Rapid determination of the fracture toughness of metallic materials using circumferentially notched bars

Three types of material whose fracture toughness tests were previously performed by using circumferentially notched bars, namely (1) a dual-phase steel with three different morphologies; (2) an Al-Zn-Mg-Cu-wrought alloy; and (3) Al-Si-cast alloys with three different Si contents, were investigated in terms of accuracy and reliability of the testing method. Also, the advantages of using circumferentially notched bars for fracture toughness determination of metallic materials were discussed. With the help of stress concentration factors, which are associated with the bluntness of the notch, correction factors for the fracture toughness calculations are derived. The corrected fracture toughness values are found to be close to the uncorrected ones, implying that the testing procedure is reliable.     

Oscillating Cup Viscosity Measurements of Aluminum Alloys: A201, A319 and A356

An oscillating cup viscometer was developed to measure the absolute viscosities of molten metals. Previous experiments established the capability of the apparatus to characterize the viscosities of molten nickel-based superalloys. However, modifications to the instrument and its theoretical analysis were required for reliable measurements on molten aluminum alloys, presumably due to their lower densities and lower viscosities. The theoretical literature for the fluid flow inside an oscillating cup is reviewed, and a working equation without any correction factor is developed for the improved viscometer. Some design parameters of the viscometer that directly affect the accuracy of viscosity estimation by using the working equation are discussed. A special vertical furnace was adopted to uniformly heat a longer cylindrical sample (10 mm inner diameter and 120 mm length) with a temperature difference of less than 2°C over the sample length. The measuring procedure was also improved to get more accurate motion parameters. It is estimated that the working equation and improved instrument provide an uncertainty of less than 4%. In addition, applications and experimental data are presented for pure aluminum and three aluminum alloys: A201, A319, and A356.     

Electroplating of nickel-cadmium alloys from alkaline solutions

The electroplating of Ni-Cd alloy coatings was carried out from alkaline baths (pH 10). For comparison, electroplating of the parent metals, Ni and Cd, was performed individually under the same conditions. The cathodic current efficiency for codeposition was high and decreased with increasing current density. The codeposition process is an anomalous type of plating with Cd being the preferentially deposited metal. The Ni content in the deposits increased with increasing current density. This increase in Ni content improves the corrosion resistance and microhardness of the deposits. X-ray diffraction analysis showed that the deposits consist of a mixture of Ni, β, γ, γ¹ phases.     

形状记忆合金薄膜的研究与发展

形状记忆合金是智能结构研究中重点开发的传感和驱元件材料之一。然而ＳＭＡ体材料响应速度较慢，在一五程度上限制了它的应用。ＳＭＡ薄膜弥补了这一缺陷，且更易于智能能结构集成化。本文介绍了国内外关于ＳＭＡ薄膜研究的现状。并展望了未来发展。     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

镍代钴矿用硬质合金的新进展

概述了镍代钴矿用硬质合金的国内外进展情况．     

制备W－Ni－Cu钨合金的热解还原法工艺探讨

用硝酸镍、氯化铜与乙酸镍、乙酸铜的溶液分别与钨粉混合，干燥，经热解还原法制备的Ｗ－Ｎｉ－Ｃｕ钨合金，其技术指标均可满足使用要求。文章分析、讨论了这两种工艺特性及存在的问题。采用硝酸镍、氯化铜代镍、铜所制备的钨合金，在热解还原过程中产生大量有毒气体、严重的污染环境。乙酸镍、乙酸铜代镍和铜制备的钨合金，在热解还原过程中较好地解决了对环境及产品的污染问题，并保持了热解还原工艺的特性。     

钛及钛合金中氧和氢的联合测定

叙述了用红外吸收法对钛及钛合金中氧和氢联合测定的方法，取得了测定的最佳条件。连续测定6次的相对标准偏差在10％以下，作加标回收试验的回收率为95．6％～103．9％。分析时间在3min以内，可应用于日常分析，结果满意。     

复合微粒高性能混凝土的二级界面显微结构及耐久性研究

将天然纳米纤维材料及活性球形掺合料复合应用于高性能混凝土中,用以改善高性能混凝土的二级界面,探讨胶凝材料的颗粒紧密堆积及显微结构。对混凝土力学性能的研究表明:改善混凝土的二级界面,可以大幅度提高其抗弯强度和弹性模量;对耐久性的研究表明,由于加入了纳米纤维材料,改善了体系颗粒级配及二级界面显微结构,增加了体系密实度,是提高混凝土抗冻性、抗渗性的有效途径。因而,研究高性能混凝土的二级界面显微结构,对于提高高性能混凝土的宏观物理力学性能及耐久性存在巨大潜能。     

Corrosion fatigue of extruded magnesium alloys

Corrosion fatigue tests were carried out on extruded AZ31 (3% Al, 1% Zn, 0.3% Mn, Mg—the rest), AM50 (5% Al, 0.4% Mn, Mg—the rest) and ZK60 (5% Zn, 0.5% Zr, Mg—the rest) Mg alloys in air, NaCl-based and borate solutions. N_sol/N_air ratios (the relative fatigue life) were used for the analysis of the corrosion fatigue behavior of Mg alloys in various environments, where N_sol and N_air are the numbers of cycles to failure in the solution and in air, respectively. Extruded ZK60 alloy reveals very high fatigue and corrosion fatigue properties in comparison with other alloys. However, it has the lowest relative fatigue life (N_sol/N_air 10⁻³–10⁻²) or the highest sensitivity to the action of NaCl-based solutions in comparison with that of AM50 and AZ31 alloys (N_sol/N_air 10⁻²–10⁻¹). Under the same stress, the corrosion fatigue life of extruded alloys is significantly longer than that of die-cast alloys (N_sol for extruded AM50 in NaCl is two to three times longer than that of die-cast AM50).