埋弧自动焊在大口径钢卷管焊接上的应用

为把埋弧焊应用在大口径钢卷管焊接上,分析了焊接工艺设计、焊接工装设计和纵缝、环缝焊接的施工要点,经过实际施工验证了这种方法是成功的,效益是高的。     

A novel arc welding inverter with unit power factor based on DSP control

A novel inverter power source is developed characterized with constant output current and unit power factor input. Digital signal processor （ DSP ） is used to realize power factor correction and control of back-stage inverter bridge of the arc welding inverter. The fore-stage adopts double closed loop proportion and integration （PI） rectifier technique and the back- stage adopts digital pulse width modulation （ PWM） technique. Simulated waves can be obtained in Matlab/Simulink and validated by experiments. Experiments of the prototype showed that the total harmonic distortion （THD） can be controlled within 10% and the power factor is approximate to 1.     

海洋平台大厚度焊接接头断裂韧度

依据BS7448断裂韧度试验标准(ISO／TC164／SC4-N400)，对采用埋弧焊(SAW)工艺施焊的、板厚为54mm的海洋石油平台大厚度对接接头试样进行了低温裂纹尖端张开位移(CTOD)试验。分别测试了-15℃下单丝和双丝埋弧焊工艺下焊缝金属和热影响区的CTOD值。试验表明，除双丝埋弧焊热影响区试件外，其余试件均满足挪威船级社DNV规定的最小特征CTOD为0．15mm的要求，为指导海洋平台的施工建造提供了科学依据。     

膜式水冷壁多焊机群控系统

基于DSP的多焊接电源群控系统被应用于膜式水冷壁焊机中.该系统引入优先级群控策略,多台焊接电源在外部参数发生波动时,按不同优先级的群控策略进行有序调整,减小了调整时间和调整误差.同时,根据焊接区域和焊接过程中管屏温度场分布规律,引入焊接参数实时调整策略,实现多台焊接电源在起弧段、稳弧段和收弧段等不同焊接过程的参数动态调整.结果表明,使用该系统控制焊机中的多台焊接电源,膜式水冷壁管屏焊接变形得到有效控制,焊接质量有较明显的提高.     

磁粉探伤焊缝区反常显示成因分析

研究了中碳钢焊缝区磁粉探伤出现的假磁痕,对焊接过程和焊缝组织进行分析,制订出合理的焊接工艺,避免表面缺陷检测的误判。     

药芯焊丝气体保护焊在高压Cr-Mo钢管上的应用

采用钨极惰性气体保护焊(GTAW)打底与药芯焊丝气体保护焊(FCAW)填充、盖面的焊接方法对ASME SA-335 P22和ASME SA-335 P11钢管做了焊接工艺评定。分别对其焊缝进行了拉伸、弯曲、冲击和硬度检测等力学性能试验，并通过金相照片对焊缝的微观组织进行了分析，结果证明工艺评定焊缝的各项力学性能指标都达到了ASME Ⅸ的要求，该焊接方法在实际生产中是可行的。     

Microstructures and mechanical properties of welded Fe-12Cr-20Mn austenitic stainless steel

The effects of welding on the tensile and fatigue properties of fully annealed and cold-worked Fe-12Cr-20Mn austenitic stainless steel were evaluated. Room temperature and 500 °C tensile tests and room temperature cantilever beam fatigue tests were accomplished on specimens that contained autogenous bead-on-plate welds. The tensile and fatigue properties of the fully annealed material were not significantly influenced by welding. The tensile properties of the welded cold-worked material were also not significantly affected by the presence of a weldment. However, welding caused a large reduction of the fatigue life of the cold-worked material. Fatigue cracks preferentially initiated at large Mn-Si inclusions that formed in the fusion zones of the weldments.     

镁合金激光焊接技术的研究现状与应用

镁在自然界中是大量存在的,我国的镁资源非常丰富,镁及其合金均具有许多优点,如重量轻、比强度和比刚度高、消震性能好、优良的机械加工性能和抛光性能、无毒性、无磁性、高热导率以及可回收利用等,已在汽车、精密仪器、电子、体育器械、核电、国防以及航空航天等许多领域得到了广泛的应用,具有广阔的应用前景.主要论述了镁合金激光焊接技术的现有水平与发展趋势以及镁合金激光焊接技术的应用领域及应用前景.     

电子束焊接工艺参数与温度场的关系

采用有限元方法,定量分析了电子束焊接工艺参数与铍环内表面温度的关系。结果表明,加热深度或电子束斑点半径增加,内表面温度增加,焊接速度增加,内表面温度降低。