Effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers

In this paper, polyborosilazane precursor was synthesied from HMDZ, HSiCl₃, BCl₃ and CH₃NH₂ using a multistep method. By controlling the storage conditions, parts of the polyborosilazane fibers were hydrolyzed. FT-IR, NMR, XRD, TEM and monofilament tensile strength test were employed to study the effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers. FT-IR and NMR results indicate that Si-N group in PBSZ reacts with H₂O to form Si-O-Si group. After pyrolysis reaction at 1400℃, Si-O-Si group will finally transformed into highly ordered cristobalite and β-quartz, resulting in formation of the wrinkled surface of the obtained SiBN ceramic fiber. The strip-like defects on fiber surface, according to monofilament tensile strength test, had a significant effect on mechanical property of the obtained SiBN ceramic fiber and caused no increase in fiber tensile strength of hydrolytic polyborosilazane fiber before and after pyrolytic process.     

不同矿区天然隐晶质石墨对天然橡胶性能的影响

选用两种不同矿区的天然隐晶质石墨材料,经过超细粉体制备研磨后用于天然橡胶,探究了不同矿区隐晶质石墨在天然橡胶中的溶解度和对性能的影响并研究了粒径和混合工艺对天然橡胶性能的影响规律。研究表明,不同矿区隐晶质石墨因集合体构成不同,在橡胶中的溶解度差异较大；粒径大小是影响橡胶性能的关键参数；混合工艺对橡胶性能的影响更为明显。     

Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

Discovery of Affinity-Based Probes for Btk Occupancy Assays

Bruton's tyrosine kinase (Btk) is an attractive target for the treatment of a wide array of B-cell malignancies and autoimmune diseases. Small-molecule covalent irreversible Btk inhibitors targeting Cys481 have been developed for the treatment of such diseases. In clinical trials, probe molecules are required in occupancy studies to measure the level of engagement of the protein by these covalent irreversible inhibitors. The result of this pharmacodynamic (PD) activity provides guidance for appropriate dosage selection to optimize inhibition of the drug target and correlation of target inhibition with disease treatment efficacy. This information is crucial for successful evaluation of drug candidates in clinical trials. Based on the pyridine carboxamide scaffold of a novel solvent-accessible pocket (SAP) series of covalent irreversible Btk inhibitors, we successfully developed a potent and selective affinity-based biotinylated probe 12 (2-[(4-{4-[5-(1-{5-[(3aS,4S,6aR)-2-oxo-hexahydro-1H-thieno[3,4-d]imidazol-4-yl]pentanamido}-3,6,9,12-tetraoxapentadecan-15-amido)pentanoyl]piperazine-1-carbonyl}phenyl)amino]-6-[1-(prop-2-enoyl)piperidin-4-yl]pyridine-3-carboxamide). Compound 12 has been used in Btk occupancy assays for preclinical studies to determine the therapeutic efficacy of Btk inhibition in two mouse lupus models driven by TLR7 activation and type I interferon.     

厚煤层放顶煤大角度扇形收尾施工工艺实践

以左云长春兴煤业公司301综放工作面扇形收尾施工工艺为背景,介绍了在工作面受地质构造或者井田边界影响,工作面两顺槽与盘区大巷斜交布置时,为了多回收煤炭资源,提高经济效益,采取大角度扇形收尾的施工工艺,为厚煤层放顶煤大角度扇形收尾提供了借鉴和理论依据。     

Effect of Biochar as Reductant on Magnetizing-roasting Behavior of Pyrite Cinder

The effect of biochar substituted for anthracite as reductant on magnetizing-roasting pyrite cinder was investigated.The key of magnetizing-roasting is the gasification reaction between reductants and CO2.Since biochar could react with CO2 more rapidly at lower temperature,the reactivity of biochar is better than that of anthracite.The gasification of biochar could produce reducing condition ofφCO/(φCO+φCO2)about 10%-20% between 700-800 ℃,which is in accord with the atmosphere and temperature of Fe2O3 reduction.So it is beneficial to the reduction of iron mineral of pyrite cinder.Compared with anthracite,biochar could decrease the roasting temperature from825 to 750 ℃ and roasting time from 20 to 15min,which shows that a better effect of magnetization could be obtained in the condition of lower temperature and shorter time.Using biochar as reductant,iron concentrate extracted from pyrite cinder as about 64%iron grade could be produced,and the recovery is over 90% under the condition of above 90% grinding particle less than 0.045 mm and magnetic intensity of 0.124-0.194 T.     

Operating Range Scheduled Robust Dahlin Algorithm to Typical Industrial Process with Input Constraint

International Journal of Control, Automation and Systems - There is a class of typical nonlinear industrial process, which can be characterized by a first-order inertia plus pure delay model in an...     

单相硼化物的制备及摩擦磨损性能研究

为了深入研究渗硼层中硼化物的性能，采用真空感应熔炼法制备单相硼化物材料。观察分析制备的硼化物微观组织，测试其力学性能。采用MMU-5G型销-盘式摩擦磨损试验机，在干摩擦条件下，研究了不同载荷下单相硼化物的摩擦学性能，观察其磨损表面形貌特征，探讨其磨损方式。结果表明：制备的硼化物为单一相，试样纯度高，试样的平均显微硬度为HV2065，平均断裂韧性值为1.68 MPa·m1/2；硼化物的断口处没有宏观的塑性变形，断口齐平光亮，表现为脆性断裂特征；干摩擦条件下随着载荷从10 N增加到30 N，硼化物的摩擦因数先降低后增加，20 N载荷时达到最小值，而其磨损量随着载荷的增加不断上升；随着载荷从10 N增加到30 N，磨损表面的粗糙度先逐渐上升后急剧上升； 10~20 N载荷下，硼化物的磨损以磨粒磨损为主，而25~30 N载荷下，硼化物的主要磨损方式从磨粒磨损转变为脆性破损。