Towards optimization of the osmotic drying process of alumina-gelatin objects: Regression analysis and verification

In this study, further analysis of the osmotic drying process was conducted to identify the optimum combination of parameters for drying rectangular alumina-gelatin beams. This study was designed to determine the effect of three variables related to the osmotic drying process (osmotic pressure, molecular weight, and immersion time) on the interaction between the liquid desiccant and the submerged alumina-gelatin samples. The water loss from the alumina-gelatin samples was positively correlated with the molecular weight, osmotic pressure, and immersion time. Up to 40% by weight of the initial water content was removed during the osmotic drying process. The samples also experienced solids gain due to the counterflow of solute from the liquid desiccant. The least amount of solids gain resulted from drying for the shortest immersion time at low osmotic pressure and high molecular weight. Evidence of possible interactions between variables was noted for the sintered density metric. Statistical methods were used to form regression equations for the measured responses (water loss, solids gain, bulk density). A verification experiment was conducted to compare the experimental outcomes to the predicted outcomes. The responses were simultaneously optimized to identify the combination of variable settings required to meet specified goals. In order to maximize water loss, minimize solids gain, and maximize bulk density, the ceramic-gelatin object should be immersed for approximately 60?min in an aqueous solution of 100,000?g/mol poly(ethylene oxide) at an osmotic pressure of 2.50?MPa. These values are valid for the range of parameter settings tested and the sample fabrication and drying methods used.     

Structure and electrical properties of Ca2+-doped (Na0.47Bi0.47Ba0.06)TiO3 lead-free piezoelectric ceramics

The lead-free piezoelectric ceramics (Na_.47Bi_.47Ba_.06)_1-xCa_xTiO₃ (x?=?0, 0.01, 0.02, 0.03, 0.05, and 0.08, abbreviated as BNBTC/0, BNBTC/1, BNBTC/2, BNBTC/3, BNBTC/5, and BNBTC/8, respectively) were obtained using the solid-state reaction method. The structure, electric conductivity, and dielectric, ferroelectric, and piezoelectric properties of the Ca²⁺-doped (Na_.47Bi_.47Ba_.06)TiO₃ ceramics were thoroughly investigated. The ceramics sintered at 1200?°C exhibit dense microstructures, having relative densities higher than 96%. The X-ray diffraction results demonstrate that all ceramics have a pure perovskite structure. The mean grain sizes of the ceramics are related to the Ca²⁺ quantity. A small quantity of Ca²⁺ ions (x?≤?0.03) improves the piezoelectric and ferroelectric properties of the samples. The dielectric behavior of the samples is sensitive to the Ca²⁺ content and electric poling. The results demonstrate that the electrical properties of the (Na_.47Bi_.47Ba_.06)TiO₃ lead-free ceramics can be well tuned by varying the Ca²⁺ quantity.     

Calorimetric study of ytterbium orthovanadate YbVO4 polycrystalline ceramics

The heat capacity of ytterbium orthovanadate was first measured by adiabatic calorimetry in the temperature range T?=?12.28–344.06?K. No obvious anomalies were observed on the curve obtained. The values of standard thermodynamic functions in the temperature range T?=?0–400 K were calculated. Based on low-temperature calorimetry data obtained, previously published data on the high-temperature heat capacity of ytterbium orthovanadate were corrected. The anomalous contribution to heat capacity for YbVO₄ was compared with the data known for YbPO₄.     

Estimation of the Stress-Strength Reliability for Exponentiated Pareto Distribution Using Median and Ranked Set Sampling Methods

In reliability analysis, the stress-strength model is often used to describe the life of a component which has a random strength (X) and is subjected to a random stress (Y). In this paper, we considered the problem of estimating the reliability R=P [Y<X] when the distributions of both stress and strength are independent and follow exponentiated Pareto distribution. The maximum likelihood estimator of the stress strength reliability is calculated under simple random sample, ranked set sampling and median ranked set sampling methods. Four different reliability estimators under median ranked set sampling are derived. Two estimators are obtained when both strength and stress have an odd or an even set size. The two other estimators are obtained when the strength has an odd size and the stress has an even set size and vice versa. The performances of the suggested estimators are compared with their competitors under simple random sample via a simulation study. The simulation study revealed that the stress strength reliability estimates based on ranked set sampling and median ranked set sampling are more efficient than their competitors via simple random sample. In general, the stress strength reliability estimates based on median ranked set sampling are smaller than the corresponding estimates under ranked set sampling and simple random sample methods.     

Self-repair of structural and functional composites with intrinsically self-healing polymer matrices: A review

Self-healing is a smart and promising way to make materials more reliable and longer lasting. In the case of structural or functional composites based on a polymer matrix, very often mechanical damage in the polymer matrix or debonding at the matrix–filler interface is responsible for the decrease in intended properties. This review describes the healing behavior in structural and functional polymer composites with a so-called intrinsically self-healing polymer as the continuous matrix. A clear similarity in the healing of structural and functional properties is demonstrated which can ultimately lead to the design of polymer composites that autonomously restore multiple properties using the same self-healing mechanism.     

Study on wax precipitation characteristics of wax deposit in pipes

Wax deposit properties are a significant concern in pipeline pigging during waxy crude oil transportation. In the present work, the impacts of flow conditions and oil properties on the wax precipitation characteristics of wax deposits are investigated. A flow loop apparatus was developed to conduct wax deposition experiments using four crude oils collected from different field pipes. The differential scanning calorimetry (DSC) technique was employed to observe the wax precipitation characteristics of crude oil and wax deposit. The results show that the wax content and the wax appearance temperature (WAT) of the deposits increase with shear stress and radial temperature gradient, and decrease with radial wax molecule concentration gradient near the pipe wall. The DSC tests on the wax deposits revealed that the deposit wax content is strongly correlated to the oil wax content. Furthermore, an empirical correlation was developed to predict the wax content and the WAT of the wax deposit. Verification of the empirical correlation using the different oils indicated that the average relative error of the wax content prediction and average absolute error of WAT prediction were 13.2% and 3.6°C, respectively.     

Bearing Failure Optimization of Composite Double-Lap Bolted Joints Based on a Three-Step Strategy Marked By Feasible Region Reduction and Model Decoupling

To minimize the mass and increase the bearing failure load of composite doublelap bolted joints, a three-step optimization strategy including feasible region reduction, optimization model decoupling and optimization was presented. In feasible region reduction, the dimensions of the feasible design region were reduced by selecting dominant design variables from numerous multilevel parameters by sensitivity analyses, and the feasible regions of variables were reduced by influence mechanism analyses. In model decoupling, the optimization model with a large number of variables was divided into various sub-models with fewer variables by variance analysis. In the third step, the optimization sub-models were solved one by one using a genetic algorithm, and the modified characteristic curve method was adopted as the failure prediction method. Based on the proposed optimization method, optimization of a double-lap single-bolt joint was performed using the ANSYS^® code. The results show that the bearing failure load increased by 13.5% and that the mass decreased by 8.7% compared with those of the initial design of the joint, which validated the effectiveness of the three-step optimization strategy.     

Tribological behavior of Zr-based bulk metallic glass sliding against polymer,ceramic, and metal materials

The tribological properties of zirconium-based bulk metallic glass (BMG) sliding against polymers, steels, and ceramics at different loads and speeds were investigated. Acoustic emission (AE) technology was used to analyze wear states. The frictional coefficients of the BMG slid against the steel and ceramic balls were high but decreased with increased applied normal load and sliding speed. As the steel balls were more ductile than the ceramic ones, the steel–BMG sliding pairs generated weaker AE signals and exhibited larger wear rates. The BMG tested against the polymer balls had much lower and more stable frictional coefficients than the ones against the steel or ceramic balls because of transferred polymer layers on the BMG surfaces. The BMG against the polymer balls also exhibited the highest AE signals among the three types of counter materials used, indicating that abrasive wear dominated in the polymer-BMG sliding pairs. These results demonstrated the potential application of the BMG as a new tribomaterial that could be an alternative to the traditional crystalline metals for various counter materials.