Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Performance of insulated FRP-strengthened concrete flexural members under fire conditions

This paper presents the results of fire resistance tests on carbon fiber-reinforced polymer (CFRP) strengthened concrete flexural members, i.e., T-beams and slabs. The strengthened members were protected with fire insulation and tested under the combined effects of thermal and structural loading. The variables considered in the tests include the applied load level, extent of strengthening, and thickness of the fire insulation applied to the beams and slabs. Furthermore, a previously developed numerical model was validated against the data generated from the fire tests; subsequently, it was utilized to undertake a case study. Results from fire tests and numerical studies indicate that owing to the protection provided by the fire insulation, the insulated CFRP-strengthened beams and slabs can withstand four and three hours of standard fire exposure, respectively, under service load conditions. The insulation layer impedes the temperature rise in the member; therefore, the CFRP–concrete composite action remains active for a longer duration and the steel reinforcement temperature remains below 400°C, which in turn enhances the capacity of the beams and slabs.     

托盘式湿法烟气脱硫塔阻力特性研究

采用冷态物理模型结合商用CFD(Computational Fluid Dynamics)软件,对山东某火电厂300 MW机组配套托盘塔的流场和阻力特性进行了研究,取得了孔板阻力损失与液气比之间的二次函数关系。研究结果表明,塔内两相流场分布合理,入口处液滴受烟气的拖拽作用形成明显的干湿界面,负荷和液气比是影响脱硫塔阻力的重要因素。当液气比一定时,托盘上方能够维持相对稳定的持液层及鼓泡过程;满负荷运行时,脱硫塔阻力损失约为1600 Pa,其中孔板占1/4,持液层占3/4。拟合获得了托盘区阻力损失同液气比之间的关系,为托盘塔的应用、运行及优化提供了理论指导。     

某340矫直机上辊快开机构裂纹原因分析及预防措施

340管线矫直机是太原重工成熟产品,在国内占有较大市场,并出口印度、印尼、缅甸、埃及等国际市场。出口印度矫直机在质保期内出现主缸裂纹问题,为探明问题原因并杜绝类似情况发生,快开机构设计静强度分析、疲劳强度分析及生产加工过程等方面探查裂纹原因并提出几点预防措施。     

Influence of SiC content on the oxidation of carbon fibre reinforced ZrB2/SiC composites at 1500 and 1650 °C in air

The microstructure and the oxidation resistance in air of continuous carbon fibre reinforced ZrB₂–SiC ceramic composites were investigated. SiC content was varied between 5–20?vol.%, while maintaining fibre content at ～40?vol.%. Short term oxidation tests in air were carried out at 1500 and 1650?°C in a bottom-up loading furnace. The thickness, composition and microstructure of the resulting oxide scale were analysed by SEM-EDS and X-Ray diffraction. The results show that contents above 15?vol.% SiC ensure the formation of a homogeneous protective borosilicate glass that covers the entire sample and minimizes fibre burnout. The scale thickness is ～90?μm for the sample containing 5?vol.% SiC and decreases with increasing SiC content.     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

Studying the effect of organo-modified nanoclay loading on the thermal stability,flame retardant,anti-corrosive and mechanical properties of polyurethane nanocomposite for surface coating

Clay polyurethane nanocomposite (CPN) coating films were fabricated by uniformly dispersing nanoclay, organically modified with 25–30 wt.% octadecylamine in varying concentrations up to 5 wt.%, in a commercial two component, glossy, acrylic aliphatic polyurethane using ultrasonication. Organo-modified nanoclay was characterized by X-ray diffraction (XRD). The dispersion of the nanoclay into the matrix was investigated by scanning electron microscopy (SEM). CPN coating films were characterized by thermogravimetric analysis (TGA), and flame retardant, corrosion resistance and mechanical properties were also investigated. The XRD measurement indicated that, the organo-modified nanoclay particles were mainly constituted of montmorillonite with traces of quartz and calcite also found to be present. The SEM analysis showed that the nanoclay layers were dispersed and intercalated into the polyurethane coating. Thermogravimetric analysis showed that incorporating 5 wt.% organo-nanoclay into polyurethane considerably enhanced the thermal stability and increased the char residue to 14.11 wt.% relative to 4.58 for the sample without organo-nanoclay (blank polyurethane). The limiting oxygen index (LOI) test revealed that incorporation of organo-nanoclay led to a further increase in LOI values, which indicate an improvement in flame retardancy properties. The corrosion resistance also improved and this improvement increases with increase nanoclay wt.%. The mechanical resistance measurements demonstrated that the gloss of the CPN coating films slightly decreased, although hardness, adhesion and impact resistance of the CPN coating films improved with the incorporation of the organo-nanoclay.     

Q690钢焊接接头微观组织对冷裂纹的影响研究

分析了Q690钢手工电弧焊与气体保护焊焊接冷裂纹产生与微观组织的联系。结果表明: 焊接冷裂纹起源于斜Y坡口根部, 沿熔合区、焊缝扩展至焊缝表面;2种工艺焊接的接头组织硬度均较母材高, 而塑性较差。热影响区为马氏体、贝氏体与铁素体混合组织, 焊缝组织由先共析铁素体、侧板条铁素体、贝氏体和针状铁素体等组成, 针状铁素体抗裂纹扩展能力较其他组织强。在2种焊接方法对应断口中观察到了冷裂纹起裂、扩展与断裂区的不同形貌, 起裂与扩展区存在塑性变形, 而断裂区为解理断裂。     

机制砂混凝土耐磨性的主要影响因素分析及多因素计算模型

本文研究了砂类型、砂率、石粉含量和抗压强度对机制砂混凝土耐磨性的影响,建立了磨损量的多因素计算模型。结果表明:由于含石粉及具有更高的粗糙度和坚固性,石灰岩与辉绿岩机制砂制备的C30、C40混凝土耐磨性比河砂混凝土提高20%以上;在0.40~0.44范围内选取较低的砂率可获得较优的耐磨性;利用石粉含量为5%~11%(质量分数)的机制砂制备混凝土,石粉含量为9%时可获得最佳的混凝土耐磨性,微观分析表明此时混凝土密实度最佳;通过灰色系统理论确定了耐磨性影响因素的影响程度排序为:砂率R₃>压碎值R₂>粗糙度R₁>抗压强度R₅>石粉含量R₄>0.6;对比验证表明提出的混凝土磨损量多因素计算模型具有较高的预测精度和良好的适用性。