固溶温度对CuZnAl合金形状记忆性能的影响

研究了Cu-26．87Zn-3．85Al(wt％)形状记忆合金固溶温度对其形状回复率的影响。结果表明，该合金采用固溶 上淬工艺处理后，在600℃～720℃范围内，形状回复率随着固溶温度的升高迅速增加，在720℃后趋于稳定，达到最大值；固溶温度越高，合金晶粒越大，会对其力学性能造成负面影响，在能保证合金形状记忆性能的基础上应尽量保证合金的晶粒小，因此其最佳固溶温度是720℃。将该合金在室温下自然时效一个月后，由于马氏体稳定化，其形状回复率有小幅度下降。     

Twice reverse shape memory effect in CuZnAl shape memory alloy

The variations of the shape memory effects in the Cu-13Zn-15Al(mole fraction, %) alloy upon successive heating (the rate of heating is 5℃/min) have been studied by means of ρ-T curve , shape memory effect measurement, optical metallographical observation and X-ray diffraction. The first abnormal reverse shape memory effect occurs when the tested alloy is heated to the temperature below 320℃ ; when it is heated to the temperature between 320℃ and 450℃, the forward shape memory effect occurs; in the two stages, the shape of the sample remains the same as that in the furnace when it is taken out from the furnace and air-cooled; when the tested alloy is heated to the temperature above 450℃, the shape of the sample remains unchanged during heating, but the second reverse shape memory effect occurs after it is air-quenched.     

形变时效温度对Fe-Mn-Si-Cr-Ni合金形状记忆效应的影响

研究了直接时效和形变时效温度对Fe-13Mn-5Si-8Cr-4Ni-0.2C合金形状记忆效应和微观组织的影响.结果表明,直接时效后Fe-Mn-Si-Cr-Ni合金在奥氏体晶界和晶内只有少量Cr23C6第二相弥散析出,而形变后再时效有大量的Cr23C6在奥氏体晶内沿某些特定的方向析出,显著强化基体的同时提高了ε马氏体的可逆逆转变性.形变时效温度影响第二相的析出数量和方向性,从而影响合金的形状记忆效应,存在一个最佳的时效温度.当形变后在1073 K时效300 min时,不仅第二相数量多且在晶内析出的方向性好,合金的形状记忆效应达到89%.     

Shape-memory effect in Co-Ni single crystal

The thermal shape-memory effect at room temperature for Co-32% Ni(mass fraction) magnetic shape memory alloy of single crystal was presented. When compressing the sample along the [001] direction at room temperature, strain can be recovered to some extent during later heating and the recovery rate varies with the pre-strain.But no obvious recoverable strain can be obtained along other crystal directions. For the thermal-mechanical training of the sample along [001], the recovery strain decreases obviously during the second round of compress and nearly no recovery happens after the third round of compress. A possible mechanism based on reversible motions of Shockley partial dislocations was proposed.     

铁基形状记忆合金（待续）

简介形状记忆效应(SME)的基本概念和形状记忆合金的发展。评述了Fe-Mn-Si,Fe-Mn-Si-Cr-Ni,Fe-Ni-Co-Ti和Fe-Ni-C等系铁基形状记忆合金的生长背景,特性及其SME的机制。     

奥氏体预变形温度对提高Fe－Mn－Si合金记忆效应的影响

本文研究了５７３─１０７３Ｋ温度范围内３％奥氏体预变形对Ｆｅ－２９．９％Ｍｎ－６．０％Ｓｉ合金记忆效应的影响．结果表明，固溶态的样品经奥氏体预变形后，在室温变形时，记忆应变（ε（ｔｒ））、应变回复率（η）及记忆应变达到饱和所对应的应变值都得到了明显的提高：随预变形温度升高，室温经约２．５％变形后应变回复率增加，并在合金动态再结晶开始温度９７３Ｋ预变形后具有最大值９８％；经９７３Ｋ预变形，合金的最大记忆应变由固溶态的１．７％提高至３．８％，完全记忆应变达２．２％；奥氏体预变形的作用在于降低了室温诱发ε马氏体的临界应力．     

NiAl合金的高温形状记忆效应SCIEI

观察到Ｎｉ－３４．６ａｔ．－％Ａｌ薄带单程和双程形状记忆效应（ＳＭＥ），单程ＳＭＥ发生在３００℃以上并具有很好的形状恢复率（１００％）。经高温退火后合金中产生了体积分数为１６％的延性γ′－Ｎｉ_３Ａｌ沉淀相、延性和韧性有进一步改善，同时发现退火后的薄带也具有良好的单程和双程高温ＳＭＥ。结果表明富Ｎｉ的ＮｉＡｌ有可能成为新型高温形状记忆合金（ＳＭＡ）。     

智能材料和智能结构——形状记忆材料

研究了形状记忆材料,如形状记忆合金、陶瓷和聚合物的结构、生产方法、特性和应用。形状记忆材料具有许多优秀的智能特性,例如传感（热、应力和场）、大行程执行器、高阻尼、自适应响应、形状记忆、超弹性等,可用于各种智能系统。形状记忆材料中的激励感应相变导致了材料的许多独特的性能,支配着材料性质的显著变化。讨论了改进目前材料系统和研发新的形状记忆材料所面临的技术障碍和挑战。     

形状记忆执行材料的研究进展

形状记忆材料是一种重要的智能材料,主要作为执行器件材料,被广泛的用在建筑、航空航天、军事和医学等领域.近年来形状记忆材料的研究和应用受到研究人员的重视.本文综述了近几年形状记忆合金、形状记忆陶瓷和形状记忆聚合物的新的研究成果和研究方向,展望了形状记忆材料未来的发展趋势.     

热致感应型形状记忆三元凝胶的制备与性能

选用疏水性单体丙烯酸十八酯（SA）和十一烯酸（HA）以及亲水性单体丙烯酰胺（AM）制备了三元共聚凝胶P（SA-co-AM-co-HA），通过X射线衍射、DSC、DMA等对三元凝胶的结构和性能进行了研究，发现三元凝胶形成了有序排列，这种有序排列会随着温度的变化发生可逆转变，从而使凝胶显示较好的形状记忆特性。