Analysis of pentasodium triphosphate hydration kinetics

The present work analyzes the effect of various factors on the hydration of pentasodium triphosphate. The experimental method is based on application of the hydration test. Technical-quality products with different proportions of phase I and phase II have been used. The variables studied are phase I/phase II ratio, initial temperature, particle size, stirring rate and composition of the slurry (presence of hexahydrate crystals and water hardness). The results have been discussed according to a kinetics model that includes a series of stages of a physical nature (dissolution of anhydrous salt and the crystallization of the hexahydrate), as well as of a chemical nature (solvation of the ions in solution). Crystallization of the hexahydrate may be the controlling stage in the process.     

CHARACTERIZATION OF EVA-BASED ADHESIVES CONTAINING DIFFERENT AMOUNTS OF ROSIN ESTER OR POLYTERPENE TACKIFIER

Different amounts (50-170 php--parts per hundred parts of EVA, 33-63 wt%) of two tackifiers (hydrogenated rosin ester, polyterpene resin) were added to an ethylene vinyl acetate (EVA) copolymer containing 28 wt% vinyl acetate. The EVA and the tackifier were characterized using infrared (IR) spectroscopy, DSC measurements, and stress-controlled plate-plate rheology. The properties and compatibility of the EVA-tackifier mixtures were studied using DSC, DMTA, and stress-controlled plate-plate rheology. Immediate adhesion was measured as a quantification of tack, and the T-peel strength of roughened styrene-butadiene rubber/EVA-tackifier adhesive joints was also obtained. The increase in the amount of tackifier noticeably changed the crystallinity of polyethylene blocks in the EVA, and the temperature at the cross-over between the curves of the storage and loss moduli as a function of the temperature was displaced to a lower value. Whereas the hydrogenated rosin ester was compatible with the amorphous ethylene vinyl acetate copolymer regions of the EVA (Tg value increased) reducing its crystallinity, the polyterpene resin was compatible with the polyethylene blocks of the EVA (T g value was not modified), increasing its crystallinity. Immediate adhesion of the EVA-tackifier mixtures was improved by adding both hydrogenated rosin ester and polyterpene tackifiers. On the other hand, there was an optimum tackifier content at which the maximum T-peel strength value was obtained.     

A New Nonlinear Controller for Trajectory Tracking of the Longitudinal Dynamics of a Small Scale Helicopter

A nonlinear control scheme is proposed for the trajectory tracking problem of a small scale helicopter’s longitudinal dynamics. The control scheme is based on a control design procedure that constructs static feedback regulators for nonlinear systems which are linearizable by dynamic feedback. Besides, the flatness characteristics of the helicopter’s longitudinal dynamics are used to design the desired trajectory. The controller proposed is based on the longitudinal model of the small scale helicopter including the main rotor and stabilizer bar dynamics. Sufficient conditions are given to guarantee asymptotic convergence to zero of the tracking error and to keep the main rotor thrust always negative assuming that all the helicopter’s parameters are known and that all helicopter’s states are measured. Numerical simulations are given to show the performance of the controller in the presence of the main rotor and stabilizer bar dynamics.     

Comparative study of the physical aging of the epoxy systems BADGE n = 0/m‐XDA and BADGE n = 0/m‐XDA/PEI

The physical aging of the epoxy network consisting of a diglycidyl ether of bisphenol A, m‐xylylenediamine, and polyetherimide was studied by differential scanning calorimetry. The glass transition temperature and the variation of the specific heat capacities have been calculated using the method, based on the intersection of both enthalpy–temperature lines for glassy and liquid states. The apparent activation energy (E_H) was calculated using a single method that involved separate temperature and excess enthalpy dependency. All calorimetric data were compared with those obtained for the epoxy network without thermoplastic. thermoplastic. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 103: 3931–3935, 2006     

Photoluminiscent Manganese Nanoparticles from Solid State Polyphosphazenes Organometallic Derivatives

Pyrolysis in air at 800°C of [{NP(OC₁₂H₁₀)}_0.6{NP(OC₆H₄PPh₂·(π-CH₃C₅H₄)−Mn(CO)₂)₂}_0.4] _n (1) in the solid state affords product 2 containing nanoclusters of Mn₂P₂O₇ with sizes ranging from 50 to 90 nm and averaging about 74 nm. The egg-shape of the unpyrolyzed organometallic polymer is retained but with increased particle size after pyrolysis. The pyrolytic material shows near-infrared photoluminescence attributed to the emission of tetrahedral Mn²⁺ embedded in a matrix of Mn₂P₂O₇. The solid-state pyrolysis of organometallic derivatives of polyphosphazenes may be a useful and general route to nano-structured Mn₂P₂O₇. An erratum to this article can be found at     

The effect of nanoclays on the nucleation,crystallization, and melting mechanisms of isotactic polypropylene

The influence of organomodified nanoclay (montmorillonite) on the crystallization and melting mechanisms of isotactic polypropylene (iPP) was studied. Films of both neat polymer and clay nanocomposites were prepared after molecular weight optimization through melt extrusion. Products exhibited the tactoidlike morphology since no compatibilizers were used. The effect of introduction of nanoclay within the polymer was studied through isothermal crystallization and linear heating. The results indicated that low nanoclay concentrations induce the formation of the β‐crystalline structure, its formation being inhibited with high nanoclay contents. Dynamic nonisothermal bulk crystallization experiments indicated that nanoclays act as nucleating agents of iPP. Isothermal, bulk crystallization studies indicated that the crystallization process (induction time and crystallization kinetics) is proportionally accelerated by the nanoclay presence. There was also an accelerated formation of secondary crystallization when nanoclays were present in high concentrations. POLYM. ENG. SCI., 47:1889–1897, 2007. © 2007 Society of Plastics Engineers     

Heterogeneously assisted oxidation of adsorbates from carbonmonoxide, methanol and ethanol by hydrogen peroxide solutions on platinum electrodes in sulphuric acid

The influence of hydrogen peroxide on the adsorption and oxidation of carbon monoxide, methanol and ethanol adlayers on porous Pt electrodes were studied in 2 M sulphuric acid solution by means of cyclic voltammetry and differential electrochemical mass spectrometry (DEMS). The oxidation of adsorbed species is observed at electrode potentials far less negative than those required for electrochemical adsorbate oxidation. The oxidation by H₂O₂ is dependent on its concentration in solution, as well as on the adsorbates and their coverages. In all cases the isolated adlayers are oxidised by dissolved H₂O₂. However, the presence of H₂O₂ during adsorption partially inhibits adlayer formation from CH₃OH and C₂H₅OH, but avoids almost completely the adsorption of carbon monoxide. The removal of the residues from the surface by dissolved hydrogen peroxide probably occurs through O_ad species formed during the heterogeneous decomposition reaction of H₂O₂ on Pt.     

Impregnation of X Zeolite with Alkaline Hydroxide During the Synthesis

Enhancement of the basic properties of the X zeolite with FAU framework has been carried out during synthesis, without further treatment such as ion-exchange or impregnation. Control of the washing stage enables retention of the optimum amount of alkaline hydroxides, which increases the basic catalytic activity of X zeolite in the alkylation of toluene. This alkaline hydroxides neither affect the FAU framework nor the silicon/aluminium molar ratio of the X zeolite. The optimum (Na + K)/Al molar ratio of the improved catalyst was 1.06 corresponding to a washing volume of 200 mL. This X zeolite presented better catalytic activity than a cesium-zeolite prepared by ion-exchange. The presence of hydroxysodalite impurity in the X zeolite increased the amount of impregnated alkaline hydroxides but not the catalytic activity. The present study shows that it is possible to increase the basic properties of the X zeolite directly in the synthesis process.     

MCM-41 Heterogenized Chiral Amines as Base Catalysts for Enantioselective Michael Reaction

Cinchonidine and cinchonine have been grafted onto pure silica MCM-41. It has been shown that both supported alkaloids are active catalysts for the Michael addition of ethyl 2-oxocyclopentanecarboxylate and methyl vinyl ketone, anchored cinchonidine being more active and enantioselective than anchored cinchonine. The study of the influence of the polarity of the solvent and reaction temperature on the optical induction shows that there is not a direct correlation between solvent polarity and enantioselectivity, and the maximum optical yield was obtained between 278 and 273 K.