高镁边缘磷矿制取阻燃剂氢氧化镁的工艺

为解决大量的高镁低磷边缘磷矿废渣堆存对环境的影响,开发了以其为原料制取阻燃剂氢氧化镁工艺.该工艺主要包括酸解磷矿和镁沉淀过程,重点讨论了沉淀氢氧化镁过程中时间、温度、氨镁摩尔比n(NH3/MgO)等多种因素的影响,得到的最佳工艺条件是:反应温度65℃,反应时间80min,n(NH3/MgO)为5∶ 1,镁的沉淀效率为80%.     

水喷雾灭火系统在电信枢纽工程燃气锅炉房的应用

分析了燃气锅炉的火灾危险性和水喷雾用于燃气锅炉消防的灭火机理,提出了水喷雾灭火系统的设计参数的选择、系统的控制方法以及在设计中可能涉及到的问题和注意事项,并结合工程实例进行了探讨。     

高合金钢铸造用涂料的试制与开发

介绍了炉爪用合金钢1Cr25Ni20Si2Re,导板用合金钢2Cr32Ni5采用串箱铸造过程中，有关镁砂粉涂料和石英粉涂料的试制。结果表明：镁砂粉涂料为不透气涂料，不太适用，而合理配方的石英粉涂料使用性能良好。     

Experimental Study on Polymer Artificial Bone with HA Coated and Fiber Liners

1Introduction HA(hydroxyapatite)wasakindofbioactiveceram ics,whichhadexcellentbiocompatibilityandtissueaffin ityinthatitscomponentsweresimilartothoseofhuman bone[1].Soitwasthebestknownhumanbonesubstitute,andunprecedentedeffecthadbeenharvestedinrecenttwo d…     

Plasma Sprayed Hydroxyapatite Coatings with Nano-hydroxyapatite Prepared by Ultrasonic Precipitation Process

Nano-particle hydroxyapatite （ HA ） was prepared with a novel ultrasonic precipitation process and the as-prepared nanopowder was used to produce hydroxyapatite （ HA ） coatings on titanium substrate via plasma spraying. The phase and the microstructare of the coating were characterized by X- ray diffraction （XRD） and scanning electron microscopy （SEM）. Results showed that spherical particles could be prepared by ultrasonic precipitation process; and a corresponding dense HA coating with molten surface and low-porosity cross-section structure was acquired. During the plasma spraying process, new phases of Ca3 （ PO4 ）2 and Ca2 P2O7 were generated. After heat-treating at 800℃ for 1 h, the contents of Ca3 （ PO4 ）2 and Ca2 P2O7 decreased while HA content increased. Tensile adhesion tests showed that the plasma sprayed coating prepared with the spherical nanoparticles exhibited high tensile bond strength.     

Water‐Stable,Magnetic Silica–Cobalt/Cobalt Oxide–Silica Multishell Submicrometer Spheres

A method to produce monodisperse magnetic composite spheres with diameters from less than 100 nm to more than 1 μm in water solution is reported. The spheres consist of a dielectric silica core and a cobalt/cobalt oxide shell which can be protected from further oxidation with an outer shell of silica or, alternatively, they can be covered with the polymer polyvinylpyrrolidone as a stabilizer. The formation of a uniform magnetic shell proceeds with the adsorption of metallic cobalt seeds, produced by the reduction of cobalt chloride with sodium borohydride, on a self‐assembled layer of polyelectrolytes on the silica core. In the second step, an outer silica shell can be formed by the hydrolysis and condensation of (3‐aminopropyl)trimethoxysilane and tetraethoxysilane. The double‐shell composite spheres show excellent sphericity, monodispersity, and a magnetic hysteresis loop at room temperature.     

激光辐照制备搪瓷涂层

激光辐照制备的搪瓷涂层表面粗糙,与金属基材结合牢固。一般由 Si,Al,Na,K,B,F,O等元素组成。在激光辐照过程中 K,Na 明显地挥发,从而在涂层中的含量明显减少;Co,Ni,主要分布在界面附近;Fe 元素也由基材进入涂层,呈梯度状分布,在界面过渡区含量很高,在涂层内含量很低。搪瓷涂层的形成与激光辐照参数,特别与激光功率间存在极为密切的关系;只有选用合理的参数,才能制得搪瓷涂层。     

防腐涂料及涂装技术(Ⅷ)

防腐涂料及涂装技术讲座系列介绍防腐蚀涂料的品种和各类应用及最新产品研究进展。本讲主要介绍涂装前的表面预处理方法及表面处理质量的评定等     

钠冷快堆中喷雾钠火的计算分析

根据钠冷快堆中喷雾钠火的特点建立了理论模型，编制了SSPRAY程序。该程序模拟钠喷雾燃料过程中钠滴的运动、钠和氧气的燃烧反应、热量传递和质量传递等瞬态过程。用该程序计算了气体和墙壁温度、气体压力、氧气摩尔份额、喷雾流燃烧速率和热量热递速率等主要参数。利用AI实验数据和美国SPRAY－3A的计算结果对程序进行了验证，结果符合较好。     

高发射率节能涂料及其应用

讨论了高发射率涂料节能的条件，了一种在1000℃仍保持高发射率的优质涂料，并解决了涂料与金属基体的粘结工艺，用此涂料制成增强辐射电阻带和复合炉衬，得到的新炉比旧炉节能20－40％。