电压对电刷镀三价铬镀层性能的影响

在45钢表面电刷镀得到三价铬镀层,镀液组成和工艺条件为:Cr2(SO4)36H2O 0.4 mol/L,甲酸铵0.5 mol/L,氨基乙酸0.5 mol/L,H3BO30.6 mol/L,NaH2PO2 H2O 0.3 mol/L,pH=1.5,温度50°C,镀笔移动速率15 cm/s。研究了电压对镀铬层显微结构、表面粗糙度、厚度、显微硬度和耐磨性的影响。随电压增大,镀层厚度增大,显微硬度和耐磨性均先提高后降低。电压为14 V时,镀层的表面平整,粗糙度为2.387μm,显微硬度为602 HV,耐磨性最好。     

脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。     

浅谈压延铜箔光面色差的成因

针对压延铜箔在表面处理过程中光面易出现色差的问题,从设备、工艺、人员操作等方面进行成因探讨,并给出了应对措施。     

基于分形插值的改进趋势面拟合法在地面沉降中的应用

针对区域地面沉降监测点数量有限、分布不均的情况,一般采用空间插值的手段建立表面拟合模型来解决。基于分形插值,采用随机选择迭代函数的思想对传统的趋势面拟合法作出改进,改进后拟合优度系数提高0.03,达到0.995,且改进前后的拟合结果符合显著性检验的要求。实验结果表明:改进前后趋势面拟合法拟合结果满足地面沉降监测的精度要求,改进后方法的拟合优度更高,对现实地面沉降量变化的描绘更加真实,可为沉降灾害评价工作提供更准确的依据。     

Development of green extraction process to produce antioxidant-rich extracts from purple coneflower

The present study was conducted to develop subcritical water extraction (SWE) of Echinacea purpurea flowers. The influence of temperature and extraction time on quality of extracts considering total phenols content, total flavonoids content, antioxidant capacity and extraction yield, was determined. Optimized extraction parameters for maximised investigated responses were as follows: 147.56 °C and 8.43 min. The experimental values agreed with the values predicted, thus indicating the adequacy of central composite experimental design for modelling the SWE of bioactive compounds from E. purpurea. Results of the study also highlighted the potential application of E. purpurea subcritical water extracts as a source of valuable bioactive compounds.     

Dynamic probe of ZnTe(110) surface by scanning tunneling microscopy

The reconstructed surface structure of the II–VI semiconductor ZnTe (110), which is a promising material in the research field of semiconductor spintronics, was studied by scanning tunneling microscopy/spectroscopy (STM/STS). First, the surface states formed by reconstruction by the charge transfer of dangling bond electrons from cationic Zn to anionic Te atoms, which are similar to those of IV and III–V semiconductors, were confirmed in real space. Secondly, oscillation in tunneling current between binary states, which is considered to reflect a conformational change in the topmost Zn–Te structure between the reconstructed and bulk-like ideal structures, was directly observed by STM. Third, using the technique of charge injection, a surface atomic structure was successfully fabricated, suggesting the possibility of atomic-scale manipulation of this widely applicable surface of ZnTe.     

Thermal and transport properties of as-grown Ni-rich TiNi shape memory alloys

Electrical resistivity, Seebeck coefficient, specific heat and thermal conductivity measurements on the Ti_50−xNi_50+x (x = 0.0–1.6 at.%) shape memory alloys are performed to investigate their thermal and transport properties. In this study, anomalous features are observed in both cooling and heating cycles in all measured physical properties of the slightly Ni-rich TiNi alloys (x ≤ 1.0), corresponds to the transformation between the B19′ martensite and B2 austenite phases. Besides, the transition temperature is found to decrease gradually with increasing Ni content, and the driving force for the transition is also found to diminish slowly with the addition of excess Ni, as revealed by specific heat measurements. While the signature of martensitic transformation vanishes for the Ni-rich TiNi alloys with x ≥ 1.3, the characteristics of strain glass transition start to appear. The Seebeck coefficients of these TiNi alloys were found to be positive, suggesting the hole-type carriers dominate the thermoelectric transport. From the high-temperature Seebeck coefficients, the estimated value of Fermi energy ranges from ∼1.5 eV (Ti_48.4Ni_51.6) to ∼2.1 eV (Ti₅₀Ni₅₀), indicating the metallic nature of these alloys. In addition, the thermal conductivity of the slightly Ni-rich TiNi alloys with x ≤ 1.0 shows a distinct anomalous feature at the B19′ → B2 transition, likely due to the variation in lattice thermal conductivity.     

Silver-plated polyamide fabrics with high electromagnetic shielding effectiveness performance prepared by in situ reduction of polydopamine and chemical silvering

In this article, the silver-plated polyamide fabrics (SPPAFs) with high electroconductibility and shielding effectiveness were fabricated by using in situ reduction of polydopamine and chemical silvering. The effects of SPPAFs dopamine (C₈H₁₁O₂N) and silver nitrate (AgNO₃) concentration on surface resistivity and electromagnetic interference shielding effectiveness were studied. The results showed that the surface resistivity of SPPAFs can reach a minimum value of 0.06 ± 0.014 Ω cm⁻¹, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 120 g L⁻¹. The shielding effectiveness of SPPAFs in the wide frequency range of 10–3000 MHz increases with the increase in the concentration of AgNO₃, and increases first and stabilizes afterward with increasing C₈H₁₁O₂N concentration. When the concentration of C₈H₁₁O₂N and AgNO₃ is 3 and 120 g L⁻¹, respectively, mean shielding effectiveness values in the low-, medium-, and high-frequency bands are 71.3, 73.8, and 76.1 dB, respectively. Moreover, the mean shielding effectiveness values is 83.79 dB in the frequency range of 1.2–2.3 GHz. The dominant shielding mechanism of SPPAFs is the reflected electromagnetic waves and the absorption shielding effectiveness is less than 2 dB. The average electromagnetic shielding values of SPPAFs are above 67 dB after 16 weeks of storage, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 80 and 100 g L⁻¹. The prepared SPPAFs show promising applications in military textiles and smart wearable clothing. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48227.     

Kariya (Hildegardia barteri) seed oil extraction: comparative evaluation of solvents,modeling, and optimization techniques

In this work, the effects of solid/solvent ratio (0.10–0.25?g/ml), extraction time (3–8?h), and solvent type (n-hexane, ethyl acetate, and acetone) together with their shared interactions on Kariya seed oil (KSO) yield were investigated. The oil extraction process was modeled via response surface methodology (RSM), artificial neural network (ANN) and adaptive neuro-fuzzy inference system (ANFIS) while the optimization of the three input variables essential to the oil extraction process was carried out by genetic algorithm (GA) and RSM methods. The low mean relative percent deviation (MRPD) of 0.94–4.69% and high coefficient of determination (R²) > 0.98 for the models developed demonstrate that they describe the solvent extraction process with high accuracy in this order: ANFIS, ANN, and RSM. The best operating condition (solid/solvent ratio of 0.1?g/ml, extraction time of 8?h, and acetone as solvent of extraction) that gave the highest KSO yield (32.52?wt.%) was obtained using GA-ANFIS and GA-ANN. Solvent extraction efficiency evaluation showed that ethyl acetate, n-hexane, and acetone gave maximum experimental oil yields of 19.20?±?0.28, 25.11?±?0.01, and 32.33?±?0.04?wt.%, respectively. Properties of the KSO varied based on the type of solvent used. The results of this work showed that KSO could function as raw material in both food and chemical industries.     

Surface modification of poly(tetrafluoroethylene) and poly(ethylene terephthalate) films via environmental crazing

This work addresses the phenomenon of the development of a patterned surface relief on polymer films via different modes of environmental crazing. Commercial films of semicrystalline poly(tetrafluoroethylene) (PTFE) and amorphous glassy poly(ethylene terephthalate) (PET) were subjected to tensile drawing in the presence of physically active liquid environments (carbon tetrachloride or aliphatic alcohols). The structure parameters and wettability of the modified films were studied by AFM, SEM, profilometer measurements and contact angle measurements. Environmental intercrystallite crazing of PTFE is accompanied by the development of an unstable structure with a high free surface, which experiences marked strain recovery upon unloading. As a result of the relief formation, PTFE hydrophobicity is enhanced (the water contact angle increases by 25°). Classical environmental crazing of PET films is accompanied by the formation of an anisotropic surface relief which is an assembly of crazes oriented perpendicular to the direction of tensile drawing, thus leading to the phenomenon of anisotropic wetting. The proposed approach for structural surface modification makes it possible to use the advantages of surface instability and spontaneous self‐organization of the polymer towards the development of a unique surface microrelief. © 2020 Society of Chemical Industry