Effect of calcination conditions on phase formation and particle size of nickel niobate powders synthesized by solid-state reaction

The solid-state mixed oxide method via a rapid vibro-milling technique is explored in the preparation of single-phase nickel niobate (NiNb₂O₆) powders. The formation of the NiNb₂O₆ phase in the calcined powders has been investigated as a function of calcination conditions by TG-DTA and XRD techniques. Morphology, particle size and chemical composition have been determined via a combination of SEM and EDX techniques. It has been found that the minor phases of unreacted NiO and Nb₂O₅ precursors and the Ni₄Nb₂O₉ phase tend to form together with the columbite NiNb₂O₆ phase, depending on calcination conditions. More importantly, it is seen that optimization of calcination conditions can lead to a single-phase NiNb₂O₆ in an orthorhombic phase.     

Potential of vibro-milling technique for preparation of electroceramic nanopowders

The potential of the vibro-milling technique as a simple method to obtain usable quantities of single-phase electroceramic powders with nanosized particles was examined. A detailed study considering the role of both milling time and firing condition on phase formation and particle size of the final product was performed. The calcination temperature for the formation of the desired phase was lower when longer milling times have been applied. More importantly, by employing an appropriate choice of the milling time and calcination condition, high purity electroceramic nanopowders have been successfully prepared with a simple solid-state reaction method.     

Formation of composites fabricated by exothermic dispersion reaction in A1-TiO2-B2O3 system

The formation of aluminum matrix composites fabricated by exothermic dispersion reaction in A1-TiO2-B2O3 system was investigated. The thermal analysis results show that the reactions are spontaneous and exothermic. The Gibbs free energy of α-Al2O3 is the lowest among all the combustion products, followed by TiB2 and Al3Ti. It is noted that when the B2O3/TiO2 mole ratio is below 1, the reaction products are composed of particle-like α-Al2O3, TiB2 and rod-like Al3Ti. The α-Al2O3 crystallites, resulting from the reaction between A1 and TiO2 or B2O3, are segregated at the grain boundaries due to a lower wettability with the matrix. SEM micrographs show that rod-like Al3Ti phase distributes uniformly in the matrix. When the BEO3/TiO2 mole ratio is around 1, the Al3Ti phase almost disappears in the composites, and the distribution of α-Al2O3 particulates is improved evidently.     

Hydrothermal Reaction Mechanism and Pathway for the Formation of K2Ti6O13 Nanowires

Calculations and detailed first principle and thermodynamic analyses have been performed to understand the formation mechanism of K₂Ti₆O₁₃ nanowires (NWs) by a hydrothermal reaction between bulk Na₂Ti₃O₇ crystals and a KOH solution. It is found that direct ion exchange between K⁺ and Na⁺ plus H⁺ interactions with [TiO₆] octahedra in Na₂Ti₃O₇ promote the formation of an intermediate H₂K₂Ti₆O₁₄ phase. The large lattice mismatch between this intermediate phase and the bulk Na₂Ti₃O₇ structure, and the large energy reduction associated with the formation of this intermediate phase, drive the splitting of the bulk crystal into H₂K₂Ti₆O₁₄ NWs. However, these NWs are not stable because of large [TiO₆] octahedra distortion and are subject to a dehydration process, which results in uniform K₂Ti₆O₁₃ NWs with narrowly distributed diameters of around 10 nm.     

高镁边缘磷矿制取阻燃剂氢氧化镁的工艺

为解决大量的高镁低磷边缘磷矿废渣堆存对环境的影响,开发了以其为原料制取阻燃剂氢氧化镁工艺.该工艺主要包括酸解磷矿和镁沉淀过程,重点讨论了沉淀氢氧化镁过程中时间、温度、氨镁摩尔比n(NH3/MgO)等多种因素的影响,得到的最佳工艺条件是:反应温度65℃,反应时间80min,n(NH3/MgO)为5∶ 1,镁的沉淀效率为80%.     

Research on charge ordering and magnetic properties in La0.3Ca0.7Mn1-xWxO3 system

The perovskite manganite sample La0.3Ca0.7Mn1-xWxO3 （x = 0.08, 0.12） was prepared by the solid-state reaction method. The effect of W doping on the Mn site to La0.3Ca0.7MnO3 charge ordering phase and the changing process of magnetic properties were studied through the measurement of the M-T curve, M-H curves, and ESR curves of the sample. The results showed that when x = 0.08, the charge ordering （CO） phase exists in the system, the transition temperature Tco= 275 K, and the system exhibits PM when T 〉 275 K. The system transforms from spin-disordering paramagnetism to spin-ordering antiferromagnetism in the charge ordering state with the temperature decreasing from 275 K to 230 K. The long-range antiferromagnetism forms and AFM/CO states coexist between 230 K and 5 K. There is a little ferromagnetic component in the AFM/CO background in a low temperature range. When x = 0.12, the CO phase in the system has almost melted completely. There is a little remnant of the CO phase below 150 K. The system exhibits paramagnetism when T 〉 150 K and transforms from paramagnetism to ferromagnetism when T〈 150 K.     

靶向抗癌药格列卫与其治疗白血病疗效监测

Gleevec是抑制致癌的融合蛋白BCR-ABL的一种分子靶向治疗药物,BCR-ABL是一种与慢性髓细胞性白血病(CML)有关的酪氨酸激酶抑制剂。用Gleevec选择性地抑制BCR-ABL活性在治疗CML中显示出很好的效果,特别是在CML慢性期,因此,监测疗效非常重要。现就Gleevec的研究进展及如何监测其在CML中的疗效作一简单综述。     

沸石孔结构对1-己烯异构化性能的影响

采用1-己烯为原料,对硅铝比相近、不同孔结构的沸石在脉冲微反装置上进行了评价试验,考察了FCC条件下沸石孔结构对烯烃异构化性能的影响。结果表明,大孔径的Y型沸石具有良好的异构化性能,异构化能力由强到弱的排列顺序为Y>β>ZRP>丝光沸石>镁碱沸石。     

MDI聚氨酯/聚硅氧烷IPN的结构与力学性能

用MDI聚醚氨酯和含少量苯基的聚二甲基硅氧烷合成了一系列的聚氨酯／聚硅氧烷IPN阻尼弹性体，研究了材料的结构与力学性能．结果表明，当聚氨酯与聚硅氧烷的质量比为90：10时。IPN的抗张强度达41．57MPa，断裂伸长率为376％，并具有良好的阻尼性能，玻璃化转变温度范围大于80℃．聚氨酯／聚硅氧烷IPN具有细微的微相分离结构，聚硅氧烷在IPN中的微相尺寸为微米级，并趋向于分布在IPN的表面．     

Motor fluency deficits in the sequencing of actions in schizophrenia.

Many everyday activities depend on the capacity to organize and smoothly execute motor sequences. The authors tested the hypothesis that a sequencing deficit is associated with schizophrenia. They used a new method to distinguish between lower and higher order mechanisms for the impairment. The 1st task involved triggered sequences in which sensory information from 1 movement was the cue for initiation of the following movement. Results showed that the motor sequences were performed as fluently in patients as in controls. The 2nd and 3rd tasks involved sequences in which the entire movement sequence could be preplanned. Patients executed the sequences less fluently than controls but only under the condition where action sequences were required. Furthermore, the patients' fluency deficit increased with sequence complexity. The high discrimination power of Task 3 gave the authors a means to control for a potential psychometric confound involving differential discriminating power and to argue in favor of a specific higher order motor fluency deficit in patients with schizophrenia. It is suggested that basic lower order mechanisms that integrate sensory information with outgoing motor commands are preserved in schizophrenia, whereas higher order integrative mechanisms that are required for the smooth coordination of motor sequences are impaired. (PsycINFO Database Record (c) 2010 APA, all rights reserved)