Seismic behavior of geosynthetic-reinforced retaining walls backfilled with cohesive soil

This study investigates the seismic performance of geosynthetic-reinforced modular block retaining walls backfilled with cohesive, fine grained clay-sand soil mixture. Shaking table tests were performed for three ½ scaled (wall height 190 cm) and ¼ scaled model walls to investigate the effects of backfill type, the influence of reinforcement length and reinforcement stiffness effects. The El Centro and Kobe earthquake records of varying amplitudes were used as base acceleration. Displacement of the front wall, accelerations at different locations, strains on the reinforcements, and the visual observations of the facing and the backfill surface were used to evaluate the seismic performance of model walls. The model walls were subjected to rigorous shaking and the walls did not exhibit any stability problems or signs of impending failure. The maximum deformations observed on the models with cohesive backfill was less than half of the deformation of the sand model. The load transfers between the geogrid and cohesive soil was comparable to that of sand and hence the needed reinforcement length was similar as well. As a result; the model walls with cohesive backfills performed within acceptable limits under seismic loading conditions when compared with granular backfilled counterparts.     

Strength of pure alumina ceramics above 1 GPa

Up to now, commercially available alumina ceramics were claimed to have strength between 400 and 550 MPa. However, our study shows strength ~ 2 times higher for commercially available alumina than commonly believed. The average and characteristic strength, measured on 31 pure alumina ceramic discs by ball on three balls (B3B) test, were 1205 ± 93 MPa and 1257 MPa, respectively, with a Weibull modulus of m = 11.8. Tested specimens were in form of discs with a diameter of 5 mm and thickness 0.5 mm. The grain size distribution of the alumina is bimodal with an average grain size of ~ 850 nm measured at the surface. The fracture reveals a mixed transgranular / intergranular failure mode. To avoid incorporation of additional flaws, the discs were tested as sintered. The characteristic flexural strength measured in B3B was recalculated according to Weibull theory for standard 4-point bending bars of size 3 × 4 × 45 mm as bend 856 MPa. The measured strength of nearly 900 MPa shows the potential of strength for high purity alumina ceramics.     

Identification of Host Cellular Protein Substrates of SARS-COV-2 Main Protease

The novel severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2) is the causative agent of coronavirus disease-19 (COVID-19) being associated with severe pneumonia. Like with other viruses, the interaction of SARS-CoV-2 with host cell proteins is necessary for successful replication, and cleavage of cellular targets by the viral protease also may contribute to the pathogenesis, but knowledge about the human proteins that are processed by the main protease (3CLpro) of SARS-CoV-2 is still limited. We tested the prediction potentials of two different in silico methods for the identification of SARS-CoV-2 3CLpro cleavage sites in human proteins. Short stretches of homologous host-pathogen protein sequences (SSHHPS) that are present in SARS-CoV-2 polyprotein and human proteins were identified using BLAST analysis, and the NetCorona 1.0 webserver was used to successfully predict cleavage sites, although this method was primarily developed for SARS-CoV. Human C-terminal-binding protein 1 (CTBP1) was found to be cleaved in vitro by SARS-CoV-2 3CLpro, the existence of the cleavage site was proved experimentally by using a His₆-MBP-mEYFP recombinant substrate containing the predicted target sequence. Our results highlight both potentials and limitations of the tested algorithms. The identification of candidate host substrates of 3CLpro may help better develop an understanding of the molecular mechanisms behind the replication and pathogenesis of SARS-CoV-2.     

GOLPH3 Regulates EGFR in T98G Glioblastoma Cells by Modulating Its Glycosylation and Ubiquitylation

Protein trafficking is altered when normal cells acquire a tumor phenotype. A key subcellular compartment in regulating protein trafficking is the Golgi apparatus, but its role in carcinogenesis is still not well defined. Golgi phosphoprotein 3 (GOLPH3), a peripheral membrane protein mostly localized at the trans-Golgi network, is overexpressed in several tumor types including glioblastoma multiforme (GBM), the most lethal primary brain tumor. Moreover, GOLPH3 is currently considered an oncoprotein, however its precise function in GBM is not fully understood. Here, we analyzed in T98G cells of GBM, which express high levels of epidermal growth factor receptor (EGFR), the effect of stable RNAi-mediated knockdown of GOLPH3. We found that silencing GOLPH3 caused a significant reduction in the proliferation of T98G cells and an unexpected increase in total EGFR levels, even at the cell surface, which was however less prone to ligand-induced autophosphorylation. Furthermore, silencing GOLPH3 decreased EGFR sialylation and fucosylation, which correlated with delayed ligand-induced EGFR downregulation and its accumulation at endo-lysosomal compartments. Finally, we found that EGF failed at promoting EGFR ubiquitylation when the levels of GOLPH3 were reduced. Altogether, our results show that GOLPH3 in T98G cells regulates the endocytic trafficking and activation of EGFR likely by affecting its extent of glycosylation and ubiquitylation.     

樟芝多糖通过降低NLRP3 Caspase1炎性小体表达改善帕金森小鼠神经行为学的机制研究

目的:研究樟芝多糖通过降低NLRP3-Caspase1炎性小体表达改善6-OHDA构建的帕金森小鼠模型的行为学机制。方法:利用6-OHDA脑内注射构建帕金森小鼠模型，通过酪氨酸羟化酶（TH）免疫组化染色和行为学判定小鼠模型的构建成功。利用樟芝多糖进行干预，分别在干预前、干预后的第1、3、7天4个时间点进行神经行为学实验，分别采用转棒实验、爬杆实验检测小鼠自主行为能力以及协调能力，4个时间点取小鼠尾静脉外周血采用ELISA法检测外周血中Caspase1和IL-1β的表达，樟芝多糖干预第7天时待进行完行为学实验后小鼠断颈处死，取小鼠脑组织-纹状体，Western blot法检测纹状体中Caspase1、proCaspase1、NLRP3的表达，高效液相色谱检测纹状体中单胺类神经递质的表达，RT-QPCR检测Caspase1、NLRP3、IL-1β、IL-4、IL-6的mRNA表达。NISSl染色检测小鼠脑组织神经细胞凋亡情况。 结果:6-OHDA脑内注射可以造成小鼠帕金森样病变，且TH蛋白表达显著下调，樟芝多糖干预后小鼠的行为学得到显著改善（P<0.05），纹状体中Caspase1、proCaspase1、NLRP3的表达显著下调，与模型小鼠相比具有统计学差异（P<0.05），且相关炎症因子Caspase1、NLRP3、IL-1β、IL-4、IL-6的mRNA表达下调（P<0.05），纹状体中单胺类神经递质表达上升（P<0.05）。结论:樟芝多糖可以通过下调NLRP3-Caspase1炎性小体表达来改善6-OHDA构建的帕金森小鼠模型行为改善，这可能是樟芝多糖治疗帕金森的机制之一。     

Milk from cows fed a diet with a high forage:concentrate ratio improves inflammatory state,oxidative stress,and mitochondrial function in rats

Excessive energy intake may evoke complex biochemical processes characterized by inflammation, oxidative stress, and impairment of mitochondrial function that represent the main factors underlying noncommunicable diseases. Because cow milk is widely used for human nutrition and in food industry processing, the nutritional quality of milk is of special interest with respect to human health. In our study, we analyzed milk produced by dairy cows fed a diet characterized by a high forage:concentrate ratio (high forage milk, HFM). In view of the low n-6:n-3 ratio and high content of conjugated linoleic acid of HFM, we studied the effects of this milk on lipid metabolism, inflammation, mitochondrial function, and oxidative stress in a rat model. To this end, we supplemented for 4 wk the diet of male Wistar rats with HFM and with an isocaloric amount (82 kJ, 22 mL/d) of milk obtained from cows fed a diet with low forage:concentrate ratio, and analyzed the metabolic parameters of the animals. Our results indicate that HFM may positively affect lipid metabolism, leptin:adiponectin ratio, inflammation, mitochondrial function, and oxidative stress, providing the first evidence of the beneficial effects of HFM on rat metabolism.     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.