环氧基的PCB对无铅组装的兼容性

综述了环氧树脂基的PCB与无铅化组装的兼容性问题。经过大量试验表明,常规的FR-4基材和双氰胺固化的高Tg基材是不能满足无铅化组装要求的,而采用酚醛固化的中等-Tg的环氧树脂基材是可能成为无铅化组装用基材的。同时,PCB制造过程也起着重要的作用。PCB设计和再(回)流焊的加热梯度也影响着无铅化的性能。     

可与氟树脂基板相匹敌的热可塑性树脂基板材料

概述了可以与氟树脂基板相匹敌的低介质特性的热可塑性树脂基板材料的开发和应用。     

辐射剂量对环氧树脂电子束固化行为的影响

分析了电子束剂量对环氧树脂体系辐射固化行为的影响规律。研究结果表明，电子束辐射过程中，温度由树脂辐射体系表面向内部逐渐降低，随着辐射剂量提高，树脂体系温度上升，辐射表面与内部的温度梯度加大，高辐射剂量下的温度变化缓慢。树脂辐射固化层厚度以及在相同厚度的固化程度均随辐射剂量增加，但增幅逐渐变小，树脂辐射固化度沿固化深度会加速下降。     

咪唑封端扩链脲改性环氧树脂E-51/酸酐MTHPA体系性能研究

以端羟基聚环氧丙烷1000，甲苯二异氰酸酯（TDI），2－甲基咪唑为原料，合成了扩链脲TI，利用DSC，动态热机械分析仪DMA，冲击试验机及扫描电镜（SEM）等手段对TI改性的环氧树脂E－51／甲基四氢化邻苯二甲酸酐（MTHPA）固化体系的反应活性，动态力学行为，冲击性能，断裂面形态结构进行了系统研究，结果表明，改性后的E－51／MTHPA体系反应活性明显提高，固化反应峰顶温度较未改性体系降低160℃－200℃，固化反应的表观活化能由未改性体系的160．3kJ/mol降至63kJ/mol-87kJ/mol，同时与未改性体系相比，经过改性的环氧树脂固化体系冲击强度有较大的提高，在TI含量为5％时体系的玻璃化转变温度Ts达到最高，各改性体系冲击断面呈韧性断裂。     

茂名石化PE农用薄膜专用料的生产和开发

概述了我国农用薄膜现状与发展趋势，分析了存在的问题，对茂名石油化工公司的聚乙烯农用薄膜专用树脂的生产和开发提出了建议。     

Anhydrous esterification of myristic acid with propylene: Ion exchange resin and acid-treated clay as catalysts

Anhydrous esterification of myristic acid with propylene was carried out in the temperature range of 110–145°C and pressure from 190–195 psig in the presence of Amberlyst-15 (cation exchange resin) and Filtrol-24 (acid-treated clay) as catalysts. The product ester, isopropyl myristate finds use in cosmetic and topical medicinal preparations where good absorption through the skin is desired. Filtrol-24 is the catalyst of choice, and the recommended operating temperature is 130°C with a pressure of 190 psig.     

The effects of glycol methacrylate as a dehydrating agent on the dimensional changes of liver tissue

The dimensional changes of liver sections during the course of processing with glycol methacrylate (GMA) or with ethanol are described. Tissue processing with ethanol served as a control. During prolonged processing steps (24 h each), linear shrinkage of tissue specimens dehydrated with GMA at room temperature was 13.2%. Subsequent infiltration with GMA resulted in trivial swelling, and polymerization in slight shrinkage (2.3%). In comparison, processing with cold GMA resulted in shrinkage during dehydration (about 10.8%), a slight swelling in pure GMA, followed by shrinkage during polymerization (2.2%). Short routine processing schedules resulted in similar shrinkage/swelling patterns, although precise values differed slightly. In all experiments, ethanolic dehydration resulted in smaller dimensional tissue changes than did GMA dehydration. The dimensional changes of tissue sections during stretching on water, mounting and drying compensated for the major part of the shrinkage manifested during processing.     

阳离子交换树脂铁中毒的复苏研究

软化器中使用的阳离子交换树脂容易受到铁离子的污染。采用均匀设计的方法,利用回归分析和最优化技术,研究了复苏剂中各组分对阳离子复苏效果的影响,得出了最佳复苏配方,开发出了一种新的复苏方法。这种方法具有腐蚀性低和复苏效果良好的特点,为生产现场树脂的复苏提供了有益的借鉴。     

J-199热熔胶膜的研制

讨论了不同VA含量不同熔体指数的EVA和各种增粘剂对热熔胶膜耐热性、软化点、剪切强度、拉伸强度、剥离强度等性能的影响。通过采用不同材料试验和配方的筛选，研制出一种90℃剪切强度0．07MPa、拉伸强度0．47MPa、耐热性好、粘接强度高的热熔胶膜，从而拓宽了热熔胶的使用范围。     

某炼油厂一级浮床除盐系统阳床工艺特性及调整试验

论述了某厂一级除盐系统阳床工艺特性及调整试验过程，对存在问题进行分析并改进，得到了实际运行最佳方式和参数，取得良好效果。