Effect of microstructure on the fatigue crack growth behaviour of a near-α Ti alloy

Fatigue crack growth behaviour of Ti–6Al–2Zr–1.5Mo–1.5V (VT-20 a near-α Ti alloy) was studied in lamellar, bimodal and acicular microstructural conditions. Fatigue crack growth tests at both increasing and decreasing stress intensity factor range values were performed at ambient temperature and a loading ratio of 0.3 using compact tension samples. Lamellar and acicular microstructures showed lower fatigue crack growth rates as compared to the bimodal microstructure due to the tortuous nature of cracks in the former and the cleavage of primary α in the latter. The threshold stress intensity factor range was highest for acicular microstructure.     

Effect of microbial hydrogen consumption on the hydrogen permeation behaviour of AISI 4135 steel under cathodic protection

The feasibility of microbial hydrogen consumption to mitigate the hydrogen embrittlement (HE) under different cathodic potentials was evaluated using the Devanathan-Stachurski electrochemical test and the hydrogen permeation efficiency η. The hydrogen permeation efficiency η in the presence of strain GA-1 was lower than that in sterile medium. The cathodic potential inhibited the adherence of strain GA-1 to AISI 4135 steel surface, thereby reducing the hydrogen consumption of strain GA-1. The adherent GA-1 cells were capable of consuming ‘cathodic hydrogen’ and reducing the proportions of absorbed hydrogen, indicating that it is theoretically possible to control HE by hydrogen-consuming microbes.     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

ZK60镁合金表面滚压强化试验研究

试验研究了ZK60镁合金表面滚压加工中工艺参数对试件表面粗糙度、表面形貌、表面残余应力和表层显微硬度的影响,结果表明滚压力和重复滚压次数对试件的表面粗糙度、表面形貌以及表面残余应力和表层硬度影响程度较大,滚压速度影响较小。对精车ZK60镁合金试件进行滚压加工,试件表面粗糙度R a、R z最大减小了50.3%和48.1%;残余压应力最大可达-54.55 MPa;显微硬度从试件表层到内部基体材料逐渐降低,表层硬度值最大为92.83 HV 0.25,比基体材料硬度提高了15.32%。     

Corrosion behaviour of AA2024 aluminium alloy in different tempers in NaCl solution and with the CeCl3 corrosion inhibitor

The paper analyses the corrosion behaviour of naturally and artificially aged AA2024 alloy in NaCl solution and in the presence of an environment-friendly corrosion inhibitor, CeCl₃. On the basis of the values of polarisation resistance and corrosion current density, the corrosion resistance of the protective inhibitor film is established as well as the general corrosion resistance of this aluminium alloy. Resistance to pit formation is determined based on the difference in pitting and corrosion potentials while resistance to pit growth is determined based on the amount of charge consumed during pit growth. A scanning electron microscope is used to examine the morphology of the pits formed during the pitting corrosion testing, as well as to determine the cerium content on intermetallic particles and the matrix AA2024 alloy. The corrosion behaviour of AA2024 alloy is investigated after different test periods in NaCl solution and in the same solution with the CeCl₃ inhibitor. The corrosion resistance of both tempers of AA2024 alloy is more than one order of magnitude higher in the presence of CeCl₃. An explanation of the observed differences in the corrosion behaviour of the naturally and artificially aged AA2024 alloy is proposed. Different corrosion behaviour of the alloy after different test periods is also explained.     

雕刻技术的研制和应用

在对铝合金铸件进行X射线实时探伤时，由于采集回来的许多图像的目标物体的轮廓比较模糊，这样在评片时容易造成对铸件的误判和漏判。针对这种现象并结合这类图像噪声源多的特点，在研究常用卷积算法的基础上，采用特殊卷积（特殊的卷积核）操作，同时根据雕刻的艺术底色为灰色，最后给卷积结果加上灰度值128，实验结果表明图像中目标物体的轮廓变得更清楚，同时处理后的图像具有比较好的三维效果，这给工作人员在看图时带来了方便。     

Microstructures and Phase Transition Points of As-Cast Mg-Zn-Y System Alloys

As-east mierostruetures and their distribution of Mg-Zn-Y ternary alloy with high magnesium, low zinc and yttrium were examined using Nikon Epiphot optical microscopy （OM）, RigakuD/max-3C X- ray diffraetion （XRD）, and JEOL JSM-6700F scanning electron microscopy （SEM） equipped with an energydispersive X-ray spectroscopy （EDS）. In the as-east mierostructures, Yttrium and zinc tend to segregate at grain boundaries,     

Oxidation of Hastelloy-XR Alloy for Corrosion-Resistant Glass-Coating

The oxidation behavior of Hastelloy-XR alloy was investigated to obtain the optimum surface condition for corrosion-resistant glass-coatings. The surface morphology of oxide scales changed significantly with variation of temperatureand oxygen partial pressure (po2 ). The oxidation kinetics was mainly parabolic independent of oxidation conditions.The oxide scales were consisted of inner Cr2O3 and outer spinel layers. The phase component of spinel layers wereMn1.5Cr1.5O4 and (Mn,Ni)(Cr,Fe)2O4 for the oxygen partial pressures po2<10 kPa and po2>10 kPa, respectively.The optimum oxidation condition to obtain an oxide scale for well-adhered glass-coating to the substrate was 1248 Kand po2 =0.01 kPa for the oxidation time of 43 ks.     

噻吩在镍基非晶态合金上的吸附和脱附

应用静态吸附、动态吸附、程序升温脱附和程序升温还原等实验方法，考察了噻吩在Ni基非晶态合金上的吸附和脱附行为。常温下，噻吩分子首先吸附在清洁的Ni表面，并立刻被活化，发生氢解反应，C-S键断裂，释放出烃类部分，S留在Ni原子上。噻吩可以在Ni基非晶态合金表面发生强度不同的化学吸附。弱化学吸附的噻吩可以脱附；强化学吸附的噻吩不会脱附，而在高温下发生氢解反应。