铸态Ti-20Zr-20Al钛合金动态压缩力学性能与断裂机制研究

采用X射线衍射仪、金相显微镜、分离式霍普金森杆和扫描电镜等手段研究了Ti-20Zr-20Al钛合金在动态压缩条件下的微观结构、力学性能和断裂机制。结果表明,Ti-20Zr-20Al铸态合金由Zr基体相和TiAl/Ti₃Al针状相组成; 随着应变率增加,合金的抗压强度增加,失效应变显著增加; Ti-20Zr-20Al合金的断裂机制为解理断裂; 随着应变率增加,试验压缩断裂后碎片总数增大,平均粒径减小。采用DID模型模拟的材料碎片尺度与实验结果比较吻合,Grady模型与实验结果的偏差较大。     

Process and joint quality of ultrasonic vibration enhanced friction stir lap welding

In order to improve the process effectiveness and joint quality, ultrasonic vibrations were integrated with friction stir lap welding. Effect of ultrasonic exertion on the process and joint quality of AA 6061-T6 were investigated. Upon ultrasonic exertion, joints owned larger effective lap width, shorter hooks and improved strength. Weld fracture mode changed from a ductile–brittle mixed mode to a more ductile mode while the fracture path shifted from lap interface to beyond the stir zone. Material flow and interface defects were characterised using lap welded dissimilar aluminium alloy joints. Ultrasonic vibration improved the material flow and reduced the interfacial defects. Variations in failure load of joints were found in accordance with the variations in material flow and interfacial defects.     

Effect of microstructure on the fatigue crack growth behaviour of a near-α Ti alloy

Fatigue crack growth behaviour of Ti–6Al–2Zr–1.5Mo–1.5V (VT-20 a near-α Ti alloy) was studied in lamellar, bimodal and acicular microstructural conditions. Fatigue crack growth tests at both increasing and decreasing stress intensity factor range values were performed at ambient temperature and a loading ratio of 0.3 using compact tension samples. Lamellar and acicular microstructures showed lower fatigue crack growth rates as compared to the bimodal microstructure due to the tortuous nature of cracks in the former and the cleavage of primary α in the latter. The threshold stress intensity factor range was highest for acicular microstructure.     

Effect of microbial hydrogen consumption on the hydrogen permeation behaviour of AISI 4135 steel under cathodic protection

The feasibility of microbial hydrogen consumption to mitigate the hydrogen embrittlement (HE) under different cathodic potentials was evaluated using the Devanathan-Stachurski electrochemical test and the hydrogen permeation efficiency η. The hydrogen permeation efficiency η in the presence of strain GA-1 was lower than that in sterile medium. The cathodic potential inhibited the adherence of strain GA-1 to AISI 4135 steel surface, thereby reducing the hydrogen consumption of strain GA-1. The adherent GA-1 cells were capable of consuming ‘cathodic hydrogen’ and reducing the proportions of absorbed hydrogen, indicating that it is theoretically possible to control HE by hydrogen-consuming microbes.     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

硅渣和玻璃粉直接烧结制备多孔材料的气孔结构与力学性能

以硅渣和玻璃粉为原料,采用粉体直接烧结法制备多孔材料,研究了烧结温度(700~900℃)、烧结时间(15~120min)和升温速率(10~100℃·min^-1)对多孔材料表观密度、气孔率、物相组成、抗压强度的影响。结果表明:气孔结构均匀性随烧结温度的升高而降低;表观密度随烧结温度的升高先减小后增大,随保温时间的延长而增大,随升温速率的增大而减小,气孔率的变化趋势与表观密度的相反;多孔材料的主要物相为玻璃相和硅、SiC、SiO2、Ca2Al2SiO7等结晶相,且结晶度随烧结温度的升高而降低;抗压强度随烧结温度的升高呈先增大后减小的趋势;当烧结温度为750℃,升温速率为30℃·min^-1,烧结时间为30 min时,多孔材料的主晶相为硅和Ca2Al2SiO7,抗压强度最大(1.60MPa),表观密度为0.43g·cm^-3,气孔率为80%。     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

ZK60镁合金表面滚压强化试验研究

试验研究了ZK60镁合金表面滚压加工中工艺参数对试件表面粗糙度、表面形貌、表面残余应力和表层显微硬度的影响,结果表明滚压力和重复滚压次数对试件的表面粗糙度、表面形貌以及表面残余应力和表层硬度影响程度较大,滚压速度影响较小。对精车ZK60镁合金试件进行滚压加工,试件表面粗糙度R a、R z最大减小了50.3%和48.1%;残余压应力最大可达-54.55 MPa;显微硬度从试件表层到内部基体材料逐渐降低,表层硬度值最大为92.83 HV 0.25,比基体材料硬度提高了15.32%。     

户内热转印粉末涂料用混合型聚酯树脂的合成研究

通过分析热转印性能的影响因素合成了不同结构的聚酯树脂，研究了树脂酸值对热转印性能的影响，同时研究了部分单体对聚酯树脂热转印性能的影响。采用 DSC热分析法研究了固化促进剂对粉末涂料固化行为的影响，结果表明：选择合适的固化促进剂对涂层转印性能的提高有至关重要的作用。     

Corrosion behaviour of AA2024 aluminium alloy in different tempers in NaCl solution and with the CeCl3 corrosion inhibitor

The paper analyses the corrosion behaviour of naturally and artificially aged AA2024 alloy in NaCl solution and in the presence of an environment-friendly corrosion inhibitor, CeCl₃. On the basis of the values of polarisation resistance and corrosion current density, the corrosion resistance of the protective inhibitor film is established as well as the general corrosion resistance of this aluminium alloy. Resistance to pit formation is determined based on the difference in pitting and corrosion potentials while resistance to pit growth is determined based on the amount of charge consumed during pit growth. A scanning electron microscope is used to examine the morphology of the pits formed during the pitting corrosion testing, as well as to determine the cerium content on intermetallic particles and the matrix AA2024 alloy. The corrosion behaviour of AA2024 alloy is investigated after different test periods in NaCl solution and in the same solution with the CeCl₃ inhibitor. The corrosion resistance of both tempers of AA2024 alloy is more than one order of magnitude higher in the presence of CeCl₃. An explanation of the observed differences in the corrosion behaviour of the naturally and artificially aged AA2024 alloy is proposed. Different corrosion behaviour of the alloy after different test periods is also explained.