Failure Analysis of Fuel System Assemblies

Fuel system assemblies used on recreational watercraft failed after a short time in service in a seawater environment. Examination of the assemblies revealed significant degradation of the polyacetal connectors of the wire subassemblies. Optical and microscopic evaluations indicated the complete loss of connector material implying decomposition of the resin, along with mud-cracking and a rough surface morphology signifying chemical attack. An elemental analysis performed on both an intact connector and degraded connector suggested a potential chemical agent in the form of zinc chloride. At elevated temperatures, concentrated zinc chloride solutions are known to decompose polyacetal resins. The source of the zinc chloride was established as corrosion products that resulted during the dezincification of the internal brass connector through exposure to saltwater in the application.     

平湖油气田古近系花港组低阻油层成因与识别分析

低阻油气层是一种非常规储层 ,其油气层电阻率与邻近水层电阻率接近 ,或有时低于水层的电阻率。通过对花港组H5砂层组的岩石类型、颗粒大小、粘土矿物的成分及其分布、孔隙结构、润湿性、地层水矿化度进行研究 ,表明该砂层组低阻的原因主要是由于高束缚水饱和度及高地层水矿化度引起的。     

沙角C电厂2号发电机转子接地检测装置改造

介绍沙角发电C厂2号发电机转子接地检测装置的基本原理和在装置发出报警信号后的分析和判断过程。对该装置出现故障后ALSTOM公司提出的临时检测方案作了分析，指出了该方案的不足之处，提出并实施改进后的临时检测方案。     

Microstructural Investigation on Failure of Internal Drive Shaft

17-4 PH stainless steel is used as internal drive shaft material in liquid engine pumps. One of the drive shafts failed during operation. The shaft pieces were in contact for short duration after failure, which has resulted in abrasion of fractured surfaces. Samples from the location of failure were taken, and investigation of the failure was carried out using optical and scanning electron microscopy. The microstructural analysis of the material and fractographic analysis of the fractured surface show that the failure was caused by excessive torsion.     

阳泉市煤矿采空区地质因素对公路的破坏

介绍了阳泉市煤矿采空区对公路建设所造成的危害，对其上覆岩层变形破坏的地质因素及其破坏机理作了分析，指出应该采取各种措施减少对公路的破坏。     

混凝土输送泵的常见故障及排除

介绍了混凝土输送泵的常见故障，阐述了混凝土输送泵墙管的排除方法，指出只有认真分析造成故障的各种原因，才能按照先外后内、先易后难的原则进行故障处理。     

巴彦浩特探区钻井液技术初探

巴彦浩特探区钻井液工艺技术的重点是，解决疏松砂砾岩地层水涌漏同层、侏罗系地层水的HCO3^-污染及可能出现的火成岩地层井塌复杂。结合内蒙古巴彦浩特探区地层和井身结构特点，采用了两性聚合物／氯化钾钻井液和氯化钾／石膏-聚磺钻井液体系。该体系抑制能力强，性能稳定．容易实现低固相、低密度近平衡钻井，保护储层效果好。对复杂情况采取了有针对性的处理办法：平稳操作和合理的钻井工程措施是预防水层涌漏同层和火成岩井塌复杂的重要手段；用井场易得的固井水泥或石膏配合烧碱处理HCO3^-污染简便易行；处理火成岩井塌复杂，控制合适的钻井液性能是必要的。     

防盐抽油泵的研制及在文留油田的应用

文留油田因其独特构造和地层特点，抽油井结盐严重，文中通过对油井结盐机理及抽油泵结盐主要形式、原因的分析，有针对性地开发了防盐抽油泵，并介绍了防盐泵的结构和主要技术特点，在实际应用中配套应用相应防盐技术，取得了较好的效果，极大地减少了盐卡泵现象，抽油井检泵周期得以延长，为其它油田类似油井生产管理提供了新方法。     

同沉积断裂带砂砾岩隐蔽油藏研究——以东营凹陷胜北断裂带为例

以构造层序、层序地层分析和基准面分析原理为手段,利用高分辨率地震剖面、测井、岩相等资料,重点研究了东营凹陷胜北断裂带深断陷型湖盆层序中的低位体系域砂体沉积特征、发育规律及其石油地质意义.研究表明,沙三期胜北断裂带的活动形成了断裂坡折带,该坡折带控制沙三段层序低位体系域冲积扇、扇三角洲、浊积扇和小型三角洲等砂体的发育及时空展布.断裂坡折带控制的低位体系域砂体位于层序底部、最大湖泛面之下,成藏条件优良,是隐蔽油气藏勘探的主要方向.      

潜油电泵易损零部件失效分析方法

通过对大庆油田近5 a潜油电泵易损零部件的数据统计,应用可靠性分析理论和方法研究了易损零部件的失效规律,得出4大部件的故障率占整个机组系统的91.7%,其可靠度由小到大的次序为电机、保护器、电泵和分离器。在这4大部件中,可靠度较低的零件主要有泵轴、叶导轮、扶正轴承、胶囊和保护器轴,其中泵轴、叶导轮、扶正轴承的主要失效模式是磨损,连接螺栓的主要失效模式是断裂失效。