Experimental and numerical investigation of fracture in double-edge notched steel plates

Double-edge notched (DENT) steel plates were pulled until complete fracture and several experimental observations were made (using profilometry and scanning electron microscopy). The essential work of fracture (EWF) model was found to be well verified. Numerical simulations—up to the maximum load only—of some experiments were performed using the finite element method (FEM), and incorporating geometric and material non-linearities (large deformation elasto-plasticity). Some experimental measurements were compared with the corresponding numerical computations and excellent agreement was found.     

提高辽河原油重交通道路沥青的质量

辽河油田石化总厂为提高从辽河原油生产重交通道路沥青的质量，对所用的辽河原油中的低凝点环烷基原油经过分储、分输、分炼，对减压蒸馏塔进行改造，控制减压拔出率，对直馏沥青进行轻度氧化，使９０号重交通道路沥青中沥青质的含量大于１０％，蜡含量小于２％，质量达到了国际先进水平。     

粘钢技术在输水管竖井加固中的应用

１９７６年汛前发现响水潭水库输水管竖井圆筒底部与闸室连接处的下游出现环形水平裂缝，对此当年曾加固处理。１９８６年复查时，发现竖井原处又出现了类似的环形裂缝，并有新的发展，为确保工程安全，于１９９４年３月再次加固。此次加固采用先止水，后粘钢板的加固方法，收到很好的效果。     

直接还原在当代冶金变革中的发展

简述了当代的直接还原现状与方法，论述了直接还原是发展短流程的重要基础，直接还原也是熔融还原法的重要组成，同时分析了发展直接还原与熔融还原是当代世界冶金变革中的重要方向之一，也是中国面向２１世纪的重大任务。     

用SBR1502胶浆制取道路沥青改性用胶乳

用附聚法和降粘法浓缩ＳＢＲ１５０２胶浆制取道路沥青改性用胶乳。结果表明：总固物质量分数可由（２１±２）％上升到４５％～５０％。该胶乳与齐鲁石化公司炼油厂１００号乙沥青混合，改性后的道路沥青具有良好的使用性能，可满足高等级路面沥青的技术要求。     

Nb,Ti微合金钢热变形的动态模拟变形抗力模型

本文报道 Nb,Ti 微合金钢的热变形动态模拟变形抗力模型。在试验中用热加工模拟试验机进行高温压缩试验,其变形温度为1123—1423K,变形速率为0.1—60s~(-1)。结果表明,在峰值以前该钢种的流变应力数学模型为:σ=5.99.ε~(0.167)·(?)~(6.47×10~(-5)·T)·exp(4064/T)。形变激活能(Q)为444 kJ/mol,β系数为0.080。峰值应力(σ_p),临界应变(ε_c)和温度补偿应变速率参数(Z)之间的关系分别为:σ_p=12.56·lnZ-391.8;lnε_c=0.157·lnZ-7.39。     

简易炉外处理在电炉钢生产中的应用

阐述了小电炉采用投资少，见较快，简单易行的炉外处理措施，提高了钢质量和生产率，生产实践和应用结果表明，本措施可为同类型企业的炼钢工艺完善和技术进步提供参考。     

THE FRACTURE MECHANISM OF 475°C EMBRITTLEMENT IN A DUPLEX STAINLESS STEEL

The mechanism of “475°C embrittlement” of a duplex stainless steel was investigated using finite element modelling of the stress distribution at brittle fracture initiation. Brittle fracture initiated at a critical shear stress, which increased with ferrite hardness. The fracture stress was affected by the duplex microstructure. Fracture was nucleated by deformation twins, which were identified using electron back-scatter diffraction. The ductile-to-brittle fracture transition was sensitive to age-hardening and could be described simply by the effect of age-hardening and test temperature on the yield stress.     

低合金高强度钢的微观组织和疲劳裂纹扩展行为

用透射电镜观察了３０ＣｒＭｎＳｉＮｉ２Ａ钢等温的微观组织，疲劳裂纹扩展行为、裂纹尖端塑性区和位错结构，结果表明，等温状态组织由马氏体和贝氏体组成。在一个奥氏体晶粒内一般存在四个板条领域、裂纹尖端的塑性区内存在主位错带，疲劳断裂的基本组织单元为板条晶或板条束。裂纹遇到板条束界时方向发生较大偏斜。     

Failure analysis of a wire rope

Wire ropes, pulleys, counterweights, and connecting systems are used for auto tensioning of contact wires of electric railways. A wire rope in one such auto tensioning system suffered premature failure. Failure investigation revealed fatigue cracks initiating at nonmetallic inclusions near the surface of individual wire strands in the rope. The inclusions were identified as Al-Ca-Ti silicates in a large number of stringers, and some oxide and nitride inclusions were also found. The wire used in the rope did not conform to the composition specified for AISI 316 grade steel, nor did it satisfy the minimum tensile strength requirements. Failure of the wire rope was found to be due to fatigue; however, the ultimate fracture of the rope was the result of overload that occurred after fatigue failure had reduced the number of wire strands supporting the load.