Impact toughness of tungsten films deposited on martensite stainless steel

Tungsten films were deposited on stainless steel Charpy specimens by magnetron sputtering followed by electron beam heat treatment. Charpy impact tests and scanning electron microscopy were used to investigate the ductile-brittle transition behavior of the specimens. With decreasing test temperature the fracture mode was transformed from ductile to brittle for both kinds of specimens with and without W films. The data of the crack initiation energy, crack propagation energy, impact absorbing energy, fracture time and deflection as well as the fracture morphologies at test temperature of-70 ℃ show that W films can improve the impact toughness of stainless steel.     

金窝子金矿床构造成矿与找矿前景

实践表明①构造对金窝子金矿床的控制作用极为明显;②矿体受区域性韧性剪切带的展布控制,北东向韧性剪切带的严格控制,近南北向的构造被石英充填成矿;③目前已经探出来的156号脉群提供了很大的找矿空间.     

钛合金热处理强化与应用

钛合金具有高的屈服强度／密度比、疲劳强度／密度比、蠕变极限，良好高、低温性能、热稳定性、抗蚀性，可减轻结构重量；在常温及超低温下，比强度高，有足够韧性与塑性：在氧化性与中性介质及海水和海洋性气氛下，具有优异的耐腐蚀性能，在还原介质中，通过合金化可进一步改善和提高抗蚀性能：具有高的活性，能吸收O、N、H2、CO2和甲烷等气体，     

压痕法测定热压MoSi2基复合材料K1C值的研究

用不同的压痕方程计算了纳米ＺｒＯ２粒子韧化ＭｏＳｉ２基复合材料的室温断裂韧性Ｋ１ｃ值，同时研究了压痕载荷对Ｋ１ｃ值的影响。结果表明，试验材料在试验条件下的断裂韧性不遵从半月状裂纹系统方程，而遵从巴氏裂纹系统方程，其室温压痕断裂韧性保持与压痕载荷的独立性。     

Analysis of damage localization for ductile metal in process of shear band propagation

1 Introduction Shear localization is an important and often dominating deformation and failure mechanism for Ti and Ti alloy in dynamic loadings[1—10]. The eventual outcome of localized deformation is ductile rupture and material separation. Shear locali…     

焊接应用——焊接结构与设计

通过选用不同的焊材及不同的焊接参数，对低温材料09MnNiDR进行了一系列的工艺评定试验。指出了影响09MnNiDR焊接接头低温韧性的主要因素，并提出了焊接时应采取的工艺措施。表6     

Effects of CeF3 on properties of self-shielded flux cored wire

0 IntroductionSelf-shielded flux cored wire is a newly developedwelding material used without gas protection. Use of suchcored wires has grown rapidly in developed countriesbecause of the following advantages: simple use, goodwind resistance ability, lower cost resulted from highproductivity and strong desulfurization ability[1]. Self-shielded flux cored wires are preferred for on-site weldingsuch as ship and barge building, storage tank, bridge,offshore oil platform buildings and so on[2 -3].…     

球铁曲轴断口金相显微与电子显微分析

利用XJG-05金相显微镜及大型金相图象分析仪对曲轴断口的断裂源、扩展区的组织进行金相显微分析，并利用EPM-810Q电子探针、扫描电镜、PV9100能谱仪，在加速电压20kV，束斑电流0．01-0．5nA的条件下，对曲轴断口的断裂源、扩展区的形貌特征进行了扫描观察和微区成分定性定量分析，得出了曲轴圆角处次表层较严重的磨削裂纹和较高的残余应力是造成曲轴早期疲劳韧性断裂重要原因。     

淬火工艺对Fe-V-W-Mo合金组织和性能的影响

在测试了Fe-5％V-5％W-5％Mo-5％Cr-3％Nb-2％Co-2％c（Fe-V-W-Mo）合金的临界点和CCT曲线基础上，研究了淬火温度、淬火冷却方式对该合金组织和性能的影响。研究结果表明，Fe-V-W-Mo合金油冷淬火温度低于1025℃。随淬火温度升高硬度升高，超过1050℃，硬度反而降低。雾冷和空冷淬火时，淬火温度对硬度影响结果相似，获得最高硬度的淬火温度高于油冷时的淬火温度。Fe-V-W-Mo合金油冷淬火淬透性最好，雾冷次之，空冷最差，但是油冷和雾冷差别不大。Fe-V-W-Mo合金红硬性和韧性随淬火温度升高而提高，超过1150℃时，韧性反而降低。最后讨论了Fe-V—W—Mo合金在不同淬火冷却条件下组织和性能变化的原因。     

WC硬质合金颗粒复合耐磨材料的韧性与断裂

采用不同类型的WC硬质合金颗粒及不同成分的金属基本组成的两种复合耐磨材料，研究了复合材料的韧性及其影响因素，观察分析了其断口形貌及断裂机理．结果表明，复合材料的韧性与断面上WC硬质合金颗粒及金属基体的面积分数有关，主要取决于金属基体的成分、组织状态、韧性和含量，基体的韧性越好，含量越多，则复合材料的韧性越高．在冲击载荷作用下，WC硬质合金的断裂为脆性解理断裂，而金属基体则为具有少量塑性变形的准解理断裂。