关于氟化氢生产中原料混合问题的讨论

在无水氟化氢生产原料中，添加了发烟硫酸作为新原料。由于液体原料混合方法的不同，在生产中会产生不同的效果。本文介绍了预混合法和在线混合法的优缺点。     

Thermooxidative degradation of natural rubber/clay composite

The clay is treated with a reducing agent and an acid so as to obtain a clay containing various metal components with a variable‐valence state. Then, the clay is coprecipitated with natural rubber (NR) latex to prepare a vulcanized NR/clay composite. The degradation process of the NR/clay composite under hot air condition was studied dynamically by using a Fourier transform infrared spectrometer attaching an in situ sample cell and was also investigated using the TGA method. The test result obtained from the infrared spectrometry indicated that under low decomposition temperature, the decomposition products of the test samples mainly are ethylene, low molecular olefinic hydrocarbon, and carbonyl compounds. As the decomposition temperature rises, the low molecular olefinic hydrocarbon content decreases, the olefine with longer chain is formed, and a lot of alkane decomposition products are formed at the same time. When the content of the metal components with a variable‐valence state in clay such as Cu, Mn, Co, and Fe increases, the oxidation products containing the carbonyl group, the olefinic hydrocarbon, and CO₂ in the decomposition product of the test sample also increase. The TGA result clearly shows a shoulder peak that appears by the side of the main peak on the DTG curve of NR/clay composite. With the increase in the content of metal components with variable‐valence state in clay, the initial degradation temperature of the test sample (T₀), the degradation peak temperature (T_p1), and the final degradation temperature (T_f1) in first‐stage reaction, as well as the degradation peak temperature (T_p2) and the last final degradation temperature (T_f) in second‐stage reaction of all the test samples more or less shift to the direction of low temperature; besides, the activation energy (E) of the reaction of the test samples more or less decreases. This means that the metal components with variable‐valence state promote the oxidative degradation of the clay–rubber masterbatch. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 3809–3815, 2006     

吸附强化的甲烷水蒸汽重整制氢反应特性

在实验室固定床反应器上研究了采用复合催化剂的吸附强化甲烷水蒸汽重整制氢反应,对吸附强化制氢反应条件进行了考查,得到了实验室条件下的最佳反应条件为温度600～640 ℃,压力0.2 MPa,水碳比4～5.在600 ℃,0.2 MPa,水碳比5的条件下,吸附强化段H2含量高达95.39%,吸附强化段CH4转化率达到81.37%,相对于理论平衡值的吸附强化因子达到26.76%.     

"绿色"电器灌封材料的研制

本文的目的是研究一种低挥发性、绿色环保型灌封材料,经测试灌封材料的性能为材料沸点192℃;拉伸剪切强度18.4MPa、冲击强度(无缺口)12.8kJ·m-2、弯曲强度82.7MPa;线性膨胀系数2.98×10-5℃-1;体积电阻率4.7×1016Ωcm;灌封元件经-50～l50℃3次温度循环后树脂本身不开裂、树脂与元件粘结处不开裂.     

炭/炭复合材料MoSi2/SiC抗氧化涂层的研究

采用包埋法制备C／C复合材料抗氧化MoSi2／SiC梯度涂层，同时对抗氧化涂层的形成、组织结构以及抗氧化性能与渗料的关系和抗氧化机理进行了研究。结果表明：采用包埋法制备的C／C复合材料抗氧化MoSi2／SiC梯度涂层致密，但有少量裂纹，涂层有良好的抗氧化效果。当Si与SiC保持一定的比例时，渗料中MoSi2的含量为50％时，涂层具有最好的抗氧化效果；当MoSi2与SiC保持一定的比例时，渗料中Si的含量为20％时，涂层具有最好的抗氧化效果。     

尖晶石质浸入式水口内衬的研究

以77%的电熔尖晶石(粒度≤1mm和≤0.074mm)、20%的α-Al2O3(≤2μm)和3%的电熔镁砂(≤0.074mm)为原料,分别在1000℃、1200℃、1500℃保温3h的条件下,研究了SiO2微粉外加量(分别为0、0.5%、1.0%、1.5%)对尖晶石材料烧结性能的影响,并在1450℃的还原性气氛下进行了尖晶石内衬材料与铝碳本体材料的复合试验。研究结果表明:在不过多增加尖晶石材料高温液相量的情况下,SiO2微粉的外加量为1.0%较为适宜;在尖晶石试样中同时添加1%SiO2微粉和3%电熔镁砂细粉能很好地降低其烧结温度,而且其热膨胀率与铝碳材料的热膨胀率较为接近,而尖晶石材料与铝碳材料的复合试验结果也表明,内衬和本体材料结合完好,且无裂纹出现。     

太阳能供热系统优化设计的相关问题研究

随着我国建筑总量和建筑能耗的快速增长,传统的供热方式已难以满足建筑供热的需求,而利用太阳能为建筑物供热,则可获得良好的节能和环保效益。就太阳能供热系统优化设计的相关问题进行了分析和研究,以期能为太阳能供热技术的推广和应用提供一定的理论依据。     

硼酸镁晶须的合成研究

报道了硼酸镁晶须的合成研究结果。硼酸镁晶须是一种性能价格比高的晶须产品，利用熔盐法合成出长10—50μm、直径0．5—2μm的硼酸镁晶须。还就硼酸镁晶须增强复合材料的研究和硼酸镁晶须工业化的前景作了展望。     

MES捕获CO2及高效催化转化研究进展

微生物电合成(Microbial electrosynthesis，MES)为二氧化碳还原为乙酸盐和其他多碳物提供了一条可持续的生化转化途径，利用电能驱动微生物固定CO2具有原料容易、操作条件温和、不含有毒物质、环境可持续性等特点，为全球碳中和、碳减排带来了新机遇。在研究人员对提高产率、转化效率、碳链延长方面的深入研究下，基于对电极材料的选择、修饰，菌群的驯化，操作条件的限制，乙酸最高产率达1330g/(m2?d)，催化转化C1废气并耦合二次发酵生产了C2-C4产物以及具有更长碳链的中链脂肪酸。在概述阴极电活性微生物吸收胞外电子的分子机制捕获和转化CO2的基础上，综述了合成有机酸的代谢原理、二维和三维等电极材料使用现状以及提高产物产率、产物及碳链延长的方法，并对未来MES的研究方向做出了展望。     

关于高氮尿素磷肥工艺的试验研究

介绍一种用尿素生产高氮磷肥的新工艺 ,分析该工艺的技术参数和影响因素。新工艺克服了过磷酸钙和尿素直接相混时会释放出结晶水的局限性 ,所得产品不仅可以作为复肥生产的原料 ,而且可以直接喷浆造粒生产NP复肥 ,因而具有良好的实用性