Zeolitic-imidazolate frameworks-derived Co3S4/NiS@Ni foam heterostructure as highly efficient electrocatalyst for oxygen evolution reaction

Transition metals sulfide-based nanomaterials have recently received significant attention as a promising cathode electrode for the oxygen evolution reaction (OER) due to their easily tunable electronic, chemical, and physical properties. However, the poor electrical conductivity of metal-sulfide materials impedes their practical application in energy devices. Herein, firstly nano-sized crystals of cobalt-based zeolitic-imidazolate framework (Co-ZIF) arrays were fabricated on nickel-form (NF) as the sacrificial template by a facile solution method to enhance the electrical conductivity of the electrocatalyst. Then, the Co₃S₄/NiS@NF heterostructured arrays were synthesized by a simple hydrothermal route. The Co-ZIFs derived Co₃S₄ nanosheets are grown successfully on NiS nanorods during the hydrothermal sulfurization process. The bimetallic sulfide-based Co₃S₄/NiS@NF-12 electrocatalyst demonstrated a very low overpotential of 119 mV at 10 mA cm^?2 for OER, which is much lower than that of mono-metal sulfide NiS@NF (201 mV) and ruthenium-oxide (RuO₂) on NF (440 mV) electrocatalysts. Furthermore, the Co₃S₄/NiS@NF-12 electrocatalyst showed high stability during cyclic voltammetry and chronoamperometry measurements. This research work offers an effective strategy for fabricating high-performance non-precious OER electrocatalysts.     

Co2FeO4@rGO composite: Towards trifunctional water splitting in alkaline media

Development of efficient, low cost and multifunctional electrocatalysts for water splitting to harvest hydrogen fuels is a challenging task, but the combination of carbon materials with transition metal-based compounds is providing a unique and attractive strategy. Herein, composite systems based on cobalt ferrite oxide-reduced graphene oxide (Co₂FeO₄) @(rGO) using simultaneous hydrothermal and chemical reduction methods have been prepared. The proposed study eliminates one step associated with the conversion of GO into rGO as it uses direct GO during the synthesis of cobalt ferrite oxide, consequently rGO based hybrid system is achieved in-situ significantly, the optimized Co₂FeO₄@rGO composite has revealed an outstanding multifunctional applications related to both oxygen evolution reaction (OER) and hydrogen counterpart (HER). Various metal oxidation states and oxygen vacancies at the surface of Co₂FeO₄@rGO composites guided the multifunctional surface properties. The optimized Co₂FeO₄@rGO composite presents excellent multifunctional properties with onset potential of 0.60 V for ORR, an overpotential of 240 mV at a 20 mAcm^?2 for OER and 320 mV at a 10 mAcm^?2 for HER respectively. Results revealed that these multifunctional properties of the optimized Co₂FeO₄@ rGO composite are associated with high electrical conductivity, high density of active sites, crystal defects, oxygen vacancies, and favorable electronic structure arisinng from the substitution of Fe for Co atoms in binary spinel oxide phase. These surface features synergistically uplifted the electrocatalytic properties of Co₂FeO₄@rGO composites. The multifunctional properties of the Co₂FeO₄@ rGO composite could be of high interest for its use in a wide range of applications in sustainable and renewable energy fields.     

Activation of LSCF–YSZ interface by cobalt migration during electrolysis operation in solid oxide electrolysis cells

High-temperature water electrolysis through solid oxide electrolysis cells (SOEC) will play a key role in building a hydrogen economy in the future. However, the delamination between the air electrode and the electrolyte remains a critical issue to be addressed. Previously, it was hypothesized that Co migration may improve the catalytic activity of the SrZrO₃ second phase at the LSCF-YSZ interface, eventually leading to the delamination. In this work, the LSCF-YSZ interfaces sintered at different temperatures were examined in detail. The activation behaviors of the LSCF electrodes upon application with electrolysis current were characterized under different conditions. Further, samples containing purposely added SrZrO₃ interlayer with and without cobalt were fabricated and compared. The activation process is less significant for the sample with cobalt-added SrZrO₃ interlayer than the sample with pure SrZrO₃ layer, supporting the hypothesis that Co migration may lead to the activation behavior.     

我国水-能源-粮食耦合关系及影响因素

为缓解我国水、能源和粮食资源紧张问题，促进资源可持续利用，构建水-能源-粮食系统，利用耦合协调度模型对我国的30个省（自治区、直辖市）进行测算,并利用空间杜宾模型分析主要影响因素。结果表明：2003—2017年，我国能源、粮食评价[JP]指数高于水资源评价指数，系统综合评价指数逐年递增；大部分省份耦合协调度处于初级协调水平且呈现逐年上升的态势，个别省份耦合协调度濒临失调；耦合协调度空间自相关性较强，虽有明显波动，但是呈现逐年加强的态势；影响耦合协调度的主要因素有从业人口数、固定资产投资额、人均生产总值、人口总数、[JP]文盲人口占比、工业污染排放、城镇化。     

A novel method of shrimp blanching by CO2 heat pump: Quality,energy, and economy analysis

To reduce the energy consumption of the shrimp blanching process and improve the economic value of the blanched product, a transcritical CO₂ heat pump blanching system (THPB system) was designed in this paper. The trends of astaxanthin were investigated at atmospheric pressure near boiling temperature, combined with the color and structural properties of shrimp samples, and the optimal blanching times of 270 s and 240 s were obtained at 90°C and 95°C, respectively. In contrast to the fuel blanching system (FB system) at 100°C, the annual standard coal consumption of the THPB system with 90°C blanching is decreased by 79%, and the annual operating cost can be saved by CNY 63,800, with a payback period of about 3.13 years.Industrial relevanceBlanching is one of the effective ways to prolong the shelf life of shrimp. However, the research on the blanching time and temperature of shrimp is not comprehensive. In addition, the traditional fuel blanching process has high energy consumption and pollution, and can no longer meet the quality requirements of the modern food processing industry. Heat pump has been shown to have better performance in food drying, but it is less used in blanching. The information presented in this study may provide other insights into food processing.     

Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Scallops as a new source of food protein: high-intensity ultrasonication improved stability of oil-in-water emulsion stabilised by myofibrillar protein

In this study, the effect of high-intensity ultrasound (HIUS) (200 and 400 W for 0, 5, 10 and 15 min respectively) on conformational changes, physicochemical, rheological and emulsifying properties of scallop (Patinopecten yessoensis) myofibrillar protein (SMP) was investigated. HIUS-treated SMP had lower α-helix content and higher β-sheet content compared with the native SMP. HIUS treatment induced the unfolding of SMP and increased the surface hydrophobicity. The particle size of SMP decreased and the absolute zeta-potential increased after ultrasonication, which in turn increased the solubility of SMP. The conformational changes and the improvement of physicochemical properties of SMP increased the ability for SMP to lower the interfacial tension at the oil–water interface and increased the percentage of adsorbed protein. As a result, the emulsifying properties, rheological properties of SMP and storage stability of emulsions were also improved. In conclusion, HIUS treatment has future potential for improving the emulsifying properties of SMP.     

Structural health monitoring system based on multi-agent coordination and fusion for large structure

In practical applications of structural health monitoring technology, a large number of distributed sensors are usually adopted to monitor the big dimension structures and different kinds of damage. The monitored structures are usually divided into different sub-structures and monitored by different sensor sets. Under this situation, how to manage the distributed sensor set and fuse different methods to obtain a fast and accurate evaluation result is an important problem to be addressed deeply. In the paper, a multi-agent fusion and coordination system is presented to deal with the damage identification for the strain distribution and joint failure in the large structure. Firstly, the monitoring system is adopted to distributedly monitor two kinds of damages, and it self-judges whether the static load happens in the monitored sub-region, and focuses on the static load on the sub-region boundary to obtain the sensor network information with blackboard model. Then, the improved contract net protocol is used to dynamically distribute the damage evaluation module for monitoring two kinds of damage uninterruptedly. Lastly, a reliable assessment for the whole structure is given by combing various heterogeneous classifiers strengths with voting-based fusion. The proposed multi-agent system is illustrated through a large aerospace aluminum plate structure experiment. The result shows that the method can significantly improve the monitoring performance for the large-scale structure.     

A review of the existing performance verification infrastructure for micro-CMMs

The performance verification of micro-CMMs is now of intense interest because of their capability to perform length measurements in three dimensions to high accuracy with low uncertainties. Currently, verification of micro-CMMs is completed in the spirit of existing specification standards, because strict adherence to these standards is often difficult. This review aims to present and discuss verification techniques available for micro-CMMs: specification standards, existing calibrated test lengths and traceability routes that can be associated with micro-CMMs. Three specification standards used in the testing of CMMs will be considered. In addition, a wide range of calibrated test lengths are reported, and any advantages and disadvantages associated with their use are discussed. It is concluded that micro-CMMs cannot yet be verified in accordance with existing specification standards. Suggestions are made for future standardisation work required to rectify these issues.     

Significant spatial co-distribution pattern discovery

Given instances (spatial points) of different spatial features (categories), significant spatial co-distribution pattern discovery aims to find subsets of spatial features whose spatial distributions are statistically significantly similar to each other. Discovering significant spatial co-distribution patterns is important for many application domains such as identifying spatial associations between diseases and risk factors in spatial epidemiology. Previous methods mostly associated spatial features whose instances are frequently located together; however, this does not necessarily indicate a similarity in the spatial distributions between different features. Thus, this paper defines the significant spatial co-distribution pattern discovery problem and subsequently develops a novel method to solve it effectively. First, we propose a new measure, dissimilarity index, to quantify the difference between spatial distributions of different features under the spatial neighbor relation and then employ it in a distribution clustering method to detect candidate spatial co-distribution patterns. To further remove spurious patterns that occur accidentally, the validity of each candidate spatial co-distribution pattern is verified through a significance test under the null hypothesis that spatial distributions of different features are independent of each other. To model the null hypothesis, a distribution shift-correction method is presented by randomizing the relationships between different features and maintaining spatial structure of each feature (e.g., spatial auto-correlation). Comparisons with baseline methods using synthetic datasets demonstrate the effectiveness of the proposed method. A case study identifying co-morbidities in central Colorado is also presented to illustrate the real-world applicability of the proposed method.