Properties of Va metal-B films prepared by r.f.-sputtering

Ta_100-x B _x alloy films were prepared by r.f.-sputtering in the chemical composition range 45 x 77. Ta_100-x B _x (45 x 58) films consist of the amorphous phase, while the TaB₂ crystal phase was observed in Ta_100-x B _x (66 x 77) films. A remarkable preferred orientation with the (001) plane of TaB₂ parallel to the film surface was observed in Ta₃₄B₆₆. The d.c. electrical conductivity of Ta_100-x B _x (45 x 77) films decreases with increasing boron content in the range 6.7 × 10³ to 1.3 × 10^3–1 cm^–1. The micro-Vickers hardness of Ta_100-x B _x (45 x 77) films was in the range 2200 to 2600 kg mm^–2.     

Residual Stress in Siliceous Glass Between Mullite Crystals

A birefringence of siliceous glass, which is coexisting with mullite crystals, was studied by an optical polarizing microscope. The cause of the birefringence was assumed to be the residual stress induced by a large contraction difference between the mullite and glass on cooling. The stress has been evaluated to be as high as—0.3 GPa, and to correspond to the elastic one which began to develop at the glass transition point.     

Adhesive properties of cured epoxide resin containing the intermolecular compound of 2,4-diamino-6-vinyl-s-triazine and isocyanuric acid

The intermolecular compound of 2,4-diamino-6-vinyl-s-triazine and isocyanuric acid was synthesized, and the glass transition temperature and the adhesive properties of the cured epoxide resin containing the above compound were studied. Epoxide reacted with amino groups of 2,4-diamino-6-vinyl-s-triazine and isocyanuric acid at the curing conditions of 150 to 180°C for 60 min and formed the cured compounds. The infrared spectra showed that epoxide reacted with isocyanuric acid in the presence of imidazole compounds and converted to 2-oxazolidinone compound on the curing process. The glass transition temperatures of the cured compounds having isocyanurate and 2-oxazolidinone rings in their structures were higher than that of the epoxide resin cured with imidazole and rise as the curing temperature rises, but fall as 2-oxazolidinone ring content increases in their cured compounds. The tensile shear and peel strengths of the steel and steel bonded with the cured compounds and the cured epoxide resin were measured at 25 and 150°C. The adhesive strengths were improved due to isocyanurate and 2-oxazolidinone rings formed in their cured compounds.     

Fat splitting by the twitchell process at low temperature

Summary A study was made of the degree of splitting of coconut and soybean oils by the Twitchell process at 35±0.1°C. with no shaking or stirring, using an agent consisting mainly of tetrabutyl naphthalene sulfonic acid with water or dilute sulfuric acid. The degree of splitting was greater with sulfuric acid than with water. In general, the degree of splitting of soybean oil was greater when the sulfonic acid was dissolved in the oil layer than when it was in water. The reverse was true with coconut oil. Although addition of glycerol had no effect on the degree of splitting, addition of glacial acetic acid to the coconut oil system decreased fat splitting to a considerable extent. Addition of coconut fatty acids to the coconut oil system had little effect, but soybean fatty acids added to the soybean oil system markedly increased the degree of splitting. For the first time it has been demonstrated that, at 35±0.1°C., splitting of a fat by the Twitchell process occurs in a stepwise way. Coconut oil in contact with 1N sulfuric acid containing the sulfonic acid, corresponding to 1% by the weight of the oil, was about 90% split in 15 to 30 days, depending on the area of contact of the two layers. The diglyceride concentration reached a maximum during the early days of the reaction and then decreased somewhat. Monoglyceride concentration appeared to reach a maximum more slowly and then continued at that level as the concentrations of free fatty acids and glycerol steadily increased. Presented at the symposia on fat of the Chemical Society of Japan, Nov. 10, 1954, and Nov. 8, 1955, Nagoya, Japan; and the 8th annual meeting of the Chemical Society of Japan, Apr. 2, 1955, Tokyo, Japan.     

A Practical Model for the Interactions Between Hydrating Portland Cements and Poly-β-Naphthalene Sulfonate Condensate Superplasticizers

The performance of poly-β-naphthalene sulfonate condensate superplasticizer (BNS) as a dispersant for cement in concrete is affected severely by slight differences in the characteristics of the cement. In order to be able to predict these effects, a model for estimating the fluidity of cement paste containing BNS is proposed. This model is based on an assumption that the fluidity of cement paste is proportional to the BNS adsorption amount per surface area of hydrated cement (Ad/Hy). BNS is known to show two types of sorption on hydrated cement: one is the bulk absorption into initial hydrates and the other one is the superficial adsorption onto hydrates. Only the superficially adsorbed BNS is expected to work as a dispersant. By assuming a competitive Langmuir-type adsorption on hydrates between BNS and SO₄²⁻, a simple method to estimate Ad/Hy is developed, with the concentrations of BNS and SO₄²⁻ as the only two independent parameters. The resulting estimates of Ad/Hy show a good correlation with paste flow and its change with elapsed time for a broad range of cements. The SO₄²⁻ concentration in the aqueous phase of the cement paste just after the beginning of the mixing is known to affect the performance of BNS as a dispersant. By using the proposed model to discriminate between the superficial adsorption and bulk absorption of BNS, this phenomenon is explained quantitatively.     

Gelation of poly(vinyl alcohol) solutions at low temperatures (20 to −78°C) and properties of gels

The flow points of atactic poly(vinyl alcohol) (a-PVA) gels with H₂O/dimethyl sulfoxide (DMSO) = 90/10 (v/v) chilled at 20 to ?78°C for 24 h depended on the chilling temperature and were 0–30°C for gels with the initial polymer concentrations (C_i) of 2–5 g/dL, whereas those for H₂O/DMSO = 50/50 chilled at 0 to ?78°C were independent of the chilling temperature and were 70–75°C. Syneresis occurred after eight cycles of freezing (?24°C) and thawing (20°C) for a-PVA hydrogels at concentrations above C_i = 4 g/dL and two such cycles for syndiotacticity-rich PVA (s-PVA) hydrogels at concentrations above C_i = 1 g/dL. The extent of syneresis per one cycle for s-PVA hydrogels was higher than that for a-PVA hydrogels at the initial cycles. In the a-PVA hydrogels with an initial polymer concentration of ca. 30 g/dL, syneresis was expected not to occur even after 20 cycles. If all the free water in the gels is assumed to have transuded by syneresis after 20 cycles, the residual water is bound water and is estimated to be six water molecules per one vinyl alcohol monomer unit. © 1994 John Wiley & Sons, Inc.     

Molecular association complex of urea with polyethylene: 3. Structural studies of the complex

The crystal structure of urea-polyethylene complex in the hexagonal form, obtained by one of our preparation methods, is analysed by X-ray power diffractometry. In this analysis, the fixed molecular parameters of urea are used, and three models with respect to rotational disorder of the guest polyethylene molecule are assumed. It is shown that the host lattice structure constructed by urea molecules is essentially the same as that of urea-n-paraffin complex. Effects of the disorder structure of the guest on X-ray scattering of the complex are presented. However, there is a difficulty in identifying the disorder structure by X-ray analysis. With the aid of a potential energy calculation between the hexagonal urea tunnel and the guest molecule, a rotational disorder model is preferred.     

Effect of Silicon Dioxide on the Thermal Diffusivity of Aluminum Nitride Ceramics

The thermal diffusivity of AlN ceramics was significantly decreased by the addition of SiO₂. The AlN ceramics with 4 wt% SiO₂ could not be densified by pressureless sintering in the temperature range 1400° to 1800°C. The thermal diffusivity of these samples was very low because of their porous structure. The AlN ceramics containing 2, 4, and 8 wt% SiO₂ were densified by hot-pressing and also had low thermal diffusivity. In these samples, the grains of the 27R polytype that resulted from the reaction between AlN and SiO₂ were dispersed, obstructing the conduction of heat. The relation between the amount of 27R polytype and the thermal diffusivity of the AlN ceramics was determined.     

Hydrolysis of human horny cells by alkaline protease: Morphological observation of the process

The interaction of highly purified alkaline protease fromBacillus sp. KSM-K16 with the horny cells of human skin contained in skin grime was directly visualized by electron microscopy. It became clear that the protease first penetrates the horny cells and then adsorbs, mainly onto the internal structure of the cells at the initial stage of hydrolysis, and directly hydrolyzes the keratin filaments, though the marginal band surrounding them retains its original shape. Then, hydrolysate produced from the keratin filaments flows out of the cell, and early in the hydrolysis process keratin filaments decrease and then disappear, leaving a marginal band, i.e., the cell turns to a hollow state. As a result, the remaining marginal band loses support from inside the cell, thus promoting cleavage and dispersion. Until this stage in the protease reaction, the remarkable liberation of hydrolysis products as water-soluble protein does not occur.     

Sintering of Ceria-Doped Tetragonal Zirconia Crystallized in Organic Solvents, Water, and Air

Amorphous CeO₂–ZrO₂ gels were prepared by coprecipitation in ammonia solutions. The onset of crystallization of the gels, from calcining in air, was 420°C, while 200° to 250°C in the presence of water and organic solvents such as methanol and ethanol. The sintering behaviors of CeO₂–ZrO₂ powders were sensitive to the crystallizing conditions, since hard agglomerates formed when the precipitated gels were crystallized by normal calcination in air, whereas soft agglomerates formed when they were crystallized in water or organic solvents. CeO₂–ZrO₂ powders crystallized in methanol and water at 250°C were sintered to full theoretical density at 1150° and 1400°C, respectively, whereas that crystallized by calcination in air at 450°C was sintered to only 95.2% of theoretical density, even at 1500°C.