Laser-Sintered Barium Titanate

Laser sintering of alkoxy-derived ultrafine BaTiO₃ powders was investigated. The temperature increases of the sample with laser irradiation were measured with a thermocouple. It was found that laser irradiation could generate enough heat to sinter ceramics. A slurry was prepared by mixing an alkoxy-derived BaTiO₃ powder, binder additives, solvent, and plasticizer. The slurry was tape cast and dried to give a green sheet. The green sheet was laser sintered and was then characterized by SEM, XRD, and density measurements. The effect of burnout before laser irradiation and the characteristic microstructure of laser-sintered BaTiO₃ are described.     

Surface modification of tetrafluoroethylene–perfluoroalkyl vinylether copolymer (PFA) by plasmas for copper metallization

Tetrafluoroethylene–perfluoroalkyl vinylether copolymer (PFA) sheet surfaces were modified with argon, helium, oxygen, and hydrogen plasmas. How the four plasmas modified the PFA sheet surfaces was investigated. All plasmas modified the PFA surfaces and at the same time initiated degradation of the PFA polymer chains. The balance between modification and degradation was strongly influenced by the magnitude of the discharge current in the plasmas. Efficiency of the plasmas in modification was hydrogen plasma > oxygen plasma > argon plasma > helium plasma. The modification involved defluorination of CF₂ carbons into CHF and CH₂ carbons and oxidation into O? CH₂, O? CHF, and O? CF₂ groups. The surface‐modification technique (a combination of hydrogen plasma treatment and silane coupling treatment) proposed in this study was applied for copper metallization of the PFA surface. The utility of the technique was confirmed. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 1087–1097, 2002     

Properties of aqueous solutions of several salts of α,ω-alkanediol disulfates

Several salts of α,ω-sulfates, MO₃SO(CH₂)_n OSO₃M(n=12, 14, 16, 18, and M=Li, Na, and K) were prepared from the corresponding α,ω-alkane diols. The Krafft points of these α,ω-sulfates with common counterion as estimated by electroconductivity measurements increased with the increase of the hydrocarbon chain length, and the effect of the counterions on the Krafft points of the α,ω-sulfates with the same hydrocarbon chain length was in the order : Li<Na<K. Solutions of the α,ω-sulfates, except disodium dodecanediol disulfate, showed two break points corresponding to the first and second critical micelle concentration in each plot of the electroconductivity as a function of the concentration. The existence of the second break point suggested that another aggregation of rearrangement of the existing aggregates occurs in α,ω-sulfate solutions in addition to the usual micelle formation. The first and second break points of α,ω-sulfates with sodium counterion decreased logarithmically with increasing total number of methylene groups. The relationships were given as follows: log(first break point)=−0.138Nc−0.095; log(second break point)=−0.104Nc−0.251. The effect of the counterions upon the break points of α,ω-sulfates with the same hydrocarbon chain length was in accordance with their positions in the lyotropic series.     

Application of enzymatically gelled chitosan solutions to water‐resistant adhesives

An investigation was undertaken on the application of dilute chitosan solutions gelled by tyrosinase‐catalyzed reaction with 3,4‐dihydroxyphenethylamine (dopamine). The tyrosinase‐catalyzed reaction with dopamine conferred water‐resistant adhesive properties to the semidilute chitosan solutions. The viscosity of the chitosan solutions increased highly by the tyrosinase‐catalyzed reaction and the subsequent reactions between o‐quinone compounds and chitosan. These highly viscous, gel‐like modified chitosan materials were allowed to spread onto the surfaces of the glass slides, which were tightly lapped together and held them in water. Tensile shear adhesive strength of over 400 kPa was observed for the modified chitosan samples. The increase in the amino group concentration of the chitosan solutions and the molecular mass of the chitosan used effectively led to the increase in adhesive strength of the glass slides. In addition, in the case where the chitosan solution was gelled by the enzymatic reaction with dopamine in the presence of poly(ethylene glycol), adhesive strength sharply increased at shorter reaction times concomitantly with the increase in the viscosity of the chitosan solutions because the tyrosinase activity effectively was retained by poly(ethylene glycol). © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 1818–1827, 2007     

Studies on the nuclear magnetic resonance spectra of olefinic protons of conjugated fatty acid methyl esters

The NMR spectra of olefinic protons in the four representative conjugated fatty acid methyl esters, methylcis-9,trans-11-octadecadienoate, methyltrans-9,trans-11-octadecadienoate, methyl α eleostearate, and methyl β eleostearate, were studied. The chemical shift of each olefinic proton in these compounds was determined by considering their intramolecular environment. Coupling constants were also obtained as the results of spectral analysis.     

Contrasting effects of water-soluble and water-insoluble dietary fibers on bile acid conjugation and taurine metabolism in the rat

The effect of the type of dietary fiber on the bile acid and taurine metabolism was examined in rats. Diets containing 10% of various water-soluble fibers (citrus pectin, konjak mannan, guar gum) as compared to a fiber-free diet increased biliary excretion of total bile acids. In contrast, water-insoluble dietary fibers (cellulose, corn bran, chitin; 10% in the diets) as well as cholestyramine (5% in the diet) considerably, decreased bile acid excretion. Water-soluble dietary fibermediated increases in bile acid excretion were totally attributable to increases in glycine-conjugates. Thus, these fibers greatly increased by the bile acid glycine-to-taurine ratio (G/T). Excretio of glycine conjugates decreased more than that of taurine conjugates in rats fed various water-insoluble dietary fibers. As a results, G/T in rats fed water-insoluble fibers was significantly lowered as compared to G/T in animals fed a fiber-free diet. Cholestyramine did not affect the G/T ratio of bile acids. Fecal bile acid excretion and the activities of hepatic cholesterol 7α-hydroxylase (EC 1.14.13.17) in rats fed various water-soluble dietary fibers approximately doubled as compared to the respective values for rats fed a fiber-free diet. Whereas cholestyramine greatly increased these parameters, water-insoluble fibers did not significantly affect them. Various water-soluble fibers decreased hepatic concentration and urinary excretion of taurine as well as the activity of hepatic cysteine dioxygenase (EC 1.13.11.20). In contrast, water-insoluble fibers considerably increased hepatic taurine concentrations and enzyme activities. The parameters for taurine metabolism were unaffected by cholestyramine. It was suggested that the types of dietary fiber affected hepatic taurine synthesis and thus modified bile acid glycine/taurine ratios.     

A novel agglomeration granulating system utilizing a centrifugal-fluidizing drive

Necessary conditions were studied for the optimum operation of agglomeration granulation. The mechanisms that would realize these conditions were investigated by several experiments.On the basis of the results obtained, a novel granulating system involving a surface wetness control mechanism has been developed.The present paper describes the mixing and dispersing characteristics of the coating vessel, the detection method for wetness control, the particular spraying units, and the operating conditions thereof, together with the characteristics of this newly developed powder coating granulation system.This system has been shown to provide an easy and reproducible granulating technique even when products below 1 mm in size are required.     

Development of reel-to-reel microchip mounting system for fabrication of meter-long LED lighting tapes

We have developed a reel-to-reel microchip mounting system that continuously mounts LED chips and other microchips on meter-long flexible printed circuit board (PCB) tape for 1.2-m-long standard LED light tubes. Mounting microchips on meter-long PCBs is difficult because a large chip mounter is expensive and the chip positioning stage is difficult to move in a meter-wide area with an accuracy of hundreds of micrometers. Hence, we developed a new microchip mounting system that utilizes a small chip mounter and reel winding machines. The system repeatedly moves the long PCB tape by a certain length with the reel winding machines and mounts the chips on it. The PCB tape (which is 5 mm wide) is made by fabricating long PCB tapes which are 25 cm × 26.6 m through a roll-to-roll PCB process and slitting them into meter-long tapes. The reel-to-reel system repeatedly mounts chips by adjusting their positions through image processing of the copper wiring pattern on the PCBs. Our constructed system mounted 24 LED chips with a pitch of 5 cm with an accuracy of 0.082 mm to form a 1.2-m-long LED tape. The luminance of the tape is 12.4 lx at a distance of 1 m, which is the luminance of outdoor corridor lighting. Therefore, this system can be used for meter-long tape lighting.     

Thermal strain of high strength polyethylene fiber in low temperature

High strength polyethylene fiber (Toyobo, Dyneema® fiber: hereinafter abbreviated to DF) has a negative thermal expansion coefficient. Relation between fiber structure and thermal strain of DF used as reinforcement of DF reinforced plastic (DFRP) for cryogenic use was investigated. The crystallinities and orientation angles of several kinds of polyethylene fibers having different modulus from 15 to 134Gpa (herein after abbreviated to DFs) were measured by NMR and X‐ray. We obtained the parameters of the mechanical series‐parallel model composed of crystal and amorphous by crystallinity and modulus. Thermal expansion coefficients of DFs were estimated by mechanical series‐parallel model. All DFs having different modulus showed negative thermal expansion coefficients in the temperature range from 180 to 300K, and absolute values of those markedly increased by increasing tensile modulus of DF. The estimated thermal expansion coefficients showed negative values, and thermal strains showed a similar curve to observed ones mostly. Average thermal expansion coefficients in the temperature range from 180 to 300K estimated by mechanical model agreed with the observed ones. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2918–2925, 2004     

Oxidation kinetics for <Emphasis Type="Italic">cis</Emphasis>-9,<Emphasis Type="Italic">trans</Emphasis>-11 and <Emphasis Type="Italic">trans</Emphasis>-10,<Emphasis Type="Italic">cis</Emphasis>-12 isomers of CLA

The autoxidation processes of the cis-9,trans-11 (c9,t11) and trans-10,cis-12 (t10,c12) isomers of CLA were separately observed at ca. 0% RH and different temperatures. The t10,c12 CLA oxidized faster than the c9,t11 isomer at all tested temperatures. The first half of the oxidation process of t10,c12 CLA obeyed an autocatalytic-type rate expression, but the latter half followed first-order kinetics. On the other hand, the entire oxidation process of c9,t11 CLA could be expressed by the autocatalytic-type rate expression. The apparent activation energies and frequency factors for the autoxidation of the isomers were estimated from the rate constants obtained at various temperatures based on the Arrhenius equation. The apparent activation energies for the CLA isomers were greater than those for the nonconjugated n−6 and n−3 PUFA or their esters. However, the enthalpyentropy compensation held during the autoxidation of both the CLA and PUFA. This suggested that the autoxidation mechanisms for the CLA and PUFA were essentially the same.