改性生物质作为型煤黏结剂的研究

探讨了用NaOH改性生物质秸秆作为型煤黏结剂的可行性,考察了NaOH溶液浓度对生物质改性的影响以及生物质添加量、无机物(MgO和MgCl2)添加量对型煤机械强度、防水性能和着火温度的影响。研究结果表明,NaOH改性液的质量分数为1.0%~2.0%时,制得的生物质型煤有较高的机械强度;生物质添加量在2%~20%时,随生物质添加量的增加,机械强度增加,着火温度降低,但防水性较差;而在生物质型煤中加入适量无机黏结剂后,型煤有很高的浸水强度,表现出优越的防水性能。     

3Cr-3Mo二次硬化钢的回火组织和力学性能

研究了3cr—3Mo二次硬化钢淬火回火后的组织和力学性能。结果表明：随回火温度的升高，试验钢中先后析出M3c、M2c和M7C3等碳化物，在575℃回火时硬度达到峰值；400一575℃回火后试验钢的抗拉强度约为l600MPa，冲击韧性为30J／cm^2；回火温度高于600℃时，强度和硬度迅速下降，冲击韧性增加；640℃回火时，以M2C型碳化物为主，抗拉强度为1100MPa，冲击韧性增加至55J／cm^2。     

注射成形Fe-50%Ni软磁合金的研究

Fe-50 %Ni合金是一种典型的高磁导率和低矫顽力的软磁材料,有着广阔的应用前景.本次实验采用注射成形方法制取Fe-50 %Ni,研究了在注射成形工艺中烧结工艺对最终产品性能及微观组织的影响,并分析了影响产品磁性能的一些主要因素.实验表明,烧结温度的提高和烧结时间的延长能够较好改善产品的力学性能;密度是影响产品磁性能的主要因素,杂质(主要指(C、O、N)的含量和晶粒尺寸对剩磁、磁导率和矫顽力也有较大的影响;通过注射成形方法制取的Fe-50 %Ni,其性能要优于采用传统粉末冶金方法制造的Fe-50 %Ni.     

4%Cr铸钢支承辊热处理工艺

以太钢1549轧机采用的4%Cr铸钢支承辊为依托,研究了该辊子从铸造成形到最终精加工之间的三次热处理工艺。最终达到其技术要求:辊身硬度65~70HS、淬硬层深≥70 mm、辊颈硬度42~48HS。     

Research on charge ordering and magnetic properties in La0.3Ca0.7Mn1-xWxO3 system

The perovskite manganite sample La0.3Ca0.7Mn1-xWxO3 （x = 0.08, 0.12） was prepared by the solid-state reaction method. The effect of W doping on the Mn site to La0.3Ca0.7MnO3 charge ordering phase and the changing process of magnetic properties were studied through the measurement of the M-T curve, M-H curves, and ESR curves of the sample. The results showed that when x = 0.08, the charge ordering （CO） phase exists in the system, the transition temperature Tco= 275 K, and the system exhibits PM when T 〉 275 K. The system transforms from spin-disordering paramagnetism to spin-ordering antiferromagnetism in the charge ordering state with the temperature decreasing from 275 K to 230 K. The long-range antiferromagnetism forms and AFM/CO states coexist between 230 K and 5 K. There is a little ferromagnetic component in the AFM/CO background in a low temperature range. When x = 0.12, the CO phase in the system has almost melted completely. There is a little remnant of the CO phase below 150 K. The system exhibits paramagnetism when T 〉 150 K and transforms from paramagnetism to ferromagnetism when T〈 150 K.     

Preparation and Properties of Rare Earth Modified Carbon Black/Natural Rubber Composites

The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln（OH）3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln （OH）3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what＇s more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy （OH）3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction.     

Structural transformation of FePt nanocomposite films during annealing and its effects on magnetic properties

Fe100-xPtx(x=30at.%-60at.% ) nanocomposite films were deposited on natural-oxidized Si(100) substrates by magnetron sputtering. The as-deposited films were annealed between 373 and 1073 K. In situ X-ray diffraction shows that the FePt nanocomposite films undergo a phase transformation from a disordered FCC phase to an ordered L10 phase between 673 and 773 K. The coercivity is 306 kA·m-1 whiles the average grain sizes is about 10 nm in the optimized FePt alloy film sample annealed at 673K. The adjustable coercivity and fine grain size suggest that this FePt nanocomposites system is suitable as recording media at extremely high areal density.     

注射成形粘结NdFeB磁体:工艺·性能·应用

综合介绍了几种适于注射成形粘结NdFeB磁体的磁粉制备方法及特点；讨论了粘结剂、改性剂及磁场取向对注射成形NdFeB磁体最终磁性能的影响及其应用市场。在此基础上，指出了今后开展研究工作的方向。     

强磁防蜡器工艺改进措施

针对影响强磁防蜡器两个性能指标的关键要素进行分析，设计并制造了专用的模具和采用水浸式焊接新工艺，提高了产品性能，产品质量的稳定性有了可靠的保证，同时加工成本也有较大幅度的下降。