针对包装机械的特点，从二次开发的定义出发，分析比较了AutoCAD二次开发的各种手段形式，给出了应用实例。     

苯并口恶嗪-环氧化合物-胺类催化剂体系开环聚合反应的研究

采用TLC，GPC，1H－NMR及IR等分析方法，对苯并恶嗪－环氧化合物－胺类催化剂体系的聚合反应进行了研究，表征了产物结构，并探讨了聚合反应机理，结果表明，苯并恶唪－环氧化合物体系在胺类催化剂如苄胺，咪唑的作用下，能发生开环聚合反应，生成低分子量的聚合物。     

Sensitizing Mechanism and Adsorption Properties of Dye—Sensitized TiO2 Thin Films

The dye-sensitized TiO2 complex films were prepared by the dye coat onto TiO2 surfaces,and the sensitizing mechanism and adsorption properties of the dye-sensitized TiO2 complex films were inverstigated.The influence of the application conditions of dye adsorbed on TiO2 films on the amount of dye adsorption was discussed.Experimental results show that the concentration,the temperature of dye solutions and the dipping time of TiO2 films in the dye solutions have a significant influence on the amount of dye adsorption.Cell test indicates that the conversion efficiency of light to electricity increases with the amount of dye adsorption.     

硫化胶交联结构及其性能

综合讨论了聚合物／聚合物之间的交联结构及聚合物／填料之间的偶联结构对硫化胶抗硫化返牟性，抗氧老化性及动态疲劳性能的影响。     

基于ODMG—93标准的面向对象视图集成机制

模式集成多数据库系统中需要解决的关键问题之一，己存在的大多数面向多数据库系统都采用了面向对象视图机制来建立集成模式。为了满足基于ＣＯＲＢＡ的ＣＩＭＳ信息集成平台呆订成的需要，本文提出了一种基于数据库管理组ＯＤＭＧ的ＯＤＭＧ－９３标准的视图集成机制并通过一个完整的例子说明了这种视图机制在模式集成中的应用。     

聚醚酰亚胺热焓松弛的分子量依赖关系

采用ＤＳＣ对不同分子量的聚醚酰亚胺的等温及动态热焓松弛行为进行了研究，并以ＫＷＷ方程对实验数据进行了非线性拟合。结果表明，分子量对热焓松弛的影响是由高分子端基引起自由体积的差异所致。不同分子量的聚醚酰亚胺分子具有不同数量的端基，淬冷时端基数目的差异将产生不同数量的过剩自由体积，从而影响松弛热焓及松弛速率、低分子量的聚醚酰亚胺松弛相对较快，且起始热焓高，松弛的表观活化能亦较小。     

湿敏半导体材料电导率计算方法的研究

结合修正了的耗尽层理论和多孔湿敏半导体的特点，本文提出了一个简单的物理模型作为ｎ型湿敏半导体特征的一级近似。描述了多孔湿敏半导体的导电机理，并给出了湿度与宏观电导率的关系。     

Growth of Fe on Si (100) at room temperature and formation of iron silicide

Low-energy electron diffraction (LEED), Auger electron spectroscopy and X-ray photoelectron spectroscopy (XPS) investigations of both the growth of an iron film on silicon (100) at room temperature and the subsequent formation of iron silicide are the subjects of this paper. An in-situ cleaned silicon (100) wafer without carbon or oxygen contamination exhibiting the known 2 × 1 reconstruction in the LEED pattern served as the substrate. Iron was deposited on this reconstructed surface at 300 K. The comparison of theoretical calculations based on three growth mechanisms with XPS data obtained with take-off angles of 0° and 50° clearly demonstrates a layer-by-layer growth of the iron film on silicon (100). At 300 K no formation of iron silicide was observed, although an interaction between iron and silicon could be detected at the interface. The formation of iron silicide was observed at annealing temperatures of 630–730 K. Quantitative XPS analysis yields the presence of FeSi₂, when the thickness is large enough. Neither the iron film on silicon nor the silicide shows any LEED pattern.     

苎麻阳离子改性的研究（三）：改性苎麻的染色机理

采用上染速率，等温吸附模型，Ｚｅｔａ电位、染料与纤维的结合力等方法从理论上研究了改性苎麻的染色机理，苎麻改性后，纤维表面的Ｚｅｔａ电位由原来的－４２ｍＶ提高到－１８ｍＶ，正电性显著增加，提高了阴离子染料对改性苎麻的亲和力，上染率高，节约染料。     

管内机器人研究中的几项新技术

介绍了我们研制的管内机器人中应用的具有创新性的三项技术：１．轮式全主动新型行走机构；２．内壁环带视觉装置；３．新型离心喷涂器。