混凝土构件的涂装保护

分析了自然环境对混凝土构件的影响，简述了混凝土构件涂装对防腐蚀涂料的要求及常规涂装保护措施。     

Normalized age applied to AAR occurring in concretes with or without mineral admixtures

This paper presents a method for assessing the normalized age factors, which allow accelerated alkali-aggregate reaction (AAR) tests performed at various temperatures (20, 40 and 60 °C) to be related to the conditions encountered in situ in concrete structures. The evaluation of normalized age factors is based on the comparison of many experimental results taken from the literature concerning laboratory tests and in situ measurements. The use of these factors permits us to evaluate, from the results of an accelerated test performed at 60 °C, the protection time against AAR that could be expected for in situ concretes containing mineral admixtures (silica fume and fly ashes). The results show that, in addition to the inhibitory action of mineral admixtures leading to a strong decrease in the final AAR-swelling, the protection against abnormal expansion caused by AAR increases significantly when mineral admixtures are used. Abnormal expansion is expected at 2-4 years for plain concrete compared to 7-50 years for concrete with mineral admixtures.     

Statistical prediction of fracture parameters of concrete and implications for choice of testing standard

This article shows how the fracture energy of concrete, as well as other fracture parameters such as the effective length of the fracture process zone, critical crack-tip opening displacement and the fracture toughness, can be approximately predicted from the standard compression strength, maximum aggregate size, water-cement ratio, and aggregate type (river or crushed). A database, consisting of 238 test data, is extracted from the literature and tabulated, and approximate mean prediction formulae calibrated by this very large data set are developed. A distinction is made between (a) the fracture energy, G_f, corresponding to the area under the initial tangent of the softening stress-separation curve of cohesive crack model, which governs the maximum loads of structures and is obtained by the size effect method (SEM) or related methods (Jenq-Shah two-parameter method and Karihaloo's effective crack model, ECM) and (b) the fracture energy, G_F, corresponding to the area under the complete stress-separation curve, which governs large postpeak deflections of structures and is obtained by the work-of-fracture method (WFM) proposed for concrete by Hillerborg. The coefficients of variation of the errors in the prediction formulae compared to the test data are calculated; they are 17.8% for G_f and 29.9% for G_F, the latter being 1.67 times higher than the former. Although the errors of the prediction formulae taking into account the differences among different concretes doubtless contribute significantly to the high values of these coefficients of variation, there is no reason for a bias of the statistics in favor of G_f or G_F. Thus, the statistics indicate that the fracture energy based on the measurements in the maximum load region is much less uncertain than that based on the measurement of the tail of the postpeak load-deflection curve. While both G_f and G_F are needed for accurate structural analysis, it follows that if the testing standard should measure, for the sake of simplicity, only one of these two fracture energies, then G_f is preferable.     

Performance of recycled aggregate concrete monitored by durability indexes

The report of an investigation into the performance of concrete manufactured with recycled aggregate (RA) using durability indexes as indicators is presented in this paper. Durability indexes, such as chloride conductivity, oxygen permeability and water sorptivity, of three different concrete mixes containing 0%, 50% and 100% RA were monitored at ages 3, 7, 28 and 56 days. The results show that durability quality reduced with increase in the quantities of RA included in a mix; however, as expected, the quality improved with the age of curing. At the age of 56 days, increases in index value of a concrete mix made with 100% RA over that made with 100% natural aggregate were 86.5% and 28.8%, respectively, for chloride conductivity and water sorptivity. The corresponding value of oxygen permeability index (OPI) for the same concrete mixes was a reduction of 10.0%. For 50% RA concrete, the reductions in chloride conductivity and water sorptivity indexes at the curing age of 56 days compared to 3 days were 62.7% and 42.7%, respectively. The corresponding figure for OPI was an increase of 37.6%. The poor performance of the RA concrete is associated with the cracks and fissures, which were formed in RA during processing, thereby rendering the aggregate susceptible to permeation, diffusion and absorption of fluids.     

Removal of phosphate from wastewaters

Gas concrete waste was used to remove phosphate from aqueous solutions in this study. The influence of suspension pH, temperature, mixing rate, and gas concrete dosage on phosphate removal was investigated by conducting a series of batch adsorption experiments. In addition, the yield and mechanisms of phosphate removal were explained on the basis of the results of X-ray spectroscopy, measurements of zeta potential of particles, both values of BET-N₂ specific surface area, and images of scanning electron microscopy (SEM) of the particles before and after adsorption. In this study, phosphate removal in excess of 99% was obtained and it was concluded that wastes of gas concrete are an efficient adsorbent for the removal of phosphate. The removal of phosphate predominantly takes place by precipitation mechanism and the weak physical interactions between the surface of adsorbent and the metallic salts of phosphate.     

Experimental research and prediction of the effect of chemical and biogenic sulfuric acid on different types of commercially produced concrete sewer pipes

New equipment and procedures for chemical and microbiological tests, simulating biogenic sulfuric acid corrosion in sewerage systems, are presented. Subsequent steps of immersion and drying, combined with mechanical abrasion, were applied to simulate events occurring in sewer systems. Both chemical and microbiological tests showed that the aggregate type had the largest effect on degradation. Concrete with limestone aggregates showed a smaller degradation depth than did the concrete with inert aggregates. The limestone aggregates locally created a buffering environment, protecting the cement paste. This was confirmed by microscopic analysis of the eroded surfaces. The production method of concrete pipes influenced durability through its effect on W/C ratio and water absorption values. In the microbiological tests, HSR Portland cement concrete performed slightly better than did the slag cement concrete. A possible explanation can be a more rapid colonisation by microorganisms of the surface of slag cement samples. A new method for degradation prediction was suggested based on the parameters alkalinity and water absorption (as a measure for concrete porosity).     

Internal deterioration of concrete by the oxidation of pyrrhotitic aggregates

This paper presents research results on the causes of a severe concrete deterioration, which occurred in many building foundations approximately 2 years after construction. Concrete samples were investigated with X-ray diffraction (XRD) analysis, a scanning electron microscope (SEM) and a petrographic examination performed with a stereomicroscope. It was found that the early cracking of concrete stemmed from the oxidation of the pyrrhotite found in the anorthosite aggregates used to produce the concrete. The oxidation process led to the precipitation of iron hydroxides having a higher volume than the original pyrrhotite does. The presence of micas (biotite) close to the pyrrhotite seemed to promote and accelerate the oxidation process.     

Effect of γ-irradiation on strength of concrete for nuclear-safety structures

Concrete applied for construction of nuclear power plant (NPP) Temelín (Czech Republic) has been exposed to γ-irradiation up to dose 6×10⁵ Gy. Depending on the level of irradiation, changes in strength, porous structure and phase composition of the concrete have been studied. It is found that irradiation lowers both the strength of concrete (about 10%) and volume (resp. surface) of porous space. On the other hand, γ-irradiation increases the ratio of calcite, CaCO₃, in the concrete. Observed effects are discussed with respect to safety of NPPs.     

A comparison of bending strength between adhesive and steel reinforced concrete with steel only reinforced concrete

Cracking of brittle cementitious composites subjected to excessive loading causes a potential reduction in material performance. Steel bars or metal fibers typically act as tensile reinforcing in concrete composites to increase the material's structural capacity in bending and to delay or prevent matrix cracking.The goal of this research is to determine whether the performance in bending strength and material integrity of a typically reinforced cementitious composite may be improved through the release of “healing” chemicals, such as adhesives, from hollow fibers into cracks induced by loading in addition to the metal reinforcing. Adhesive-filled repair fibers are intended to break immediately upon cracking in the concrete thereby activating the healing process with the release of a sealing or adhering substance. This self-repair occurs whenever and wherever cracks are generated.     

国内聚羧酸系高性能减水剂的合成及研究状况

简述了聚羧酸类减水剂合成方法、分子结构与性能的关系,讨论了大单体聚乙二醇丙烯酸酯等的制备工艺技术。