Spray coating process variable and property analysis of UV-curable polyurethane acrylate coating on polycarbonate substrate

A series of spray coating experiments were conducted on an UV-curable, polyurethane-modified, acrylate-based coating formulation with the aim to control defects, coating thickness, and thickness variation. Statistical approaches including design of experiment, residual examination, analysis of variance, and t-test were used in designing the experiments and analyzing data. Viscosity of formulation, atomizing pressure, liquid feeding pressure, distance between nozzle and substrate, and travel speed of substrate were the process variables studied. The ranges of process variables that gave defect-free coating were identified and used in the subsequent experiments to determine process variables and interactions that had significant contribution to the changes in coating thickness and thickness variation. All process variables studied were found to have contribution to the change in coating thickness, but they showed no significant contribution to the variation of coating thickness. No interaction displayed significant contribution. Confirmation tests performed on extra samples prepared with varying coating thicknesses indicated a good agreement with the experimental results. Additional samples were tested for total transmittance, transmission haze, adhesion, surface roughness, hardness, scratch hardness, abrasion resistance, and durability to attack of car wash chemicals. Spray coated samples showed slight improvement in the total transmittance over the uncoated samples, while maintaining the transmission haze and exhibiting rougher surfaces. Only samples with thin coatings were found to possess sufficient adhesion to the substrate. These thin coatings gave improved hardness, scratch hardness, and durability to car wash attack to the level comparable to commercial coated polycarbonate headlamp lenses, whilst giving better abrasion resistance.     

积分中值屈服准则解析厚板轧制椭圆速度场

为解决非线性Mises比塑性功率积分困难以及由此导致的轧制功率解析式难以获得的问题,本文通过建立并利用线性比塑性功率表达式对提出的椭圆速度场进行能量分析,得到了轧制力能参数的解析解.文中通过对变角度屈服函数求积分中值,构建了一个新的屈服准则,它是主应力分量的线性组合,在π平面上的轨迹是逼近Mises圆的等边非等角的十二边形,其基于Lode参数表达式的理论结果也与实验数据吻合较好.同时,根据厚板轧制时金属流动速度从入口到出口逐渐增大的特点,提出了水平速度分量满足椭圆方程的速度场,该速度场满足运动许可条件.通过相应的轧制能量分析,获得了基于线性屈服准则的内部变形功率以及基于应变矢量内积法上的摩擦功率与剪切功率.在此之上,通过泛函的极值变分导出了轧制力矩、轧制力以及应力状态系数的解析解,并与现场实测数据进行了对比,结果表明利用本文提出的屈服准则与速度场所建立的轧制力矩与轧制力模型与实测值吻合较好,其中轧制力误差小于5.3%,轧制力矩误差在6%左右.     

Contribution of metal vapor mass at periphery part of pulsed arc to electromagnetic force in weld pool

The arc welding has been used in various welding methods because it is inexpensive and high in strength after welding. However, it is a problem that accidents such as collapse of the bridge occur because of the welding defects. The welding of low cost and high productivity is required without the welding defects. The pulsed TIG welding is inexpensive and capable of high‐quality welding. The electromagnetic force contributing to penetration changes because the transient response of arc temperature and iron vapor generated from anode occurs. However, the analysis of pulsed TIG welding with metal vapor has been elucidated only metal vapor concentration near anode with transient phenomenon and heat flux. Thus, the theoretical elucidation of penetration depth with control factor has not been researched. In this paper, the contribution of metal vapor mass at the periphery part of pulsed arc to the electromagnetic force in the weld pool is elucidated. As a result, the iron vapor mass at periphery part decreased with increasing the frequency. The iron vapor was stagnated at axial center within one cycle. The electromagnetic force to the penetration depth direction in weld pool increased at axial center. Therefore, the metal vapor mass at periphery part plays an important role for the electromagnetic force increment at axial center.     

Numerical Investigation of the Capture of Polydisperse Particles by Charged Droplets

The capture of particles by charged droplets was simulated by considering the electrostatic interactions of droplet-droplet and droplet-particle. The results indicate that the electrostatic repulsion between droplets leads to a dynamic accumulation mode of particles. However, the droplet spacing has an insignificant effect on the capture efficiency when the electrostatic deposition predominates. The increase of droplet charge remarkably improves the capture efficiency, in which the capture of fine particles accounts for the largest proportion. Compared to the droplet charge, the droplet size shows a limited improvement in the capture efficiency. Reducing the droplet velocity prolongs the capture time instead of enhancing the capture capacity per unit time, thereby improving capture efficiency.     

Ergonomically based design of tractor control tools

Musculoskeletal injuries are well-known disorders among the agricultural tractor operators. Overexertion is a critical factor which can agitate these injuries. Physical body characteristics should be measured for an ergonomically best-fit-optimal design for the operators. In this study, a designed setup was employed to derive the applied forces by tractor operators on the control tools. The different muscle strengths including leg/foot strength, hand push/pull strength, and torque strength applied by both hands were measured. A comparison was made for the obtained values for different strengths by considering the effects of hand dominance. The obtained data were used to estimate the maximum allowed forces in these tools. In contrast to the previous studies, the minimum allowed actuating forces of the pedals were calculated using reasonable assumptions. These values could provide more comfort and less exhaustion for the tractor operators. The obtained ranges were benchmarked against corresponding recommended values in some standards (ISO, ISIRI, and ASABE family). The results revealed the unsuitability of evaluated standards for a proper design and the excessive overestimation of those recommended values (in some cases more than 3 times). In all of the design procedure, a suitable attention was paid to accommodate it with more than 90% of target population.Relevance to industryA prosperous industry which considers ergonomic factors in the design of agricultural machine workplace can overcome the disorders and generate more comfort. Evaluating more exact mechanical forces can result in a suitable design of workplace.     

Growth,mechanical properties,and tribological performance of TiAlN/NbN and NbN/TiAlN bilayer coatings

Three different coatings, namely TiAlN, TiAlN (external)/NbN (internal) and NbN (external)/TiAlN (internal), were deposited on cemented carbides by arc ion plating. The comparative investigation conducted in this study elucidates the effect of the NbN layer and coating systems on the growth, mechanical properties, and tribological performance of the coatings. The results showed that the surface of the TiAlN and TiAlN/NbN coatings was smoother when TiAlN served as the external layer. The NbN/TiAlN coating, wherein NbN formed the external layer, had a much rougher but more symmetrical surface. With the introduction of the NbN layer, the increased micro stress induced a lower adhesion strength in the TiAlN/NbN and NbN/TiAlN coatings. The TiAlN/NbN and NbN/TiAlN coatings exhibited higher hardness and hardness/effective elastic modulus (H/E*). During the friction test, when the temperature was elevated to 700 °C, the tribological performance of the monolayer TiAlN coating was the lowest because of the TiO₂-induced breakage of the dense tribo-oxide film. The NbN layer participated in the formation of a NbO_x film at elevated temperatures, which was responsible for the high tribological performance of the two bilayer coatings. When the NbN layer was on the outermost layer and in direct contact with the elevated temperature atmosphere, the NbN/TiAlN coating generated a tribo-oxide film with high integrity, and its coefficient of friction decreased by 27% of that at room temperature. Therefore, the NbN/TiAlN coating exhibited the highest wear resistance at 700 °C.     

Selective Coating of SnS on the Bio‐Inspired Moth‐Eye Patterned PEDOT:PSS Polymer Films

A new strategy for the selective coating of tin sulfide (SnS) on the surface of moth‐eye patterned (MEP) conducting polymer film is studied by considering the optical properties of the antireflective moth‐eye pattern and flexibility of polymer films. The semiconductor SnS is selectively coated on the surface of MEP microdomes of poly(3,4‐ethylenedioxythiophene) poly(styrene‐sulfonate) (PEDOT:PSS) film. The SnS coated MEP film is obtained by using pore selectively SnS thin layer functionalized polystyrene honeycomb‐patterned porous (HCP) film as a template. Aqueous PEDOT:PSS solution is poured on the SnS functionalized HCP films and detached for the fabrication of SnS coated MEP films. The films show a satisfactory photo‐responsive property under solar stimulated light illumination due to the antireflective MEP structure of PEDOT film and homogenous SnS coating on the surface of the conducting polymer.     

Quantitative investigation of electromechanical coupling of potassium sodium niobate-based thin films

High-performance environment-friendly piezoelectric potassium sodium niobate (KNN)-based thin films have been emerged as promising lead-free candidates, while their substrate-dependent piezoelectricity faces the lack of high-quality information due to restraints in measurements. Although piezoresponse force microscopy (PFM) is a potential measuring tool, still its regular mode is not considered as a reliable characterization method for quantification. After combining machine-learning enabled analysis using PFM datasets, it is possible to measure piezoelectric properties quantitatively. Here we utilized advanced PFM technology empowered by machine learning to measure and compare the piezoelectricity of KNN based thin films on different substrates. The results provide a better understanding of the relationship between structures and piezoelectric properties of the thin films.     

Separation of hematite from banded hematite jasper (BHJ) by magnetic coating

The separation of iron oxide from banded hematite jasper(BHJ) assaying 47.8% Fe, 25.6% Si O2 and 2.30%Al2O3 using selective magnetic coating was studied. Characterization studies of the low grade ore indicate that besides hematite and goethite,jasper, a microcrystalline form of quartzite, is the major impurity associated with this ore. Beneficiation by conventional magnetic separation technique could yield a magnetic concentrate containing 60.8% Fe with 51% Fe recovery. In order to enhance the recovery of the iron oxide minerals, fine magnetite, colloidal magnetite and oleate colloidal magnetite were used as the coating material. When subjected to magnetic separation, the coated ore produces an iron concentrate containing 60.2% Fe with an enhanced recovery of56%. The AFM studies indicate that the coagulation of hematite particles with the oleate colloidal magnetite facilitates the higher recovery of iron particles from the low grade BHJ iron ore under appropriate conditions.