十二酰胺丙基二甲基羟乙基氯化铵与十二烷基硫酸钠水溶液的表面吸附和胶束形成

利用十二酰胺丙基二甲胺和氯乙醇反应 ,合成了十二酰胺丙基二甲基羟乙基氯化铵 (DDHA)阳离子表面活性剂 ,将其与十二烷基硫酸钠 (SDS)以不同摩尔比进行混合 ,测定了混合系统的表面张力 ,计算了单一系统和混合系统的饱和吸附量、分子最小截面积 ,表面层和胶束中 DDHA的摩尔分率及分子间相互作用参数 ,目视观察了混合系统的浑浊情况。结果表明 :在降低γcmc和 cmc方面 ,DDHA SDS混合系统有协同效应 ,表面层和胶束的组成与二组分配比有关 ,但是非对称的 ,等物质的量混合物中 ,DDHA在胶束和表面层中具有较大的摩尔分数。DDHA与 SDS在实验测定的各混合系统中都不出现混浊     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。     

Continuous precipitation of calcium sulfate dihydrate from waste sulfuric acid and lime

Precipitation of calcium sulfate dihydrate, gypsum, from (i) a pure sulfuric acid/lime suspension and (ii) a waste sulfuric acid/lime suspension in a continuous pilot plant in the temperature range from 40 °C to 80 °C was studied. It was observed that in the case of waste sulfuric acid with a high content of Mg²⁺ and Fe²⁺ ions, several hours after the beginning of the precipitation, partial dissolution of the product and modification of the crystals from needle‐ and plate‐like to agglomerated structures occurred. It is suggested that the secondary changes occur due to the increased concentration of Mg²⁺ and Fe²⁺ ions in the reactor. Below 60 °C, and above 70 °C plate‐like and needle‐like single crystals respectively were formed. The mean size (d₅₀) of the crystals was found to increase with increasing temperature and decrease with the initial concentration of lime. Gypsum produced between 70 °C and 80 °C is suitable for further processing for construction plaster. In a precipitation process with pure sulfuric acid only single perfect needle‐like crystals occurred. Copyright © 2005 Society of Chemical Industry     

Improvement of the deflocculating power of polyacrylates in ceramic slips by small additions of quaternary ammonium salts

In this work, we examine the effect of small additions of cationic quaternary ammonium salts (QAS) of different molecular weight on the rheology of an industrial ceramic suspension deflocculated with sodium polyacrylate and sodium metasilicate. The observed shear thinning behaviors obey the typical power law of fluid rheology. In order to characterize the rheological behavior of these slurries, three new parameters are introduced: a low shear rate consistency index and two transient viscosities, distant from the equilibrium, after increasing and decreasing the shear rates. These parameters vary with polyacrylate molecular weight and on additions of small quantities of QAS, which we found to be useful for decreasing the slurry viscosity.     

延迟破胶及强制裂缝闭合技术的研究及应用

采用延迟破胶技术,在压裂施工过程中加入不同浓度的胶囊破胶剂,利用它的延缓释放特性,使植物胶压裂液耐温、耐剪切稳定性增强,并且可以在不造成压裂液的流变性、滤失性和携砂性等过早丧失的前提下高浓度使用胶囊破胶剂。该技术与常规破胶技术相比,延缓释放率达50%,能更有效地清除液体残渣,减少压裂液对储层的伤害。同时由于有延缓破胶的特性,放喷采用相应的措施,可以降低支撑剂沉降速度,形成较好的沉砂剖面,提供高的裂缝导流能力,并且可以降低滤饼和压裂液残渣的伤害。     

新型香料苹果酯-B的合成

以硫酸高铈为催化剂,通过乙酰乙酸乙酯和1,2-丙二醇反应合成了苹果酯-B,研究了各有关因素对产品收率的影响。实验表明,硫酸高铈是合成苹果酯-B的良好催化剂,在酯醇物质的量比为1∶1.25、催化剂用量为0.3g/0.1mol乙酰乙酸乙酯、环己烷10mL、反应时间2h的条件下,苹果酯-B的收率可达91.5%。     

硫酸钙氨法制取硫酸钾新工艺的实验研究

利用K2 +2 ,Ca2 +/ /SO2 -4 ,Cl2 -2 ,NH3—H2 O混合体系相图作为工艺指导 ,进行硫酸钙制取硫酸钾工艺的相图研究和分析 ,确定实验优选因素及水平并进行正交实验 ,根据实验结果进行极差分析 ,得出新的结论。合适的工艺条件为 :氨浓度为 40 % ,配料比n( 2KCl) :n(CaSO4 ·2H2 O)为 1:1,反应温度为 5℃ ,反应时间为 1h。     

硫酸锆、碳酸锆的性质、应用及生产技术综述

综述了硫酸锆，碳酸锆产品的性质，生产技术及应用，收集整理了国内外部分厂家和公司该产品的化学指标与生产技术；介绍了“分步液相沉淀法”生产工艺，与“一步法”生产工艺相比，其具有流程短，投入少，操作简单，制造成本低等优点。     

SDS/正戊醇/水体系的液晶研究

在 2 5℃测定了十二烷基硫酸钠 (SDS) /正戊醇 /水三元体系的相平衡 ,确定了液晶区域的边界范围。在液晶区域内选取一系列样品点 ,用差示扫描量热法 (DSC)和2 HNMR与液晶照片对照 ,研究了该体系的液晶结构特点。结果表明 :在恒定温度下 ,该体系存在着两个液晶区域 ,并且随含水量的增加 ,液晶结构发生变化。当组成固定时 ,体系的液晶相结构随温度升高也发生变化     

高岭土生产硫酸铝及沉淀法除铁的研究

对工业品硫酸铝的制备及沉淀法除铁的工艺进行了研究。实验结果表明，硫酸原料的质量分数可提高至６３％，用高锰酸钾作为除铁剂可除去产品中４５％～５０％的铁。