高合金钢铸造用涂料的试制与开发

介绍了炉爪用合金钢1Cr25Ni20Si2Re,导板用合金钢2Cr32Ni5采用串箱铸造过程中，有关镁砂粉涂料和石英粉涂料的试制。结果表明：镁砂粉涂料为不透气涂料，不太适用，而合理配方的石英粉涂料使用性能良好。     

Experimental Study on Polymer Artificial Bone with HA Coated and Fiber Liners

1Introduction HA(hydroxyapatite)wasakindofbioactiveceram ics,whichhadexcellentbiocompatibilityandtissueaffin ityinthatitscomponentsweresimilartothoseofhuman bone[1].Soitwasthebestknownhumanbonesubstitute,andunprecedentedeffecthadbeenharvestedinrecenttwo d…     

Plasma Sprayed Hydroxyapatite Coatings with Nano-hydroxyapatite Prepared by Ultrasonic Precipitation Process

Nano-particle hydroxyapatite （ HA ） was prepared with a novel ultrasonic precipitation process and the as-prepared nanopowder was used to produce hydroxyapatite （ HA ） coatings on titanium substrate via plasma spraying. The phase and the microstructare of the coating were characterized by X- ray diffraction （XRD） and scanning electron microscopy （SEM）. Results showed that spherical particles could be prepared by ultrasonic precipitation process; and a corresponding dense HA coating with molten surface and low-porosity cross-section structure was acquired. During the plasma spraying process, new phases of Ca3 （ PO4 ）2 and Ca2 P2O7 were generated. After heat-treating at 800℃ for 1 h, the contents of Ca3 （ PO4 ）2 and Ca2 P2O7 decreased while HA content increased. Tensile adhesion tests showed that the plasma sprayed coating prepared with the spherical nanoparticles exhibited high tensile bond strength.     

Water‐Stable,Magnetic Silica–Cobalt/Cobalt Oxide–Silica Multishell Submicrometer Spheres

A method to produce monodisperse magnetic composite spheres with diameters from less than 100 nm to more than 1 μm in water solution is reported. The spheres consist of a dielectric silica core and a cobalt/cobalt oxide shell which can be protected from further oxidation with an outer shell of silica or, alternatively, they can be covered with the polymer polyvinylpyrrolidone as a stabilizer. The formation of a uniform magnetic shell proceeds with the adsorption of metallic cobalt seeds, produced by the reduction of cobalt chloride with sodium borohydride, on a self‐assembled layer of polyelectrolytes on the silica core. In the second step, an outer silica shell can be formed by the hydrolysis and condensation of (3‐aminopropyl)trimethoxysilane and tetraethoxysilane. The double‐shell composite spheres show excellent sphericity, monodispersity, and a magnetic hysteresis loop at room temperature.     

橡塑共混热塑性弹性体的形态结构与性能

综述了影响共混热塑性弹性体的形态结构与性能的主要因素。     

电子自旋共振在橡胶研究中的应用

综述了电子自旋共振在橡胶的合成、加工和应用领域的应用现状及其发展前景。     

激光辐照制备搪瓷涂层

激光辐照制备的搪瓷涂层表面粗糙,与金属基材结合牢固。一般由 Si,Al,Na,K,B,F,O等元素组成。在激光辐照过程中 K,Na 明显地挥发,从而在涂层中的含量明显减少;Co,Ni,主要分布在界面附近;Fe 元素也由基材进入涂层,呈梯度状分布,在界面过渡区含量很高,在涂层内含量很低。搪瓷涂层的形成与激光辐照参数,特别与激光功率间存在极为密切的关系;只有选用合理的参数,才能制得搪瓷涂层。     

顺丁橡胶后处理新型交替运输机

在顺丁橡胶后处理生产线上，用处行开发的新型交替运输取代原有运输机。试用结果表明，采用新型交替运输机后，胶块的导向到位率由７０％提高到９８％；减轻了劳动强度，提出了生产开工率，运行周期可达１ａ以上。     

Some factors affecting the electrical properties of carbon-black-loaded butyl rubber during vulcanization

Butyl rubber mixtures loaded with 70 phr general purpose furnace black (GPF) and tetramethyl thiuram disulphide (TMTD)/S as vulcanizing system were prepared. The kinetics of their electrical conductivity development during the vulcanization process were followed by using an especially devised system. It was found that the increase in the electrical conductivity during vulcanization obeys an exponential growth function with time constant τ, which markedly decreases with increasing vulcanization temperature as well as with the efficiency of the vulcanizing system. After completion of the vulcanization process, about 80 min, the samples obtained possess reasonable stability and reproducibility of electrical conductivity.     

防腐涂料及涂装技术(Ⅷ)

防腐涂料及涂装技术讲座系列介绍防腐蚀涂料的品种和各类应用及最新产品研究进展。本讲主要介绍涂装前的表面预处理方法及表面处理质量的评定等