用AFM导电探针在n-Si(111)表面进行纳米加工的机理研究

本文介绍了在AFM针尖与氢钝化硅表面之间施加电场作用对硅表面进行修饰的纳米加工方法，重点讨论了加工机理。实验考虑了样品的表面状态，周围大气状况，所加电压的极性、大小和加压方式等影响纳米加工的因素。对机理的研究表明，针尖和样品之间发生的是场致电子发射而非热电子发射，电流热效应增强粒子的扩散能力，提高了电化学反应速度。最后给出了电场诱导阳极氧化扩散增强的加工机理。     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

催化裂化汽油光化学氧化脱硫

以水为萃取剂、空气中的O2为氧化剂、500W高压汞灯为紫外光光源,研究了催化裂化(FCC)汽油光化学氧化反应的机理和氧化产物,考察了反应条件对FCC汽油脱硫率的影响。实验结果表明,FCC汽油中的极性含硫化合物首先部分溶于水相中,然后在水相中被氧化。在空气通入量为150mL/min、水与FCC汽油的体积比为1.0的条件下,反应5h后FCC汽油脱硫率达40.6%,加入0.45g4A分子筛作为O2的吸附剂后FCC汽油脱硫率提高到70.2%。FCC汽油的光化学氧化反应为一级动力学反应,加入4A分子筛时的反应速率常数为0.217 4h-1,半衰期为3.18h。FCC汽油光化学氧化反应的主要产物为亚砜和砜,并进一步生成CO2、草酸、SO24-等。     

电子产品研制阶段可靠性增长试验研究

结合工程实际经验,深入讨论了可靠性增长过程及实现途径,在保持试验条件和改进过程不变的条件下,实施了对具体型号电子产品的可靠性增长试验,达到了预期的可靠性增长目标,并且利用可靠性增长试验的数学模型(AMSAA模型)来评估产品的可靠性增长,对开展可靠性增长与可靠性增长试验工作具有重要的实际意义.     

油品质量检验工作中应注意的十个问题

介绍了油品质检员做好油品检验工作在具体操作试验中应注意的十个问题，以确保试验数据真实有效，结论准确。     

橡胶促进剂DM的合成工艺

M氧化生成DM是自由基反应机理，结合微反应器机理，采用分子氧化的反应方式，选用绿色溶剂异丙醇、环境友好型氧化剂H202，一步法制取高品质DM。对反应时间、反应温度、氧化剂用量等因素进行考察，确定最佳工艺条件为：反应时间90min，反应温度55℃，氧化剂不过量，碱过量5％，M—Na溶液M含量30％，加料时N60 min，溶剂用量为M—Na溶液质量的1．5倍，所得产品质量合格，熔点可达180℃。     

Methane oxidation over vanadium-modified Pd/Al2O3 catalysts

Three different vanadium-modified Pd/Al₂O₃ catalysts were prepared and tested as catalysts for the deep oxidation of methane. Vanadium was added to the palladium catalyst by incipient wetness of palladium catalyst in order to modify its properties and improve its thermal stability and thioresistance. The behaviour of vanadium-modified catalysts depends on the concentration of this compound, being 0.5 wt.% the optimum amount. However, when strong catalyst poisons are present in the gas (SO₂), these modified catalysts do not show a better performance than unmodified catalyst. Bimetallic catalysts were tested with and without further reduction, being observed that reduced bimetallic catalysts perform worse than the non-reduced ones.     

仑16块泡沫辅助混气水驱先导性试验研究

百色盆地子寅油田仑16块砂岩油藏已进入特高含水开发后期,水驱剩余可采储量少,注水开发效果差。为提高区块采收率和开发效果,借鉴百色油田灰岩裂缝性油藏空气泡沫驱的成功经验,开展了泡沫辅助混气水驱先导性试验。试验结果表明,在地层温度49·5℃的低温轻质油藏中,注入的空气与地层残余油可以发生低温氧化(LTO)反应,产出气中氧含量低于2·6%,未出现气窜现象;对应油井产油上升、含水下降,预计最终采收率将提高10%左右,投入产出比大于1∶3·2。该试验的成功对砂岩油藏注水开发后期提高采收率具有重要的指导意义。     

CeO2对RuO2／γ-A12O3催化剂湿式氧化降解苯酚性能的影响

采用浸渍法制备了RuO2／γ-A12O3和RuO2／CeO2／γ-A12O3催化剂，并利用XRD、SEM和XPS对催化剂进行了表征，研究了Ce的加入对RuO2／γ-A12O3催化剂表面分散性和催化剂表面元素Ru，O和Ce化学态的影响，同时考察了RuO2／γ-A12O3和RuO2／CeO2／γ-A12O3催化剂湿式氧化降解苯酚的活性，并深入探讨了Ce对RuO2／γ-A12O3催化剂的助催化作用。结果表明：Ce掺杂改性后，使催化剂表面Ru的化学态降低、表面氧空位增加，并且活性组分Ru的分散性增加，从而使RuO2／CeO2／γ-A12O3催化剂的活性提高，因此Ce起到了显著的助催化作用。     

Oxidation of doped europium in BaMgAl10O17 by annealing studied by x‐ray‐absorption fine‐structure measurements

Abstract— We studied the influence of annealing in air on doped europium in BaMgAl₁₀O₁₇ by performing x‐ray absorption fine‐structure measurements. We determined the oxidation of doped divalent europium by annealing in air at over 500°C. The interatomic distance between the europium and the surrounding oxygen atoms was compressed by oxidation. It also appears that the oxidation process of europium is determined by the diffusion of oxygen into BaMgAl₁₀O₁₇.