The Effect of Structural Defects on the Thermal Conductivity of ZnS, ZnSe, and CdTe Polycrystals

ZnS, ZnSe, and CdTe polycrystals are experimentally investigated. Mechanisms are treated which restrict the thermal conductivity in samples prepared by recrystallization pressing and by deposition from the vapor phase and subjected to additional strain. Anomalies are observed on the temperature dependences of the thermal resistance of investigated samples, which are due to the special features of their phonon spectra and to the variation of the contribution made by longitudinal and transverse phonon branches to the heat transfer in the Debye temperature region and higher.     

Threshold and growth mechanism of fatigue cracks under mode II and III loadings

ABSTRACT The fatigue crack growth behaviour of 0.47% carbon steel was studied under mode II and III loadings. Mode II fatigue crack growth tests were carried out using specially designed double cantilever (DC) type specimens in order to measure the mode II threshold stress intensity factor range, ΔK_IIth. The relationship ΔK_IIth > ΔK_Ith caused crack branching from mode II to I after a crack reached the mode II threshold. Torsion fatigue tests on circumferentially cracked specimens were carried out to study the mechanisms of both mode III crack growth and of the formation of the factory‐roof crack surface morphology. A change in microstructure occurred at a crack tip during crack growth in both mode II and mode III shear cracks. It is presumed that the crack growth mechanisms in mode II and in mode III are essentially the same. Detailed fractographic investigation showed that factory‐roofs were formed by crack branching into mode I. Crack branching started from small semi‐elliptical cracks nucleated by shear at the tip of the original circumferential crack.     

金属基复合材料的热残余应力力学模型研究进展

金属基复合材料在高温制备的冷却过程中或热处理过程中由于组分间热膨胀系数（CTEs）的差异会产生较大的热残余应力，热残余应力对复合材料的宏观性能有着重要的影响。本文综述了分析金属基复合材料热残余应力的有限元模型和解析模型等理论模型，并指出有待深入研究的问题。     

Low-cycle fatigue properties of eutectic solders at high temperatures

This paper details the deformation mechanism and low‐cycle fatigue life of eutectic solder alloys at high temperature (around 0.8T_m). Grain boundary sliding generally nucleates a wedge‐type cavity that reduces the low‐cycle fatigue life of metals. In this study, grain boundary sliding has promoted intergranular failure contributing to the reduction in fatigue life of Sn–Ag–Cu alloy. However, grain boundary sliding has exerted no deleterious effects on fatigue resistance of eutectic Pb–Sn and Bi–Sn alloys. The phase boundary sliding with very fine microstructure induces exceptional ductility in these alloys leading to superior low‐cycle fatigue endurance for theses eutectic Pb–Sn and Bi–Sn alloys.     

Off-axis fatigue cracking behaviour in notched fibre metal laminates

The off‐axis fatigue cracking behaviour of notched fibre metal laminates under constant amplitude loading conditions was investigated experimentally and numerically. It was found that the off‐axis fatigue crack initiation life decreased as the off‐axis angles increased. This indicated that the off‐axis laminates raised the applied stress level in the aluminium (Al) layer and subsequently resulted in earlier cracking in the Al layer. The off‐axis fatigue crack initiation lives of notched fibre metal laminates were predicted using lamination theory and an energy‐based critical plane fatigue damage analysis from the literature. After a crack initiated in the Al layer, it was observed that the crack path angles of the off‐axis specimens were neither perpendicular to the fibre nor to the loading direction. A finite‐element model was established for predicting the crack path angles.     

Crack closure in fibre metal laminates

GLARE is a fibre metal laminate (FML) built up of alternating layers of S2-glass/FM94 prepreg and aluminium 2024-T3. The excellent fatigue behaviour of GLARE can be described with a recently published analytical prediction model. This model is based on linear elastic fracture mechanics and the assumption that a similar stress state in the aluminium layers of GLARE and monolithic aluminium result in the same crack growth behaviour. It therefore describes the crack growth with an effective stress intensity factor (SIF) range at the crack tip in the aluminium layers, including the effect of internal residual stress as result of curing and the stiffness differences between the individual layers. In that model, an empirical relation is used to calculate the effective SIF range, which had been determined without sufficiently investigating the effect of crack closure. This paper presents the research performed on crack closure in GLARE. It is assumed that crack closure in FMLs is determined by the actual stress cycles in the metal layers and that it can be described with the available relations for monolithic aluminium published in the literature. Fatigue crack growth experiments have been performed on GLARE specimens in which crack growth rates and crack opening stresses have been recorded. The prediction model incorporating the crack closure relation for aluminium 2024-T3 obtained from the literature has been validated with the test results. It is concluded that crack growth in GLARE can be correlated with the effective SIF range at the crack tip in the aluminium layers, if it is determined with the crack closure relation for aluminium 2024-T3 based on actual stresses in the aluminium layers.     

S-N-P curves in 7075 T7351 and 2024 T3 aluminium alloys subjected to surface treatments

The S-N-P (stress, number of cycles, failure probability) curves for 2024 T3 and 7075 T7351 aluminium alloys were obtained. Previously, surface treatments of degreasing and different types of anodizing were applied to samples, evaluating the influence of these treatments on the fatigue life of the alloys. The determination of the S-N-P curves was done using Maennig's method. Rotary fatigue was used because this technique produces greater stress on the sample surfaces, the zone in which it is important to evaluate fatigue resistance. Both the transition range and the finite life range were evaluated, calculating the 1, 50 and 99% fracture probability. SEM was performed in order to characterize the fracture micromechanism. The conclusions were that Maennig's method is useful to evaluate fatigue life of these materials in a fast and efficient manner. Moreover, surface treatments produce a decrease in the fatigue life of both alloys, associating this effect with the surface damage produced on each sample during the treatment.     

Finite-element analysis and experimental study on tensile fatigue behaviour of bitumen–stone adhesion

Tensile fatigue behaviours of bitumen–stone adhesion were investigated using a dynamic mechanics analyser under stress‐controlled mode at two temperatures of 5 and 25°C and various controlled‐stress levels. Failure characteristics including interfacial failure and cohesive failure were examined using image analysis of fracture surfaces. Finite‐element analysis on stress distributions was conducted under different temperatures, film thickness and interfacial bonding conditions. A Coulomb–Mohr like criterion in combination with shear and normal stresses is proposed to deal with the extreme thin adhesive layer, which can be further simplified into an adhesive zone without significant loss of accuracy for stress analysis.     

改进的基于TMS320DM642的疲劳检测系统

针对疲劳检测算法中大数据量、高速传输、复杂运算的实际需要，设计了以SAA7115为视频采集A／D、DSPTMS320DM642为核心处理器、SAA7105为视频输出D／A，并以FPGA控制输出来实现增强显示功能的实时视频处理系统。该系统采用双摄像头控制采集数据，可以满足多路视频的实时采集、处理、显示需求，可以作为疲劳检测算法、视频处理和图像处理的硬件平台。