Control of the particle microstructure during the synthesis of bulk-polymerized transparent methacrylate-acrylonitrile-butadiene-styrene resin

A series of methacrylate-acrylonitrile-butadiene-styrene (MABS) resins was prepared using bulk polymerization. The polarity of the continuous phase and the compatibility of two phases were changed by adjusting the methyl methacrylate (MMA) content, choosing values that were close to styrene-butadiene rubber solubility value. The possibility of controlling the microstructure of the MABS resin by changing the polarity of the components and the compatibility of two phases was assessed. The dynamic mechanical analysis shows that the compatibility of two phases varies with the MMA content. The morphological analysis shows that increasing MMA contents results in a gradual decrease in the sub-inclusion structure with a network skeleton of rubber particles, and that all the particles become solid rubber when the MMA content reaches 75%. The sub-inclusion structure reappears but does not have a network skeleton when the MMA content is 90%. The impact strength and morphological analysis indicate that the solid rubber particles and the sub-inclusion structure with a network skeleton provide excellent toughness, while the sub-inclusion structure without a network skeleton does not. In contrast, the transmittance of the ABS resin first increased and then decreased with increasing MMA content.     

改性剂用量对紫炭黑填充天然橡胶/顺丁橡胶并用胶性能的影响

研究改性剂（间苯二酚/六次亚甲基四胺共混物）用量对紫炭黑填充天然橡胶/顺丁橡胶并用胶性能的影响。结果表明：随着改性剂用量增大，胶料的硬度和定伸应力提高，拉伸强度、撕裂强度先下降后提高，阿克隆磨耗量先增大后减小；当改性剂/紫炭黑用量比为4%时，胶料的物理性能较好。添加改性剂可提高紫炭黑对胶料的补强作用，并在一定程度上改善胶料的热稳定性。     

基于滑模的运载器主动段俯仰通道姿控系统设计

与传统比例-积分-微分（PID）控制方法相比，滑模控制（SMC）方法可以比较容易地将不确定性纳入控制器设计中，从而增强系统的鲁棒性。探索了SMC技术在运载器主动段姿态控制中的工程应用，首先通过分析基于趋近律的SMC系统，提出了降低不连续切换项系数的需求，然后研究了基于干扰上界的SMC方法。三通道小偏差仿真结果验证了两种方法的控制效果，表明第2种控制器的鲁棒性更好，稳态误差小，同时发动机喷管摆角需求较小。     

关于硬件木马电路检测技术分析及发展趋势探讨

本文结合HTH电路的复杂性等特征分析与实际应用现状,研究了HTH电路的具体检测技术方法并对当前热点技术进行对比分析,探讨了HTH电路检测方法的技术发展趋势。     

Silver-plated polyamide fabrics with high electromagnetic shielding effectiveness performance prepared by in situ reduction of polydopamine and chemical silvering

In this article, the silver-plated polyamide fabrics (SPPAFs) with high electroconductibility and shielding effectiveness were fabricated by using in situ reduction of polydopamine and chemical silvering. The effects of SPPAFs dopamine (C₈H₁₁O₂N) and silver nitrate (AgNO₃) concentration on surface resistivity and electromagnetic interference shielding effectiveness were studied. The results showed that the surface resistivity of SPPAFs can reach a minimum value of 0.06 ± 0.014 Ω cm⁻¹, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 120 g L⁻¹. The shielding effectiveness of SPPAFs in the wide frequency range of 10–3000 MHz increases with the increase in the concentration of AgNO₃, and increases first and stabilizes afterward with increasing C₈H₁₁O₂N concentration. When the concentration of C₈H₁₁O₂N and AgNO₃ is 3 and 120 g L⁻¹, respectively, mean shielding effectiveness values in the low-, medium-, and high-frequency bands are 71.3, 73.8, and 76.1 dB, respectively. Moreover, the mean shielding effectiveness values is 83.79 dB in the frequency range of 1.2–2.3 GHz. The dominant shielding mechanism of SPPAFs is the reflected electromagnetic waves and the absorption shielding effectiveness is less than 2 dB. The average electromagnetic shielding values of SPPAFs are above 67 dB after 16 weeks of storage, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 80 and 100 g L⁻¹. The prepared SPPAFs show promising applications in military textiles and smart wearable clothing. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48227.