仿生矿化的研究Ⅰ．文石型碳酸钙的合成

在聚乙二醇（ＰＥＯ）存在下，ＣａＣｌ２和Ｎａ２ＣＯ３反应生成了类似红鲍鱼壳的含有ＰＥＯ的碳酸钙──高聚物复合材料。Ｘ－衍射和电镜照片显示，它有两种微观结构：外层为文石型和方解石型结构，内层为针状文石型结构。热重分析表明，该材料中含有３％左右ＰＥＯ。结果说明，聚合物对碳酸钙晶核的形成和晶体的生长有很大影响，并对其形成机理进行了初步探讨。     

Nitric oxide reduction and carbon monoxide oxidation over carbon-supported copper-chromium catalysts

Carbon supported copper-chromium catalysts are shown to be very active for both the reduction of nitric oxide with carbon monoxide and the oxidation of carbon monoxide with oxygen. Mixed copper-chromium oxide active phases have good activity in the simultaneous removal of nitric oxide and carbon monoxide from exhaust gases. The influence of several catalyst variables has been investigated. The activity per volume of catalyst increases with increasing loading, while the intrinsic activity shows a maximum around C/M=100−50. An optimum catalyst for nitric oxide reduction and carbon monoxide oxidation has a copper/chromium ratio of 2/1. The apparent activation energy for the carbon monoxide oxidation over carbon supported copper-chromium catalysts is 77 kJ/mol, suggesting that the Cu---O bond rupture is the rate-limiting process. The reduction of nitric oxide takes place at higher temperatures. Since all catalysts have a low selectivity for molecular nitrogen formation at lower temperatures, the dissociation of nitric oxide is probably rate determining, resulting in a slightly reduced catalyst system. In an excess of carbon monoxide the reaction is first-order in nitric oxide and zero-order in carbon monoxide. Moisture inhibits the reaction by reversible competitive adsorption, whereas carbon dioxide does not. Oxygen completely inhibits the reduction of nitric oxide due to the more rapid reoxidation of the catalytic sites compared to nitric oxide. Therefore, the reduction of nitric oxide takes place only when all oxygen has been converted and, hence, is shifted to higher temperatures. As a possible consequence, the production of nitrous oxide is reduced. Nitric oxide and molecular oxygen react preferentially with carbon monoxide, so, in an excess of oxidizing component, gasification of the carbon support occurs at higher temperatures after carbon monoxide has been completely consumed.     

高质量ZnO薄膜的退火性质研究

在LP－MOCVD中，我们利用Zn(C2H5)2作Zn源，CO2作氧源，在（0002）蓝宝石衬底上成功制备出皮c轴取向高度一致的ZnO薄膜，并对其进行500℃-800℃四个不同温度的退火。利用XRD、吸收谱、光致发光谱和AFM等手段研究了退火对ZnO晶体质量和光学性质的影响。退火后，（0002）ZnO的XRD衍射峰强度显著增强，c轴晶格常数变小，同时（0002）ZnOX射红衍射峰半高宽不断减小表明晶粒逐渐增大，这与AFM观察结果较一致。由透射谱拟合得到的光学带隙退火后变小，PL谱的带边发射则加强，并出现红移，蓝带发光被有效抑制，表明ZnO薄膜的质量得到提高。     

氧化钨物理特征的测量

对铵钨青铜（ATB）、氢钨青铜（HTB），紫色氧化钨（TVO）和蓝色氧化钨（TBO）四种氧化钨粉的氮气吸附/脱附等温线数据的分析。可以得出其表面积，微孔体积，微孔分布，中孔体积，平均孔径和分数维数。吸附/脱附等温线数据的分析表明，TVO粉末具有最大的中孔体积，最小的微孔体积，最窄的孔径分布，最小的分数维数和最大的平均孔径，其有利于氢还原制取超细钨粉，而不利于掺杂工艺，HTB粉末具有最大的微孔体积，最宽的孔径分布，最高的分数维数和最小的平均孔径，对于掺杂工艺来说是有利的，ATB和ABO的上述参数界于TVO和HTB之间。结果表明，利用吸附/脱附等温线来研究氧化物的物理特征是一个很好的方法；在氧化钨用于氢还原工艺和掺杂工艺之前必须研究其物理特征。     

多层薄膜结构气敏效应研究

在SnO2气敏薄膜层上覆盖一层或多层钝化材料（SiO2,Al2O3) 薄膜，制成的多层膜气敏元件，可很好地排除大分子气体如乙醇等对小分子H2检测的干扰，使其具有单独检测H2的功能。本文还通过测量元件的升温曲线，推导出敏感体表面的氧吸附活化能；找出活化能与灵敏度、选择性的关系。根据实验现象和物性分析结果，试着探讨了元件的敏感机理。     

用菱锌矿制取轻质氧化锌的研究

介绍了以菱锌矿为原料生产轻质氧化锌的方法，论述了反应酸浓度，煅烧温度，溶液PH值对实验的影响，并对生产工艺条件进行了研究。其工艺流程是将粉碎后的菱锌矿进行循环酸浸，净化后再直接和碳化母液反应，经沉降后再煅烧分解为轻质氧化锌，产品质量符合国家标准，视比容大，活性强，成本低，经济效益显著。     

The Synthesis of Sulfated Titanium Oxide Nanotubes

TiO₂ nanotubes can be prepared in gram quantities by treating anatase TiO₂ powder with concentrated NaOH solution. These TiO₂ nanotubes acquired strong acidity after being impregnated with sulfuric acid solution and calcined at 300 °C. The anatase TiO₂ powder used to prepare the nanotube did not catalyze the esterification between cyclohexanol and acetic acid, while sulfated TiO₂ nanotubes were very reactive toward the esterification reaction.     

Growth Stresses in the Oxide Scales on TiAl Alloys at 800 and 900°C

In the oxidation of TiAl alloys, the role of scale-growth stresses formed during oxidation has, thus far, been unknown. In the present paper the oxide-growth stresses were investigated by the deflection-test method in monofacial oxidation (DTMO) accompanied by acoustic-emission measurements. On unmodified surfaces the growth stresses are compressive and reach levels of around –100 MPa. At the same time, significant acoustic emission occurs indicating that even under isothermal conditions, stresses are relieved by a scale-cracking mechanism. For oxide scales on TiAl surfaces, which had been ion implanted with chlorine before oxidation, a very thin protective alumina layer is formed which, however, develops growth stresses in the range of several GPa, accompanied by intensive acoustic emission. In all stress–time curves, a dynamic situation is observed. This consists of phases of stress relief by scale microcracking and phases of stresses increase due to crack healing and further oxide growth. As a result, the level of stress as a function of oxidation time, is characterized by an oscillating course.     

熔融碳酸盐燃料电池阴极材料的导电性

通过交流阻抗方法研究了熔融碳酸盐燃料电池阴极材料锂镍氧化物、锂钴氧化物和锂铁氧化物的导电性能。结果表明:锂镍氧化物电极的导电性最好,锂钴氧化物电极的导电性次之,锂铁氧化物电极的导电性最差;它们的导电性都随着温度的升高而按指数规律增加;在合成锂钴氧化物(或锂铁氧化物)的过程中,使Li2CO3轻微过量,可以提高锂钴氧化物(或锂铁氧化物)电极的导电性,而且在同一温度下,随着nLi∶nCo(或nLi∶nFe,摩尔比)值的增大,锂钴氧化物(或锂铁氧化物)电极的导电性显著增加。     

Relating catalyst structure and composition to the water–gas shift activity of Cu–Zn-based mixed-oxide catalysts

In order to investigate the effect of cerium oxide on Cu–Zn-based mixed-oxide catalysts four catalyst samples were characterized by means of XRD, in situ XANES and thermogravimetric analysis. The activity of the catalyst samples was tested for the forward water–gas shift reaction. Cerium oxide was found to increase the crystallinity of the ZnO phase indicating a segregation of the Cu and ZnO phases. The TOF of the water–gas shift reaction based on chemisorption data was found to be independent of composition and preparation conditions of the four catalyst samples. In contrast, the catalyst stability depends on composition and preparation conditions. Cerium oxide impregnated before calcination of the hydrotalcite-based Cu–Zn precursors leads to a more stable water–gas shift catalyst.