Si及变质处理对Mg2Si/Mg复合材料的影响

分析了Mg-Si二元合金直接原位形成Mg2Si/Mg复合材料的过程,研究了Si含量以及变质处理对复合材料组织和性能的影响。试验结果表明,随着合金中Si含量的增加,合金的流动性降低,复合材料中原位Mg2Si的数量增多,树枝晶形态更为发达;对优化的Mg-8Si合金,进行混合稀土(MM)和Sb变质处理,可明显改善Mg2Si的形态和分布,但Sb变质的效果要好于MM。合金经质量分数为1.2%的Sb变质处理后,Mg2Si以颗粒状均匀分布在Mg基体中,从而使复合材料具有较好的耐磨性。     

利用高频磁场制备自生梯度复合材料的熔体温度选择

研究了通过在熔体凝固过程中的不同温度范围施加高频磁场制备自生梯度复合材料的工艺.对于Al/Mg2Si/Si自生梯度复合材料,近似计算及实验结果表明:Al Mg2Si二元共晶区(555～595C)是施加高频磁场的最佳温度范围,此时处于低粘性熔体中的增强颗粒容易被外加电磁阿基米德力分离.高频磁场施加温度过高或过低,均不易使增强颗粒产生梯度分布效果.     

Si_3N_4结合SiC窑具材料抗氧化涂层的研究

本文针对Si_3N_4结合SiC窑具材料在900—1100℃易氧化的特点,研制了该材料的抗氧化涂层,并用试验验证了涂层的抗氧化性能。结果表明:抗氧化涂层的抗氧化效果十分显著,具有很好的推广价值。     

氮化硅结合碳化硅管状制品的研制

简介了氮化硅结合碳化硅管状制品研制的必要性 ,确定了原材料及粒度配比 ,选择了合适的成型方法及添加剂 ,介绍了氮化烧成机理。研制出的制品其质量和使用性能接近同类进口产品 ,具有良好的市场前景和广泛的推广应用价值。     

Si加入量对Si_3N_4-SiC复合材料性能的影响

固定其他组分配比不变,仅改变配方中Si粉加入量即Si粉从10％增加到60％,经过准静态氮化法反应烧结制得Si3N4——SiC复合材料,并对其进行力学性能、XRD和SEM检测,实验结果显示:随着Si加入量的增加,复合材料的强度逐渐增大,而密度却呈现减小趋势,生成的Si3N4-中β-Si3N4含量增加,形成的网络结构的致密度也相应增大,但β-Si3N4晶粒减小。     

表面处理对氮化硅陶瓷力学性能的影响

采用X射线衍射应力分析的sin2ψ法计算了Si3N4陶瓷试样的残余应力，并分别测量了表面处理前后Si3N4试样的力学性能。结果表明，经平面磨削后的Si3N4试样表面残余应力为拉应力，而抛光处理可适当降低残余应力。两种方法都使试样抗弯强度降低。     

Effect of ortho- and pyrophosphates on dissolution of Fe,Al, Si,Ca, and organic C in three soils

Phosphate application changes chemical properties of surface soils, consequently influencing crop nutrient availability and pedological process. Sodium ortho- (OP) or pyrophosphate (PP) was equilibrated with three Quebec soils: an Uplands sand (Orthic-Podzol), a St. Bernard loam (Eutric-Cambisol), and a Dalhousie clay (Humic Gleysol) in 0.03 M KClO₄ solution at an initial pH 6.0. Both autoclaved and nonautoclaved soils were used, and dissolution of Fe, Al, Si, Ca and organic C was studied.Concentrations of Fe and Al in OP equilibrated solutions were not detectable. Ca solubility was reduced while dissolution of Si and organic C was increased in the presence of OP. These changes were possibly due to P—Ca precipitates or increased Ca sorption by P, and competition between OP and Si or organic materials for sorption sites. PP enhanced dissolution of Fe, Al, Si and organic C but reduced solubility of Ca. Comparisons showed that PP added to autoclaved soils had greater effects on increasing dissolutions of Fe, Al, Si and organic C and on reducing Ca solubility than OP in both autoclaved and nonautoclaved soils. Autoclaving resulted in greater dissolution of organic C. Dissolved Si with added OP was greater with nonautoclaved soils probably due to more P sorption in the nonautoclaved system, compared with autoclaved soil. Added PP dissolved Fe and Al ions which may ultimately enhance P precipitation by forming less soluble compounds upon hydrolysis of PP to OP.     

高硅铸铝合金镀前浸锌液

针对高硅铸铝件在组成，组织与性能上的特点，研究了8种高硅铝合金镀前浸锌液。用扫描电镜（SEM）观察了8种不同的浸锌液配方浸锌的试片的表面浸锌膜的微观形貌，测定了浸锌后镀镍层与试片的结合力，优选了能获得良好结合力的最佳浸锌液配方。并研究了随浸锌时间的增加，锌晶核的析出与成长的过程，结果表明，当氢氧化钠140g/L，氧化锌14～20g/L、氯化镍1.5g/L时，试片镀镍后结合力良好。发现浸锌液能够溶解铝合金部分组织，并在铝表面造成孔洞，这种孔洞对镀层起着锚链作用，铝合金表面孔洞的均匀分散以及细小锌晶粒的高度弥散是得到良好结合力的前提。     

无压烧结Al2O3/Si3N4纳米复合陶瓷的力学性能

本文对Al2O3／Si3N4体系进行无压烧结。获得试样相对密度大于98％，采用物相分析，烧结体中并没有Si3N4颗粒存在而是形成SIALON相。Si3N4和Al2O3反应生成的β-SIALON相颗粒不仅分布在Al2O3晶粒晶界处也存在于Al2O3晶粒内部，形成独特的“内晶型”结构。当受到外力时既能诱发穿晶断裂，又能引起裂纹偏转，从而起到增强的作用。由于产生晶界滑移，韧性有所下降。