45钢表面超音速电弧喷涂Ti-Al涂层的组织与性能研究

采用自行开发研制的超音速电弧喷设备，在45钢表面制成了钛铝合金复合涂层。并利用金相显微镜、X射线衍射仪、扫描电镜、电子探针，对涂层的成分、相结构、显微组织及其结合强度、显微硬度进行了研究。结果表明，利用超音速电弧喷涂设备，可以在45钢表面形成 度高、孔隙率低，结合强度较好和硬度高的Ti-Al合金涂层。     

摩擦焊在钢制实心抽油杆修复中的应用

通过对焊接工艺及焊后热处理工艺优化，采用摩擦焊接技术对报废抽油杆中仍有使用寿命的杆头与杆体进行了拼接，获得了性能达标的抽油杆。从而提高了旧杆的修复率．降低了采油成本。该技术可在抽油杆修复及相关行业进行推广应用。     

植筋施工工艺

以某网球馆改造工程为例 ,就植筋技术的概念及所用材料进行了介绍 ,详细阐述了其施工工艺流程及措施 ,指出植筋技术具有工艺简单、操作方便、造价相对较低等优点     

铁素体球墨铸铁与20钢的闪光对焊

试验使用铁素体球墨铸铁和20钢的实心棒料进行了闪光对焊，通过改变次级电压4～8级，通电时间3～5s，观察其焊接接头组织的变化并测定其抗拉强度。结果表明，接头由三个区组成；当通电时间一定时，抗拉强度随次级电压的升高先减小后增大；当次级电压一定时，抗拉强度随通电时间的增加而增大。在次级电压为8级、通电时间为5s时，抗拉强度达最大值，为370．8MPa，是20钢母材的90.4％，是球墨铸铁母材的83.7％。     

强磁防蜡器工艺改进措施

针对影响强磁防蜡器两个性能指标的关键要素进行分析，设计并制造了专用的模具和采用水浸式焊接新工艺，提高了产品性能，产品质量的稳定性有了可靠的保证，同时加工成本也有较大幅度的下降。     

A classification of tournaments having an acyclic tournament as a minimum feedback arc set

Given a tournament with an acyclic tournament as a feedback arc set we give necessary and sufficient conditions for this feedback arc set to have minimum size.     

On regular drawn symbolic picture languages

Drawn symbolic pictures are an extension of drawn pictures obtained by associating a symbol from an alphabet to each point of the picture. In the paper we will address some new interesting issues derived from the introduction of the symbols and we will identify the conditions, which ensure the preservation of properties holding for drawn pictures in the setting of the proposed extension.     

Effect of Rare Earth Element Cerium on Mechanical Properties and Morphology of TiN Coating Prepared by Arc Ion Plating

TiN coatings were deposited on polished substrates of W18Cr4V high speed steel by means of vacuum arc ion plating. The effect of cerium on adhesion between TiN coating and substrate was studied. The microstructures and composition of TiN coatings were also investigated by means of scanning electron microscope (SEM), Auger electron spectroscopy (AES), and X-ray diffraction (XRD) technique. It was found that cerium is an effective modifying agent and the addition of suitable amount of cerium to TiN coatings can produce relatively excellent properties such as micro-hardness, wear resistance, oxidation resistance and porosity. The experimental results show that the added cerium in TiN coatings makesa contribution to form the preferred direction along with a (111 ) or (222) close packed face, which may be one of the reasons that improves some properties mentioned above.     

爆炸焊接——热轧双相不锈钢复合钢板研制

本文主要阐述了通过爆炸焊接和热轧的方法,研制成功可焊性良好的且具有较好强度、韧性与综合性能的双相耐应力腐蚀的不锈复合钢板。还将热轧与热处理的两种试验作了较全面的常规、特殊检验试验,结果完全达到使用要求。     

不锈钢管子—管板的激光焊接

试验研究了不锈钢的深溶焊接。研究了聚焦光束回转的光具。在工件不动的情况下,焊接管子—管板连接环缝。焊缝质量满足压力容器的要求,焊接效率大大提高。