高压锅炉补给水系统管道的腐蚀

讨论了锅炉补给水管道的腐蚀情况 ,指出溶解氧和二氧化碳是产生腐蚀的主要原因 ,其腐蚀速率为0 .4 2mm/a。确保真空除气系统正常运行和二级除盐水箱的密封效果是控制腐蚀的主要手段。在此情况下 ,该管线尚可运行 7年     

氧浓度对近临界水中纤维素分解的影响

研究了不同初始氧浓度对纤维素在近临界水中分解的影响，实验结果表明，氧浓度显著地影响产物总碳收支平衡，液相不同组分的收率、气体的产量以及气相产物的组成，微量氧对产物总碳收支平衡影响不大，而对液相不同组分的收率有一定的影响。从实验结果可以看出，离子型反应机理在纤维素水解的第一步中起主导作用。而单糖的进一步分解是一个以自由基反应机理为主的过程。     

Mechanical and thermal properties of HVOF sprayed Ni based alloys with carbide

The objective of the present study is to develop multi-functioned coating to the components, which are made of copper with electroplated Ni and are widely used for steel making industry. In this paper, we report the mechanical and thermal properties of Ni based superalloys with carbide sprayed by high velocity oxygen fuel (HVOF), and the detailed effects of sprayed material, spraying conditions, and initial powder structure on these properties. It was found that, among commercial Ni self-fluxing alloys (without fusing treatment), coating with a carbon content of 0.58 mass% had the most preferable properties, with a good balance of the hardness, strength, and thermal shock resistance. The thermal shock resistance depended not only on the strength of the coating but also on the volume contraction when tested at high temperatures. For the several developed Ni based superalloys with carbide, Ni20Cr8Mo5Fe–WC and Ni16Cr15Mo3–WC demonstrated the prominent adhesion strength and thermal shock resistance with high Galvanic corrosion resistance through optimized spraying condition. Also, 20 mass% NiCr–Cr₃C₂ coating sprayed by using employed relatively small primary particle succeeded in achieving the multi-superior properties; high adhesion strength, high corrosion resistance and thermal shock resistance.     

高压热处理对氧沉淀低温形核的影响

研究了外加高压(1GPa)下对450℃热处理硅片中氧沉淀行为的影响.透射电镜观察表明相对于大气压下热处理的样品,高压处理的样品会产生密度更高、尺寸更小的氧沉淀,表明高压有利于小直径氧沉淀的生成.电学性能测试表明,高压下处理的样品其热施主生成浓度和生成速率远远高于常压下处理的样品,这表明热施主与低温热处理过程中生成的高浓度氧沉淀核心有密切的关系.     

Effect of oxygen flow rate on the structural and electrochemical properties of lithium nickel oxides synthesized by the sol–gel method

The structural and electrochemical properties of LiNiO₂ powders were investigated as a function of the oxygen flow rate employed in the preparation of lithium nickel oxide. It was found that oxygen played an important role in the synthesis of highly crystallized LiNiO₂(R3¯m). In the crystallization process of LiNiO₂, a deficiency of oxygen in the calcination reactor induced the formation of impurities and cubic rock-salt structure (Fm3m) in LiNiO₂ powders. For LiNiO₂ prepared at higher oxygen flow rates, the electrode delivered high discharge capacities with relatively good retention rates. But very low electrode capacity was obtained from LiNiO₂ prepared at lower oxygen flow rates.     

板式换热器热端跑冷问题的分析及处理

１００００ｍ３／ｈ制氧机板式换热器损坏修复后，热端跑冷严重，氧气取出量不足，制氧机工况恶化，通过分析找出了原因是因某单元氧通道堵塞，并采取了处理措施。     

节能润滑油在KTK-12.5/35氧压机上的使用

对氧压机试用节能润滑油前后的相关参数进行比较,通过计算验证该设备使用此油后的节电率,取得了预期的经济效益。     

钛及钛合金中氧和氢的联合测定

叙述了用红外吸收法对钛及钛合金中氧和氢联合测定的方法，取得了测定的最佳条件。连续测定6次的相对标准偏差在10％以下，作加标回收试验的回收率为95．6％～103．9％。分析时间在3min以内，可应用于日常分析，结果满意。     

Selective oxidation of alcohols using octahedral molecular sieves: influence of synthesis method and property–activity relations

Manganese oxides having a tunnel structure (OMS-2) have been utilized as selective catalysts for alcohol oxidation. In this study manganese oxide catalysts were synthesized in different media and modified by exchanging the tunnel cation by H⁺, using acid treatment or exchanging with NH₄⁺ followed by thermolysis. Various alcohol oxidations were performed using these catalysts to ascertain the influence of synthesis method on their activity. A correlation is made between lattice oxygen instability and activity of the catalysts, which indicates involvement of the lattice oxygen in the mechanism. The exchange of the tunnel cation with the smaller H⁺ ions leads to weakening of the Mn–O bond, as verified by temperature programmed desorption (TPD) results. Only the chemisorbed oxygen on the surface (O⁻) and the lattice oxygen in the layers close to the surface is involved in the oxygen transfer during the reaction.     

具有复合埋层的新型SIMON材料的制备

采用氮氧共注入方法制备了新型的 SIMON(separation by implanted oxygen and nitrogen) SOI材料 .采用不同的制备方法分别制作出样品并进行了结构测试和分析 ,发现 SIMON材料的结构和质量对注入条件和退火工艺非常敏感 .并对各种氮氧复合注入技术做了分析和比较 ,发现氮氧分次注入可以得到更好的结构和性能