Impacts of varnishes and impregnation chemicals on combustion properties of oak (Quercus petreae lipsky)

This study was performed to determine the effects of varnishing after impregnation with boron compounds on combustion properties of oak. For this aim, the test samples prepared from oak (Quercus petreae Liebl.) wood were impregnated according to ASTM D 1413‐99 with boric acid (Ba) and borax (Bx) by vacuum technique. After impregnation, surfaces were coated by cellulosic (Cv), synthetic (Sn), polyurethane (Pu), waterborne (Wb), acrylic (Ac), and acid hardening (Ah) varnishes in accordance to ASTM D 3023. Combustion properties of samples after varnishing process were determined, according to ASTM E 160‐50. According to material and process types, combustion temperature was the highest in Bx and Cv, the lowest in Ba and Ac. An important difference was not observed between without flame source combustion (WFSC) and flame source combustion (FSC). According to combustion type, impregnation material and varnish type, combustion temperature was the highest value in WFSC + Bx + acid hardening varnish combination and the lowest in WFSC + Ba + acrylic varnish combination. As a result, the tested varnishes showed an increasing impact but boron compounds showed a decreasing impact on combustion properties of oak. In consequence, for usage areas having a high risk of fire, impregnation of wood material with boron compounds before varnishing will decrease combustion temperature and provide security. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

高温合金表面激光熔敷热障涂层组织结构与氧化性能

采用 5KW连续CO2 激光器对Ni基高温合金上二次重熔NiCoCrAlY和ZrO2 陶瓷层进行了研究。结果表明 :激光快速熔化和凝固获得定向外延生长、紧密堆积的柱状晶氧化锆陶瓷层。NiCoCrAlY结合层与柱状晶之间存在氧化铝层 ,保证了柱状晶与NiCoCrAlY层的联结。扫描电镜和电子探针联合分析发现 ,氧化锆层与NiCoCrAlY结合层、结合层与基体间均为冶金结合。采用化学改性氧化锆消除了涂层裂纹。高温氧化性能测试得出激光重熔试样氧化动力学近似地遵守抛物线速率方程。在 12 0 0℃ ,空气下激光熔敷TBCs 抗氧化性明显高于等离子喷涂TBCs。     

A study of neutron and gamma radiation effects on transmission of various types of glasses, optical coatings, cemented optics and fiber

A study of radiation effects on various types of glasses, dielectric optical coatings, cemented optics and fiber was undertaken with a view to select them for extreme radiation environments. Samples were exposed to different radiation doses in the Pakistan Research Reactor-I (PARR-I) for neutron and Cobalt 60 source for gamma irradiation. Transmissions were measured before and after irradiation. The dielectric coatings were subjected to additional tests (adhesion, abrasion and humidity, etc.) as per MIL-M-13508C and MIL-C-675C. All 15 glasses studied showed varying amounts of transmission loss as expected, with negligible degradation for three types. Recovery of transmissions with time/ageing was also studied, with more or less complete recovery with temperature annealing. A faster bleaching of darkened/brown glasses was achieved by using UV lamps or UV laser. The dielectric coatings (HR, AR) and one of the two commercial optical cements showed excellent resistance to neutrons and gamma radiations, and could be good candidates for the fabrication and utilization of optical components in extreme radiation environments. The data allowed several Chinese glasses to be studied for the first time.     

Platinum promoted zirconia-sulfate catalysts: one-pot preparation,physical properties and catalytic activity

A new innovative methodology for the single-stage preparation of ZrO₂-SO₄ and Pt/ZrO₂-SO₄ catalysts is reported, based on the sol-gel technique. Catalysts are characterized by analysis, XRPD, BET and IR methods and are tested in the isomerization of butane.     

Optimisation of metallic pigments in coatings by an electrochemical technique and an investigation of manganese powder as pigment for metal rich primers

Zinc dust and manganese powder as pigments were incorporated in epoxy-polyamide and butyl titanate medium, with different pigment volume concentration (PVC) ranging from 20 to 74. These protective coatings were coated on sand blasted mild steel substrates and immersed in 3 wt.% sodium chloride solution and the corrosion current was measured by the Tafel extrapolation method. From the corrosion current produced by these primers, the optimum level of the pigments in these binders was identified. Thus the protective performance of optimised primers was evaluated on a sand blasted mild steel surface by the Tafel polarisation method in 3 wt.% sodium chloride solution, over different periods of time. The results were found to be comparable with the salt spray test and galvanic current measurements. The manganese powder used for this investigation showed that it could be used as an alternative to zinc powder for metal rich primers.     

Oxidation of methane over platinum in a solid proton-conducting electrolyte cell

Studies of the complete oxidation of methane on a Pt electrode-catalyst in the cell with a solid proton-conducting electrolyte (CH₄ + O₂, Pt ¦ SrCe_0.92Dy_0.08O₃ ¦ Pt, H₂O + N₂) were carried out. The non-Faradaic effect of electrochemical hydrogen pumping on the rate of methane oxidation has been demonstrated. The induced change in the reaction rate at anodic polarization of a Pt electrode-catalyst was over two orders of magnitude higher than the rate of hydrogen pumping from the reaction zone through the electrolyte.     

化学镀Ni-P-PTFE复合镀层的性能

本文对化学镀ＮｉＰＰＴＦＥ复合镀层的性能作了测定和评价。实验表明，用优化的镀液配方和工艺可获得含ＰＴＦＥ粒子２５～３０％ｖｏｌ的ＮｉＰＰＴＦＥ复合镀层。这种镀层具有优良的结合力和良好的耐蚀性，其硬度随ＰＴＦＥ含量增加而降低，其特别突出的性能是优异的减摩性和耐磨性，是一种具有自润滑功能的表面复合材料。     

The applicability of the ITS-90 method to platinum resistance thermometers of different purity

The static characteristics of platinum resistance thermometers with different platinum purities were measured. It is shown that in the 0–420°C range the ITS-90 method gives an error of less than 0.01°C, while in the 0–230°C range the error is less than 0.006°C. __________ Translated from Izmeritel’naya Tekhnika, No. 12, pp. 33–36, December, 2006.     

Advanced Coatings on Furnace Wall Tubes

Nickel-based self-fluxing alloy coating extends the service life of furnace wall tubes at waste incineration plants due to its excellent corrosion resistance and heat resistance. Fusing of such coatings by induction heating offers improved efficiency and reliability of products. Compared with conventional plasma, flame, and high-velocity oxy-fuel spraying thermal-sprayed coatings, induction-fused coatings provide a far stronger metallurgical bond at the interface, while minimizing the inclusion of pores. In addition, the tubes are less costly than those with welded coatings, and the process reduces the distortion of the products, facilitating easier final assembly. A successful experimental application of 11 units in a waste incinerator revealed virtually no corrosion on the exposed surfaces, and showed an improved water heating efficiency over that of the original tubes. Such units are now being employed in four incinerators in Taiwan, and continuing tests are showing great promise.