Effect of Biochar as Reductant on Magnetizing-roasting Behavior of Pyrite Cinder

The effect of biochar substituted for anthracite as reductant on magnetizing-roasting pyrite cinder was investigated.The key of magnetizing-roasting is the gasification reaction between reductants and CO2.Since biochar could react with CO2 more rapidly at lower temperature,the reactivity of biochar is better than that of anthracite.The gasification of biochar could produce reducing condition ofφCO/(φCO+φCO2)about 10%-20% between 700-800 ℃,which is in accord with the atmosphere and temperature of Fe2O3 reduction.So it is beneficial to the reduction of iron mineral of pyrite cinder.Compared with anthracite,biochar could decrease the roasting temperature from825 to 750 ℃ and roasting time from 20 to 15min,which shows that a better effect of magnetization could be obtained in the condition of lower temperature and shorter time.Using biochar as reductant,iron concentrate extracted from pyrite cinder as about 64%iron grade could be produced,and the recovery is over 90% under the condition of above 90% grinding particle less than 0.045 mm and magnetic intensity of 0.124-0.194 T.     

Unveiling the role of Fe3O4in polymer spin valve near Verwey transition

The spinterface formed between ferromagnetic(FM)electrode and organic materials is vital for performance optimization in organic spin valve(OSV).Half-metallic Fe₃O₄with drastic change in structure,conductivity and magnetic property near Verwey transition can serve as an intrinsic spinterface regulator.However,such modulating effect of Fe₃O₄in OSV has not been comprehensively investigated,especially below the Verwey transition temperature(Tv).Here,we highlight the important role of Fe₃O₄electrode in reliable-working and controllable Fe₃O₄/P3HT/Co polymer spin valves by investigating the magnetoresistance(MR)above and below 7V.In order to distinguish between different contributions to charge transport and related MR responses,the systematic electronic and magnetic characterizations were carried out in full temperature range.Particularly,the first-order metal-insulator transition in Fe₃O₄has a dramatic effect on the MR enhancement of polymer spin valves at 7V.Moreover,both the conducting mode transformation and MR line shape modulation could be accomplished across 7V.This research renders unique scenario to multimodal storage by external thermodynamic parameters,and further reveals the importance of spin-dependent interfacial modification in polymer spin valves.     

Operating Range Scheduled Robust Dahlin Algorithm to Typical Industrial Process with Input Constraint

International Journal of Control, Automation and Systems - There is a class of typical nonlinear industrial process, which can be characterized by a first-order inertia plus pure delay model in an...     

救生舱的防护性能试验分析

通过模拟灾变环境,完成了12人106 h的综合性能防护试验,验证了舱内供氧系统、气幕喷淋系统、温湿度调节与空气处理系统、监测与通讯系统、动力系统等的运行可靠性,进一步优化了产品设计。     

ZSM-5沸石膜用于生物油的脱水分离及其再生过程研究

在水热条件下通过无模板剂法合成了连续的ZSM-5沸石膜，并将其用于生物油的渗透汽化以进行高效脱水分离。ZSM-5沸石膜在强酸性、多组分的生物油体系中保持了很好的化学稳定性和优异的分离选择性，但在分离过程中面临着较强的膜污染问题，导致了膜通量的大幅下降。ZSM-5沸石膜的再生研究表明，膜的渗透通量随着再生温度的升高而逐渐提高。当再生温度为220℃时，ZSM-5沸石膜的渗透通量可以恢复至初始的88%。再生的机理研究表明，ZSM-5沸石膜中大量的晶内孔在生物油体系中极易被污染，从而导致渗透通量迅速下降；而相对较大的晶间孔却难以被完全堵塞，水分子在被污染的ZSM-5沸石膜中主要通过晶间孔进行渗透。上述结果表明，通过合理调控ZSM-5沸石膜的晶间孔的数量和尺寸大小可有效提升ZSM-5沸石膜在生物油中的渗透汽化脱水分离性能。     

Structure, properties, and thermal stability of nanocrystallite Fe-Ti-N soft magnetic films

We deposited Fe-Ti-N magnetic films with a high sputtering power of 7 W/cm/sup 2/. When the composition of the films was in the range of Fe-Ti(3.9 at.%)-N(8.8 at.%) to Fe-Ti(3.3 at.%)-N(13.5 at.%), the films were composed of /spl alpha/' and Ti/sub 2/N precipitates. With the addition of nitrogen, 4/spl pi/M/sub s/ became higher than that of pure iron, reaching a maximum of 23.8 kG. At the same time, H/sub c/ was reduced to a minimum of 1.12 Oe. The best films can meet the needs of the recording head in dual-element giant magnetoresistive/inductive heads, yielding high storage density (10 Gb/in/sup 2/). The incorporation of N in /spl alpha/-Fe brought about the /spl alpha/' phase with its higher saturation magnetization. Ti additions inhibited the equilibrium decomposition /spl alpha/'/spl rarr//spl alpha/+/spl gamma/'. Because H/sub C//sup D//spl prop/D/sup 6/, where D is average grain diameter, grain size control is very important. The nitrogen induces severe distortion of the /spl alpha/' lattice, which can cause the grains to break into pieces and reduce the grain size. High sputtering power also led to the formation of fine grains, with diameter in the order of 14 nm. Probably Ti/sub 2/N is preferentially precipitated on the grain boundary, pinning the grain boundary and stabilizing the grain size during high-temperature heat treatment. The temperature limit for stability of the structure and its associated low coercivity was not less than 520/spl deg/C.     

空间相机中的偏流角分析

高分辨率星载TDI-CCD相机在成像过程中,偏流角会对相机的成像质量产生影响.因此根据卫星轨道方程给出了偏流角和偏流角角速度随纬度变化的具体形式,基于此分别研究了偏流角在卫星穿航方向和沿航方向引起的像移量和它对相机成像质量的影响.结果表明,偏流角是纬度的函数,由它引起的像移在穿航方向对相机像质的影响较为严重,必须加以校正.并针对极地圆轨道详细计算了像移对像质的影响程度和在MTF偏流角＞0.95的情况下偏流角需要调整的最小时间间隔.     

储层泥浆侵入深度预测方法研究

泥浆侵入半径的确定尚缺乏严格的验证标准.以油水两相渗流理论和离子扩散方程为基础,结合储集层特点,研究了不同储层参数下泥浆滤液对地层的侵入特性.数值模拟侵入时间选取10 d和20 d.数值模拟结果表明,侵入半径在渗透率不变的情况下随孔隙度的增大而减小,在孔隙度不变的情况下随渗透率的增大而增大;当渗透率和孔隙度都发生变化时,泥浆侵入半径一般随孔隙度的增加呈幂函数增加.依据这种关系对测井资料约束处理,得到的泥浆侵入半径较客观地反映了地层的真实情况.