 将任意差分精细积分法用于三维波动方程地震正演，关键在于如何消除数值计算中有限波场区域边界引起的边界反射。文中采用Berenger给出的电磁波完全匹配层吸收边界条件，推导出三维波动方程任意差分精细积分法地震正演的完全匹配层吸收边界条件计算公式，并给出了完全匹配层吸收边界条件算例。计算结果表明，此方法压制边界反射效果明显。三维波动方程地震正演模拟实例表明，完全匹配层吸收边界条件的任意差分精细积分法为复杂区地震波传播规律研究提供了一种实用的正演模拟工具     

垫层载荷试验应注意的几个问题

介绍了垫层上载荷试验的类型，通过工程实例对不同类型垫层上的载荷试验应注意的问题进行了分析和探讨，这对通过载荷试验确定双层地基承载力具有一定的实际意义，可供同类工程参考借鉴。     

溅渣护炉工艺探讨

从炉渣对炉衬和溅渣层的侵蚀机理入手,提出了兼顾冶金和溅渣双重效果的直接造渣工艺,探讨了终渣碱度、MgO、FeO含量等的调整范围,分析了溅渣操作中枪位、时间等的控制和炉底上涨的原因,以期更好地运用溅渣护炉技术。     

以不同PAN系炭纤维布制备燃料电池气体扩散层之研究

采用石墨化PAN系炭纤维布制备了高分子电解质燃料电池气体扩散层。通过电学实验、X-ray绕射与元素分析考察了所制气体扩散层的性能。结果表明：随热处理温度的升高，气体扩散层的电阻率降低，L2增加，d（x）2减小。高温处理后的炭纤维布作为高分子电解质燃料电池气体扩散层显示了较高的电池效能。     

Influence of the Preheat Treatment on the Microstructure and Properties of X37CrMoV5-1 Steel

The technological properties of the hot-work tool steels depend on their microstructural quality induced by the production process and the heat treatment. One of the frequently applied methods to improve microstructure is preheat treatment. The treatment of carbonitriding X37CrMoV5-1 steel has been investigated in fluidized bed furnaces. Thickness and phase composition have been conducted using optical microscopy Neophot 32 and scanning microscopy, JEOL 5400, after etching in nital.     

坨五站中间乳化层快速增长原因及治理方案

胜利采油厂坨五站高含水(95％)原油化学预脱水中，二级沉降罐内油水相之间的中间乳化层增长迅速，引起了一系列问题。现场调查和大量室内测试结果表明，产生这一现象的原因有：油溶性破乳剂WD-1加入点不合理。有2／3的含水原油在通过油水分离器之后才与破乳剂混合；二级沉降罐进油口伸入油相内，油流的冲击达不到中间层；WD-1对坨五站混合原油中的稠油破乳脱水性能欠佳，不能适应坨五站混合原油组成和含水的变化。针对上述各种原因筛选出了性能更好的一种破乳剂1916。根据确定的几种原因采取了相应的措施：将破乳剂加入点改在3个并联油水分离器之前；将二级沉降罐的进油口移到水相内；改用筛选出的破乳剂1916，结果使中间乳化层的增长受到了抑制。图2表4参2。     

Transition to turbulence in rotating-disk boundary layers—convective and absolute instabilities

This work is an experimental study of mechanisms for transition to turbulence in the boundary layer on a rotating disk. In one case, the focus was on a triad resonance between pairs of traveling cross-flow modes and a stationary cross-flow mode. The other was on the temporal growth of traveling modes through a linear absolute instability mechanism first discovered by Lingwood (1995, J Fluid Mech 314:373–405). Both research directions made use of methods for introducing controlled initial disturbances. One used a distributed array of ink dots placed on the disk surface to enhance a narrow band of azimuthal and radial wave numbers of both stationary and traveling modes. The size of the dots was small so that the disturbances they produce were linear. Another approach introduced temporal disturbances by a short-duration air pulse from a hypodermic tube located above the disk and outside the boundary layer. Hot-wire sensors primarily sensitive to the azimuthal velocity component, were positioned at different spatial (r,θ) locations on the disk to document the growth of disturbances. Spatial correlation measurements were used with two simultaneous sensors to obtain wavenumber vectors. Cross-bicoherence was used to identify three-frequency phase locking. Ensemble averages conditioned on the air pulses revealed wave packets that evolved in time and space. The space–time evolution of the leading and trailing edges of the wave packets were followed past the critical radius for the absolute instability, r _{c A} . With documented linear amplitudes, the spreading of the disturbance wave packets did not continue to grow in time as r _{c A} was approached. Rather, the spreading of the trailing edge of the wave packet decelerated and asymptotically approached a constant. This result supports the linear DNS simulations of Davies and Carpenter (2003, J Fluid Mech 486:287–329) who concluded that the absolute instability mechanism does not result in a global mode, and that linear-disturbance wave packets are dominated by the convective instability. In contrast, wave-number matching between traveling cross-flow modes confirmed a triad resonance that lead to the growth of a low azimuthal number (n = 4) stationary mode. At transition, this mode had the largest amplitude. Signs of this mechanism can be found in past flow visualization of transition to turbulence in rotating disk flows.     

不同加工工艺的锑化镓晶片损伤研究

用透射电子显微镜、扫描电镜对锑化镓材料切、磨、抛等加工工艺引入的表面损伤进行观察和检测。结果表明：切割加工是锑化镓单晶晶片表面损伤层引入的主要工序；锑化镓单晶切割片表面极不平整，有金刚砂所引起的较粗桔皮皱纹；其表面损伤层深度≤30μm；双面研磨的锑化镓晶片表面仍有较粗桔皮皱纹，但比切割片的要细，而且桔皮皱纹的深浅随磨砂（Al2O3)粒径的减小而变细变浅；晶片的表面损伤层深度（≤5μm）也随着磨砂粒径的减小而减小。一般情况下，其损伤层的深度约为磨砂粒径的1/2。机械化学抛光加工的锑化镓晶片表面的SEM像观察不到桔皮皱纹；其损伤层深度约55nm。     

针对混合应用业务的ARQ改进方案

在高速无线通信中,自动请求重传(ARQ)是链路层不可缺少的技术,它通过重传向上层屏蔽无线链路上包的丢失。随着无线网络的发展,无线传输速率不断提高,应用的业务类型也越来越广泛。目前,众多ARQ技术的研究都集中在如何提高该技术的确认效率,以适应更高的传输速率,但鲜有研究着手于如何使ARQ能够更好地应用于混合业务环境。针对混合业务环境下的ARQ改进提出了2种方案,并给出其中1种在实际应用中的改善效果。     

埋地管道三层PE外覆盖层及其检测方法研究

文章介绍了埋地管道三层PE外覆盖层系统的构造参数和性能特点,论述了两种用于埋地钢质管道外覆盖层状况检测的方法,一种是多频管中电流法,另一种是DCVG/CIPS组合检测技术。分别介绍了两种方法的工作原理、操作方法和设备,并结合工程实例进行了说明。这些方法和设备可分别或同时用于管道不开挖检测防腐层破损点的位置以及漏点大小。