21.
《Ceramics International》2023,49(3):4412-4421
Bauxite- and alumina-based spinels were employed as refractory aggregates, and sintered magnesia fine powder, calcium aluminate cement, microsilica, and activated α-Al2O3 were utilized as matrices. The effects of alumina powder, analytically pure zinc oxide, and analytically pure zirconia on the properties of magnesium aluminate spinel–periclase castables were studied. The results demonstrated that the addition of the three additives promoted the sintering of magnesium aluminate spinel–periclase castables. Simultaneously, the three additives significantly improved the high-temperature properties of the samples. The thermal shock resistance of the alumina powder sample increased by 200%, that of the pristine zinc oxide sample by 75%, and that of the zirconia sample by 125%. The additives effectively improved the thermal shock resistance of the magnesium aluminate spinel–periclase castable. In addition, the slag resistance depths of the samples with alumina powder and zirconia were 41% lower than that of the sample without additives, which significantly improved the slag resistance of the magnesium aluminate spinel–periclase castable. 相似文献
22.
Zhenying Liu Hanxin Zhang Kai Wang Kai Cui Nan Xie Shouwu Huang Changguo Xue Hongzheng Zhu Yin Liu 《International Journal of Applied Ceramic Technology》2023,20(5):3194-3205
This study presents new lightweight periclase-magnesium alumina spinel refractories for the working lining of cement rotary kilns in which magnesium alumina spinel hollow spheres are used to replace conventional dense fused magnesia-aluminate spinel aggregates. The effects of adding spinel hollow spheres on the physical properties, mechanical strength, thermal conductivity, and slag resistance of the samples were explored. The results showed that compared with the sample prepared with dense aggregates, the sample prepared with hollow spheres had a 10.3% higher cold compressive strength, 44.1% higher modulus of rupture (MOR), and lower bulk density. Additionally, with increasing hollow spheres content, the thermal conductivity decreased from 3.79 W/(m·K) to 2.53 W/(m·K), and the high-temperature MOR increased from 2.82 to 4.09 MPa. The highest residual strength ratio was 90.73% (15 wt.% hollow spheres), which is 1.17 times that of the sample prepared without hollow spheres. Moreover, microstructure and energy dispersive spectroscopy of crucible specimens after corrosion by cement clinker showed that specimens with 15 wt.% hollow sphere additions had a better slag resistance. Introducing hollow spheres reduced the thermal conductivity of the refractories, providing a new strategy for improving the heat insulation performance of kiln linings. 相似文献