切削参数对锯片铣刀切削振动特性的影响研究

锯片铣刀切削加工过程中,普遍存在严重的振动问题.为研究锯片铣刀的切削振动特性,设计了多种切削条件下的锯片铣刀切削实验.在理论计算锯片铣刀固有频率的基础上,对实验结果进行了分析和讨论.结果表明:锯片铣刀切削系统的频率仅仅取决于系统的固有频率,基本不受切削参数的影响.因此,通过增加刀具系统的刚度或改变切削速度,使激振频率远离刀具系统的固有频率可有效降低和控制切削系统的振动.     

切削加工表面完整性建模现状与发展趋势

针对切削加工表面完整性建模方法种类繁多且相互关系揭示不明等问题,总结了各表面完整性指标,包括表面形貌、残余应力、加工硬化和相变的主要建模方法,并从各建模方法的应用范围以及主要成果的角度概括了表面完整性建模的研究现状.论述了解析建模与数值建模方法在预测表面完整性各指标时的优缺点及内在联系,重点分析了数值模拟技术在表面完整性建模中的作用.指出了国内外表面完整性研究体系的区别及联系,并对表面完整性建模的发展方向作了展望.     

Comparison of TiAIN,AICrN, and AICrN/TiAIN coatings for cutting-tool applications

Monolayer and bilayer coatings of TiAlN, AlCrN, and AlCrN/TiAlN were deposited onto tungsten carbide inserts using the plasma enhanced physical vapor deposition process. The microstructures of the coatings were characterized using scanning electron microscopy （SEM） and atomic force microscopy （AFM）. The SEM micrographs revealed that the AlrN and AlCrN/TiAlN coatings were uniform and highly dense and contained only a limited number of microvoids. The TiAIN coating was non-uniform and highly porous and contained more micro droplets. The hardness and scratch resistance of the specimens were measured using a nanoindentation tester and scratch tester, respectively. Different phases formed in the coatings were analyzed by X-ray diffraction （XRD）. The AlCrN/TiAlN coating exhibited a higher hardness （32.75 GPa）, a higher Young＇s modulus （561.97 GPa）, and superior scratch resistance （LcN = 46 N） compared to conventional coatings such as TiAlN, A1CrN, and TiN.     

环形刀高度变化刀路轨迹规划方法

为提高汽车覆盖件模具加工效率,将环形刀应用于汽车模具小曲率面的半精及精加工过程.通过对三坐标铣削小曲率面的刀具切触几何分析,确定环形刀最佳进给方向应沿工件高度变化方向,此时可使有效切削带宽达到最大.基于此结论,分别对两类特殊型面进行了刀路轨迹规划.对于单一方向曲率变化面采用垂直截面法,截面方向沿最大主曲率方向,实验表明:垂直截面法与等高线法相比可提高加工效率25%,并且有较好的表面质量;对于圆鼓面采用放射精加工方法,仿真结果表明:此方法与三维偏置方法相比可提高加工效率22.64%,并且避免了周边欠切.     

刀具几何角度对高速铣削性能影响的仿真分析

切削力和切削温度是影响刀具耐用度及被加工表面质量的重要因素,其中刀具几何角度在金属切削加工过程中对切屑的形成、切削力的大小以及散热条件等影响很大。因此,合理地选择刀具几何角度对提高刀具使用寿命和生产效率、降低生产成本具有重要意义。以铝合金7075-T651高速铣削为研究对象,借助金属切削工艺软件AdvantEdge对铣削加工进行模拟仿真,得到加工过程中切削力和温度随时间的变化关系,并结合单因素法,分析了不同刀具角度的选择对切削力和切削温度的影响。该结果为高速铣削刀具几何角度的选择提供参考。     

难加工材料细长薄板件的加工

针对难加工材料细长薄板零件的加工特点,设计了这类零件加工的刨削加工工艺方案,探讨了刨削加工方法在细长薄板零件加工中的应用.     

智能井用管线切割工具设计

采用智能完井技术的油井,修井周期长,长年生产的井中积累较多的油垢、胶质等杂物,修井时起出管柱较为困难。在管柱起出遇卡时,常规的切割工具只能对油管进行切割,无法对井下工具的控制管线进行切割。设计了一种专用的管线切割工具。介绍了该工具的结构、工作原理、技术参数、施工工艺。分析了关键结构的强度。通过ANSYS软件对管线剪切模型进行有限元分析,结果表明管线切割工具可承受拉力达800 kN,可对6根不同尺寸多种组合的控制管线进行切割。进行下部管柱打捞过程中,不会有冗杂的管线阻碍打捞作业。     

深井裸眼封隔器分段酸压管柱打捞实践

安岳气田灯影组气藏广泛采用大斜度井/水平井裸眼封隔器分段酸压工艺试油完井,悬挂封隔器及下部管柱被“永久性”留在井下。如果利用原裸眼侧钻,则需要打捞分段酸压管柱至套管鞋以下30 m左右。MX126井和GS121井前期打捞作业历时均超过50 d,打捞效率非常低,主要原因为：悬挂封隔器双向锚定,裸眼封隔器和连接油管埋卡严重且位于大斜度井段,压井后长时间静止埋卡越来越严重;钻井液压井后切割油管受阻,没有完成落鱼切割分段;套磨铣导致封隔器解体,倒扣时落鱼出现多处退扣,倒扣打捞效率低。针对上述问题,优化了打捞技术措施：钻井液压井前,采用泵送径向切割工艺在清水中切割油管,确保切割成功率;采用带压拔出插管循环压井,缩短钻井液浸泡时间,降低次生卡钻风险;优选磨铣工具和打捞工具,优化磨铣工艺和震击解卡打捞工艺,维持落鱼完整性、力求捞出整段被切割落鱼。该技术成功应用于MX146井和GS127井后期的打捞作业,分别用时12 d和5 d。该技术可以显著提高裸眼封隔器分段酸压管柱的打捞效率,具有推广应用价值。     

Machinability of a nickel aluminide intermetallic alloy

This article reports the results of an experimental study on the machinability of a nickel aluminide intermetallic alloy. Machining was conducted at various speeds, and results indicate low material removal rates. Chips collected for each test run were measured for thickness for shear angle calculation and were subsequently observed microscopically. Chip segmentation was observed microscopically, and a fluctuation in the shear angle was evidenced. A parameter characterizing the severity of the machining process, the chip reduction coefficient (K), was calculated from chip thickness measurements. The calculated values ofK were found to be low, indicating a low severity of the metalcutting process. This, however, is in contract with the observed low rates of metal removal and low tool life. Thus, conventional metalcutting characterization parameters require re- examination in terms of machining high-strength materials.     

Mechanism and prediction of failure of diamond films deposited on various substrates by HFCVD

Diamond films were deposited on the WC-Co cemented carbide and Si3N4 ceramic cutting tool substrates by hot-filament-assisted chemical vapour deposition. The adherence property of diamond films was estimated using the critical load (Pcr) in the indentation test. The adhesive strength of diamond films is related to the intermediate layer between the film and the substrate. Poor adhesion of diamond films to polished cemented carbide substrate is owing to the formation of graphite phase in the interface. The adhesion of diamond films deposited on acid etched cemented carbide substrate is improved, and the peeling-off of the films often happens in the loosen layer of WC particles where the cobalt element is nearly removed. The diamond films' adhesion to cemented carbide substrate whose surface layer is decarbonizated is strengthened dramatically because WC phase forms by reaction between the deposited carbon and tungsten in the surface layer of substrates during the deposition of diamond, which results in chemical combination in the film-substrate interface. The adhesion of diamond films to silicon nitride substrate is the firmest due to the formation of chemical combination of the SiC intermediate layer in the interfaces. In the piston-turning application, the diamond-coated Si3N4 ceramic and the cemented carbide cutting tools usually fail in the form of collapsing of edge and cracking or flaking respectively. They have no built-up edge(BUE) as long as coating is intact.As it wears through, BUE develops and the cutting force on it increases 1 - 3 times than that prior to failure. This can predict the failure of diamond-coated cutting tools.