对鞍钢股份无缝钢管厂连轧机前毛管坯横移装置存在的设计缺陷进行了分析,并提出改进方案,将原横移装置由高架轨道横移机构及上下升降链传动装置,改进为地面轨道横移系统及同步旋转臂实现取管、放管过程。实施后消除了生产故障,缩短了轧制周期,降低生产成本。     

脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。     

优化作业方式提高始极片质量

针对某厂铜电解种板工序存在的始极片质量波动较大的问题,从种板系统体积控制和添加剂匹配的角度出发,分析各种因素对始极片质量的影响,做出了相应的改进措施,使种板系统运行更加稳定,始极片质量得到进一步提升。     

Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.     

Hot corrosion Type II of FeCr‐based model alloys for boiler and heat exchanger applications

The hot corrosion Type II of the alloys FeCr20, FeCr20Ni10, FeCr20Ni20, and FeCr20Co10 is investigated at 700°C in air + 0.5% SO₂ with deposits consisting of Na₂SO₄ and a eutectic mixture of Na₂SO₄ and MgSO₄ for 24, 100, and 300 h. The alloying elements nickel and cobalt have a positive influence when tests are conducted using a MgSO₄‐Na₂SO₄ deposit. In this case, they reduce the metal loss and increase the time to the propagation stage. In contrast, when the alloys are exposed with a Na₂SO₄ deposit, these alloying elements increase the metal loss and allow for the transition to the propagation stage because they can form molten phases with the Na₂SO₄. During the incubation stage an oxide scale forms on the FeCr20 alloy, which is thicker than the one formed during exposure without a deposit, and iron oxides are observed, which precipitate in the deposit. The propagation stage occurs by a dissolution and precipitation mechanism forming localized pitting attack. Iron is the main species that dissolves and precipitates, while chromium remains mainly as an oxide beneath the initial surface. The additional elements are found in the pit and in the salt deposit.     

Fatigue limit evaluation of various martensitic stainless steels with new robust thermographic data analysis

Thermography represents an important tool to study fatigue behaviour of materials.In this work, the fatigue limit of martensitic and precipitation hardening stainless steels has been determined with thermographic methods. Despite their use in corrosive and cryogenic environments, there is a data lack in literature concerning the study of fatigue behaviour.The peculiarity of these materials is the brittle behaviour: therefore, during fatigue tests the characteristic small deformations determine small changes of temperature. Thus, to properly determine the fatigue limit of aforementioned stainless steels, a more accurate setup is necessary in order to correctly detect surface temperature of specimens due to dissipation heat sources.In literature, different procedures have already been proposed to evaluate the fatigue limit from thermal data but very few works lead to an early detection of dissipation process which can obtain a further reduction of overall testing time. The aim of the paper is to propose a new robust thermal data analysis procedure for estimating fatigue limit of stainless steels in automatable way.     

Slow strain rate technique for studying hydrogen induced cracking in 34CrMo4 high strength steel

Alloy hardened steels offer excellent combination of mechanical properties, hardenability and corrosion resistance. 34CrMo4 is a medium carbon, low alloy steel widely used due to a good combination of high-strength, toughness and wear resistance. However, this steel experiences hydrogen embrittlement (HE), a complex phenomenon depending on the composition and microstructure. This work estimates de loss of the mechanical properties caused by hydrogen in electrochemically H-charged specimens in absence of mechanical stress but also, at low strain rate and constant load. H-charging for 2 and 6 h induce YS losses of about 40% and 71% and UTS losses of 39% and 59%, respectively. The synergistic effect of the stress and the H-charging process leads to a higher loss, 91%, and a faster brittle fracture even though hydrogen content is similar to those firstly H-charged and then tested in air.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

Corrosion of hot-dip-galvanised steel and zinc alloy-coated steel in ammonia and ammonium chloride

There are many potential causes of corrosion in animal buildings. Animals exhale large quantities of moisture into the air creating high relative humidity in the building if the moisture is not properly vented. High humidity increases the potential for condensation. In addition, ammonia may be found in large quantities in animal buildings. Ammonia is released from manure and urine. In addition, ammonium chloride is used as a nitrogen source in fertilisers. In this study, the atmospheric corrosion of hot-dip-galvanised steel and zinc alloy-coated steel such as zinc–aluminium and zinc–aluminium–magnesium has been studied in atmospheres containing different levels of ammonia. Investigations have also been conducted at different levels of ammonium chloride. The results are discussed in view of the mechanisms of corrosion of zinc and zinc alloy-coated steel in ammonia and ammonium chloride-containing environments.