高速电喷镀制备纳米PTFE镍基复合镀层

研究了以Q235和65Mn钢为基底,经高速电喷镀形成的纳米PTFE镍基复合镀层,考察了喷射速度对镀层沉积速率、表面显微硬度、结晶组织形貌以及镀层结合力的影响,探讨了喷射速度影响镀层性能组织的原因机理。结果表明,喷射速度在4.2～6.3m/s时获得的镀层有较高的沉积速率和表面硬度,晶粒细小、组织致密,镀层结合力较高。     

Effect of binder-phase modification and Cr3C2 addition on properties of WC-IOC0 cemented carbide

For production of fine-grained and corrosion-resistant tungsten carbide (WC) based cemented carbides, addition of chromium carbide (Cr₃3C₂) in small amounts is standard practice. No systematic study, however, has been made of the effects of large additions (maximum 6 wt % ) of Cr₃C₂ as a substitute for tungsten carbide. This study focuses on the effect of hard-phase substitution by C₃C₂ in WC-1OCo cemented carbide. An attempt is also made to modify the binder metal cobalt by partial or complete substitution of nickel. Specimens were prepared using the standard liquid-phase sintering process and were tested for sintered porosity, mechanical properties, corrosion resistance, and microstructural parameters. Results confirm the findings of earlier workers regarding grain refinement and improvement of mechanical properties upon the addition of small amounts (<2 wt%) of Cr₃C₂. Modification of the binder phase improves indentation fracture toughness and corrosion resistance. Addition of Cr₃C₂ independent of the binder type improves corrosion resistance.     

脉冲电场作用下SiCp/2014颗粒增强铝基复合材料的制备

介绍了一种新的制备颗粒增强铝基复合材料的方法，对处于熔点以上的铝液及SiCp颗粒施加一定时间的电脉冲，观察其凝固组织，发现增强颗粒分布均匀，基体合金晶粒细小，致密度正常，强度，耐磨性较高，该 方法是一种简单易行的制备颗粒增强铝基复合材料的新方法。     

离心铸造CrMoWVNb白口铸铁轧辊的研究

应用离心铸造方法：以Cr,Mo,V,Nb为主要合金元素，研制成功了CrMoWVNb白口铸铁轧辊，分析了合金元素在轧辊中的作用，指出在轧辊中加入适量稀土和钛可细化轧辊组织，改善轧辊性能，同时还分析了轧辊生产中裂纹产生的原因，提出了消除裂纹的措施，并应用于高速线材轧机预精轧机架，使用寿命达到高镍铬无限冷硬铁轧辊的4－5倍。     

旋转交变磁场和静磁场对Al-18%Si合金变质处理的影响

分别研究了旋转磁场和静磁场对过共晶Al-18％Si合金变质处理的影响。结果表明：变质处理后．不施加磁场的条件下，块状初晶Si偏聚在试样边缘处，试样中心处为共晶Si；施加旋转交变磁场的条件下，粗大的板条状初晶Si偏聚在试样边缘处，试样中心处为共晶Si；施加静磁场的条件下，在试样整个横断面上初晶Si都是细小的块状，且大小和分布均匀。     

WELL-DISPERSED NANODIAMOND AQUEOUS SUSPENSIONS——PREPARATION,PROPERTIES AND APPLICATIONS

1　INTRODUCTIONAsitwassynthesizedundertheconditionofhightemperatureandhighpressure ,andowingtothecommoncharacteristicsoffinedimensionandhighsurfaceenergyofnanoscaledparticles ,nanodiamond (ND )preparedbydetonationexplosioncaneasilyformstrongaggregates WhenNDpowderwasaddedinaqueousmedia ,obviousaggregationandsedimentationcanbeobserved ,whichimpairsitscharacteristicsasananometerparticle ,andthushindereditsapplication Inthiscase ,stabledispersionofNDinaqueousmediaisofgreatimportance[1 4 ] …     

阻燃镁合金AZ91D的研究

研究了通过添加铍，可得到直接暴露在大气中熔炼的镁合金AZ91D。通过金相组织观察发现：当铍的含量达到0.015%时，合金的晶粒度最好，而且具有很好的阻燃性能；同时研究了采用不同的变质剂AZ91D合金进行变质处理。实验结果表明：变质处理的AZ91D合金，组织明显细化，尤其是时效处理后，其力学性能得以大幅度提高，拓宽了合金的使用范围。     

Gas chromatographic thermodynamics on hydration processes of magnesium chloride with low water

1　INTRODUCTIONMagnesiumchlorideisabasicmaterialforchem icalindustry ,andithaswideapplicationsinmetallur gy,architecturalmaterialandtextileindustry .Itisalsoamaterialforfire resistantproducts ,cryogenandcompoundfertilizerproductions[1] .Thefullydehy dratedmagnesiumchlorideisagoodmaterialforelec trolyticmetalmagnesium production .Becausemag nesiumchloridehasastrongadsorptiveability ,itisalsousedasadryingagent .Manysuccessfulworkshavebeendoneonthedehydrationofbischophite[2 10 ] .Butinfact,…     

钛及钛合金表面强化技术

介绍了钛及钛合金的表面强化处理技术，综合评述了钛及钛合金表面氮化、渗碳和激光熔覆技术的发展现状。根据目前的研究趋势指出：今后对钛及钛合金表面强化处理技术，应结合各种工艺技术的特点制备多层复合涂层，以及涂层 渗层的思想进行研究。作者认为，降低表面改性层处理成本，使表面处理工艺更加简单．同时综合多种表面处理技术的优点，提高表面改性层的综合性能是钛及钛合金表面强化技术今后的研究方向。     

亚共晶铝硅合金锶变质处理的孕育和衰退

通过考察A356合金变质后在静置和重熔过程中细化效果的变化,分析研究了亚共晶铝硅合金变质处理的孕育和衰退,以及合金锭预变质对变质效果的影响.结果表明,变质衰退表现为Sr含量低于某一临界值,有效期取决于初始Sr含量、熔化工艺及精炼方法等;变质处理孕育期的直接成因是中间合金释放Sr元素并与Si晶胚达到吸附平衡需要一定的时间;采用预变质合金锭,能够消除变质处理孕育期,稳定变质效果.