工作的几点思考

本文介绍了江汉油田员工考勤管理工作的基本情况,梳理和分析了当前员工考勤管理中存在的问题及原因,提出了要进一步细化和完善管理制度,强化过程监督和责任落实,逐步推进考勤公示制度化等措施。     

Three‐dimensional color prediction modeling of single‐ and double‐layered woven fabrics

In this research, the three‐dimensional structural and colorimetric modeling of three‐dimensional woven fabrics was conducted for accurate color predictions. One‐hundred forty single‐ and double‐layered woven samples in a wide range of colors were produced. With the consideration of their three‐dimensional structural parameters, three‐dimensional color prediction models, K/S‐, R‐, and L*a*b*‐based models, were developed through the optimization of previous two‐dimensional models which have been reported to be the three most accurate models for single‐layered woven structures. The accuracy of the new three‐dimensional models was evaluated by calculating the color differences ΔL*, ΔC*, Δh°, and ΔE_CMC(2:1) between the measured and the predicted colors of the samples, and then the error values were compared to those of the two‐dimensional models. As a result, there has been an overall improvement in color predictions of all models with a decrease in ΔE_CMC(2:1) from 10.30 to 5.25 units on average after the three‐dimensional modeling.     

生物质源多孔碳制备及其对废水中药物吸附研究进展

城市现代化与工业化的快速发展给环境造成的污染日趋严重，尤其以水体污染最为明显。近年来，工业废水中药物的含量逐年上升，污染程度已经不容忽视。因此，开发新型多孔材料用于废水中药物分子的吸附分离，已经成为了当前的研究热点。综述了近年来生物质源多孔碳（生物炭）在废水中污染物吸附分离方面的研究，首先简单介绍了废水中污染物的治理方法，在此基础上重点探讨了生物炭的制备与修饰，并结合碳材料表面化学性质与孔道结构，总结并展望了生物炭对药物的吸附性能。