Study on corrosion resistance and roughness of micro-plasma oxidation ceramic coatings on Ti alloy by EIS technique

Micro-plasma oxidation (MPO) technique has been developed quickly in recent years. The produced ceramic coatings are reported to possess fine properties and promising application prospects in many fields. The aim of this work is to study the corrosion resistance and the roughness of the micro-plasma oxidation ceramic coatings on Ti alloy by electrochemical impedance spectroscopy (EIS) technique. Compound ceramic coatings were prepared on Ti-6Al-4V alloy by pulsed bi-polar micro-plasma oxidation in NaAlO₂ solution. The phase composition and element distribution in the coating were investigated by X-ray diffractometry and electron probe micro-analyzer. EIS of the coatings was measured through CHI604 electrochemical analyzer in 3.5% NaCl solution. The ceramic coating is composed of a large amount of Al₂TiO₅ and a little α-Al₂O₃ and rutile TiO₂. The coating is of double-layer structure with the loose outer layer and the dense inner layer. The thickness of the coatings is reduced when the working frequency or the cathode pulse current density is increased, while the thickness is increased when the frequency or the anode current density is increased. The established “equivalent circuit” of the coatings is consistent with the double-layer structure. The electric charge transfer resistance (R_t) in the equivalent circuit can be used to assess the corrosion resistance of the coatings, which is consistent with the result of the polarizing curves test. And the empirical exponent (n₁) of the constant phase element (Q₁) in the equivalent circuit can be used to assess the surface roughness of the coatings, which is consistent with the surface SEM analysis of the coatings.     

Ambient‐cured polyesteramide‐based anticorrosive coatings from linseed oil—A sustainable resource

Ambient‐cured polyesteramide (APEA) coating resin synthesized from dihydroxy fatty amide obtained from linseed oil, a sustainable resource, and poly(styrene‐co‐maleic anhydride), a bifunctional acid component, was found to exhibit improved physicomechanical and anticorrosive properties. The structural elucidation of APEA resin has been carried out by FTIR, ¹H‐NMR, and ¹³C‐NMR spectroscopies. The physicomechanical and chemical resistance properties were investigated by standard methods. The corrosion resistance performance was evaluated in acid, alkali, and organic solvent. The thermal behavior was studied by TGA technique. A comparative study of these properties of APEA with reported baked polyesteramide (PEA) coatings was carried out. A remarkable improvement in the drying property of APEA was observed. The APEA coatings also showed improved physicomechanical and anticorrosive properties as compared to the baked PEA coatings. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 1818–1824, 2005     

槽液稳定性好的高硬度丙烯酸阳极电泳涂料的研制

在混合溶剂中加入甲基丙烯酸、各种甲基丙烯酸酯单体以及引发剂AIBN和链转移剂DDM,在85℃下反应合成了丙烯酸树脂。分别研究了不同酸值和羟值的丙烯酸单体、不同Tg的丙烯酸树脂以及各种助溶剂和中和剂对漆膜性能的影响。获得了丙烯酸阳极电泳涂料的最佳配方:丙烯酸共聚树脂的酸值为65 mg KOH/g、羟值为69 mg KOH/g、Tg为20℃,溶剂是体积比为1∶1的丙二醇单甲醚和异丙醇的混合物,中和剂是二乙醇胺。该电泳涂料具有良好的槽液稳定性和起泡消泡性。制得的涂膜外观平整、丰满、光亮,厚度为18~20μm,硬度为5 H,冲击强度为500 N/cm2,附着力为1级,柔韧性为1 mm,耐烟雾实验超过400 h。     

双组分高固体丙烯酸聚氨酯涂料的研究

介绍了改性高固体分羟基丙烯酸树脂的合成工艺，通过对引发剂、链转移剂、反应温度及叔碳酸缩水时油酯等因素的讨论，合成了新型的羟基丙烯酸树脂。以其为基料配制了丙烯酸聚氨酯涂料，并讨论了该磁漆的配方设计和各项性能。     

高性能环氧树脂涂料的研制

以甲基丙烯酸、丙烯酸丁酯及苯乙烯的聚合为接枝体，在过氧化苯甲酰作用下对E-51环氧树脂进行接枝改性，同时对三乙烯四胺进行曼尼希改性，制得多种改性固化剂，并用其与改性的环氧树脂配制成涂料，实验结果表明，当苯酚、甲醛和三乙烯四胺的物质的量比为3：3：1时固化剂的固化性能最好。     

耐高温绝缘涂层的研制

采用有机硅树脂、无机粘结剂和无机填料制备的有机无机复合耐高温绝缘漆，其涂层经600℃，1h的热处理后可具有良好的附着力和绝缘性能。配套后的绝缘涂层，可在250℃下长期使用，并具有良好的耐冷热循环、耐湿热的能力。     

钢结构防火涂料的研究和应用

作者结合工作实践,综述了国内外钢结构防火涂料的研究及应用情况,展望了钢结构防火涂料的发展前景。     

Thermal Shock Failure in Thick Epoxy Coatings

In this paper we describe an apparatus for reproducibly measuring thermal shock resistance of thick polymer layers bonded to metals. The thermal shock behavior is discussed in terms of epoxy samples bonded to an aluminum substrate. It was found that both high resin toughness and low resin thermal expansion coefficient improved thermal shock resistance of thick coatings, but only a sample containing 60wt. % glass beads did not develop a failure crack. Effects of sample thickness, temperature gradient, and resin composition on thermal shock behavior are discussed.     

Molybdenum Oxycarbide and Tungsten Oxycarbide Coatings on Silicon Carbide Fibers

The strength and toughness of fibrous composites depend on the interface properties which control the bonding between the fibers and matrices. One method of controlling the interface involves coating the fiber with an appropriate material. In a previous study, it was found that there is a definite advantage in using low coating temperatures to prevent fibers from degrading. We therefore were interested in a report that Mo₂C could be deposited from Mo(CO)₆ at temperatures as low as 300° to 475°C. Our studies indicated that the material was not Mo₂C, but an oxycarbide, which, with an analogous tungsten oxycarbide coating, was applied to SiC yarns. Both oxycarbides could be converted to the metals by heat-treating in N₂.     

船舶防污涂料的研究与发展

简要介绍船舶防污涂料的发展历程,并对几种新型无毒防污涂料的前景作了展望。