La0.6Sr0.4Co0.2Fe0.8O3-δ nanofiber cathode for intermediate-temperature solid oxide fuel cells by water-based sol-gel electrospinning: Synthesis and electrochemical behaviour

Water-based sol-gel electrospinning is employed to manufacture perovskite oxide La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ (LSCF) nanofiber cathodes for intermediate-temperature solid oxide fuel cells. LSCF fibrous scaffolds are synthesized through electrospinning of a sol-gel solution employing water as the only solvent. Morphological characterizations demonstrate that the LSCF fibers have highly crystalline structure with uniform elemental distribution. After heat treatment, the average fiber diameter is 250 nm and the porosity of the nanofiber tissue is 37.5 %. The heat treated LSCF nanofibers are applied directly onto a Ce_0.9Gd_0.1O_1.95 (CGO) electrolyte disk to form a symmetrical cell. Electrochemical characterization is carried out through electrochemical impedance spectroscopy (EIS) in the temperature range 550?°C–950?°C, and reproducibility of the electrochemical performance for a series of cells is demonstrated. At 650?°C, the average measured polarization resistance R_p is 1.0 Ω cm². Measured performance decay is 1 % during the first 33?h of operation at 750?°C, followed by an additional 0.7 % over the subsequent 70?h.     

Synergistic flame retardant effects of activated carbon and molybdenum oxide in poly(vinyl chloride)

The synergistic effects of activated carbon (AC) and molybdenum oxide (MoO₃) in improving the flame retardancy of poly(vinyl chloride) (PVC) were investigated. The effects of AC, MoO₃ and their mixture with a mass ratio of 1:1 on the flame retardancy and smoke suppression properties of PVC were studied using the limiting oxygen index and cone calorimeter tests. It was found that the flame retardancy of the relatively cheaper AC was slightly weaker than that of MoO₃. In addition, the incorporation of AC and MoO₃ greatly reduced the total heat release and improved smoke suppressant property of PVC composites. When the total content of AC and MoO₃ was 10 phr, PVC/AC/MoO₃ had the lowest peak heat release rate and peak smoke production rate values of 173.80 kW m^?2 and 0.1472 m² s^?1, which represented reductions of 47.3 and 59.9%, respectively, compared with those of PVC. Furthermore, thermogravimetric analysis and gel content tests were used to analyze the flame retardant mechanism of AC and MoO₃, with results showing that AC could promote early crosslinking in PVC. Char residue left after heating at 500 °C was analyzed using scanning electron microscopy and Raman spectroscopy, and the results showed that MoO₃ produced the most compact char, with the smallest and most organized carbonaceous microstructures. © 2017 Society of Chemical Industry     

Hierarchical Ni-BDC coated FeOOH nanosheets: A coordination tuning synergistic electrocatalyst with enhanced activity for water oxidation

Hierarchical composites represent a class of efficient electrocatalysts for renewable energy storage and conversion technologies owing to the porous structure and additional exposure of metal sites. Herein, a Ni-based metal organic frameworks (MOFs) (marked as Ni-BDC, BDC stands for 1,4-benzenedicarboxylic acid) nanosheet is successfully fabricated on hydroxyl iron oxide (FeOOH) array with carbon fiber cloth (CFC) as substrate. Benefit from the coordination tuning synergistic effect of the distinct chemical composition and the hierarchical structure for fast mass transportation, the as-obtained FeOOH@Ni-BDC illustrates excellent catalytic ability for electrochemical water oxidation with low overpotential of 270 mV to reach 10 mA/cm² current and good durability in alkaline electrolyte. The novelty of this work lies in the modulation of electronic structure of the FeOOH with Ni-BDC through coordination effect to enhance the activity of the hierarchical composite electrocatalyst. This work is expected to guide the preparation of efficient electrocatalyst for new type alternative energy sources exploitation in near future.     

Enhanced graphitic domains of unreduced graphene oxide and the interplay of hydration behaviour and catalytic activity

Previous studies indicate that the properties of graphene oxide (GO) can be significantly improved by enhancing its graphitic domain size through thermal diffusion and clustering of functional groups. Remarkably, this transition takes place below the decomposition temperature of the functional groups and thus allows fine tuning of graphitic domains without compromising with the functionality of GO. By studying the transformation of GO under mild thermal treatment, we directly observe this size enhancement of graphitic domains from originally ≤40 nm² to >200 nm² through an extensive transmission electron microscopy (TEM) study. Additionally, we confirm the integrity of the functional groups during this process by a comprehensive chemical analysis. A closer look into the process confirms the theoretical predicted relevance for the room temperature stability of GO and the development of the composition of functional groups is explained with reaction pathways from theoretical calculations. We further investigate the influence of enlarged graphitic domains on the hydration behaviour of GO and the catalytic performance of single atom catalysts supported by GO. Additionally, we show that the sheet resistance of GO is reduced by several orders of magnitude during the mild thermal annealing process.     

Enhancement of optical and electrical properties of SILAR deposited ZnO thin films through fluorine doping and vacuum annealing for photovoltaic applications

Undoped and fluorine doped ZnO thin films were deposited onto glass substrates using successive ionic layer adsorption and reaction (SILAR) technique and then annealed at 350 °C in vacuum ambience. The F doping level was varied from 0 to 15 at% in steps of 5 at%. The XRD analysis showed that all the films are polycrystalline with hexagonal wurtzite structure and preferentially oriented along the (002) plane. Crystallite sizes were found to increase when 5 at% of F is doped and then decreased with further doping. It was seen from the SEM images that the doping causes remarkable changes in the surface morphology and the annealing treatment results in well-defined grains with an improvement in the grain size irrespective of doping level. All the films exhibit good transparency (>70%) after vacuum annealing. Electrical resistivity of the film was found to be minimum (1.32×10⁻³ Ω cm) when the fluorine doping level was 5 at%.     

Facile synthesis of Co0.5Zn0.5Fe2O4 nanoparticles decorated reduced graphene oxide hybrid nanocomposites with enhanced electromagnetic wave absorption properties

Herein, reduced graphene oxide/cobalt-zinc ferrite (RGO/Co_0.5Zn_0.5Fe₂O₄) hybrid nanocomposites were fabricated by a facile hydrothermal strategy. Results revealed that the contents of RGO could affect the micromorphology, electromagnetic parameters and electromagnetic wave absorption properties. As the contents of RGO increased in the as-synthesized hybrid nanocomposites, the dispersibility of the particles was improved. Meanwhile, numerously ferromagnetic Co_0.5Zn_0.5Fe₂O₄ particles were evenly anchored on the wrinkled surfaces of flaky RGO. Besides, the obtained hybrid nanocomposites exhibited superior electromagnetic absorption in both X and Ku bands, which was achieved by adjusting the RGO contents and matching thicknesses. Significantly, when the content of RGO was 7.4 wt%, the binary nanocomposites showed the optimal reflection loss of -73.9 dB at a thickness of 2.2 mm and broadest effective absorption bandwidth of 6.0 GHz (12.0–18.0 GHz) at a thin thickness of merely 2.0 mm. The enhanced electromagnetic absorption performance was primarily attributed to the multiple polarization effects, improved conduction loss caused by electron migration, and magnetic loss derived from ferromagnetic Co_0.5Zn_0.5Fe₂O₄ nanoparticles. Our results could provide inspiration for manufacturing graphene-based hybrid nanocomposites as high-efficient electromagnetic wave absorbers.     

Studies on influence of hydrogen and carbon monoxide concentration on reduction progression behavior of molybdenum oxide catalyst

Temperature programmed reduction (TPR) analysis was applied to investigate the chemical reduction progression behavior of molybdenum oxide (MoO₃) catalyst. The composition and morphology of the reduced phases were characterized by X-ray diffraction spectroscopy (XRD), X-ray photoelectron spectroscopy (XPS), and field emission scanning electron microscopy (FE-SEM). The reduction progression of MoO₃ catalyst was attained with different reductant types and concentration (10% H₂/N₂, 10% and 20% CO/N₂ (%, v/v)). Two different modes of reduction process were applied. The first approach of reduction involved non-isothermal mode reduction up to 700 °C, while the second approach of reduction involved the isothermal mode reduction for 60 min at 700 °C. Hydrogen temperature programmed reduction (H₂-TPR) results showed the reduction progression of three-stage reduction of MoO₃ (Mo⁶⁺ → Mo⁵⁺ → Mo⁴⁺ → Mo⁰) with Mo⁵⁺ and Mo⁴⁺. XRD analysis confirmed the formation of Mo₄O₁₁ phase as an intermediate phase followed by MoO₂ phase. After 60 min of isothermal reduction, peaks of metallic molybdenum (Mo) appeared. Whereas, FESEM analysis showed porous crater-like structure on the surface cracks of MoO₂ layer which led to the growth of Mo phase. Meanwhile, the reduction of MoO₃ catalyst in 10% carbon monoxide (CO) showed the formation of unstable intermediate phase of Mo₉O₂₆ at the early stage of reduction. Furthermore, by increasing 20% CO led to the carburization of MoO₂ phase, resulted in the formation of Mo₂C rather than the formation of metallic Mo, as confirmed by XPS analysis. Therefore, the presented study shows that hydrogen gave better reducibility due to smaller molecular size, which contributed to high diffusion rate and achieved deeper penetration into the MoO₃ catalyst compared to carbon monoxide reductant. Hence, the reduction of MoO₃ in carbon monoxide atmosphere promoted the formation of Mo₂C which was in agreement with the thermodynamic assessment.     

The influence of activated carbon as an additive in anode materials for low temperature solid oxide fuel cells

The effects of activated carbon (AC) as an additive in multi-oxide nano composite LiNiCuZn–O for application as anode in solid oxide fuel cell (SOFC) is reported. The composite was synthesized using solid state reactions method with varying content of AC in range 0.1%–0.9% for use as anode in the cell. The cell was composed of the synthesized composite as anode, LiNiCuZn–O as cathode and Samaria doped ceria (SDC) as electrolyte. The prepared composites were characterized for morphology and crystal structure by scanning electron microscope (SEM) and x-ray diffraction (XRD) respectively. Furthermore, the crystallite sizes of LiNiCuZn–O and LiNiCuZn–O with AC as an additive have been found in the range from 50 nm to 70 nm. The prepared composite materials were observed porous and the porosity of the sample having 0.5% additive was found highest. The conductivity and power density of the SOFC were studied at temperature of 600 °C. The maximum value of conductivity was found as 4.79 S/cm for the composite containing 0.5% AC as measured by using 4-probe method. The maximum value of power density of the fuel cell with anode comprising of 0.5% AC along with the mentioned cathode and the electrolyte was 455 mW/cm². Therefore, out of the compositions studied, the composite comprising of LiNiCuZn–O with 0.5% AC offered best performance for anode in the cell. This oxide composite is reported as a potential candidate for use as anode in low temperature SOFCs.     

Al2O3/Yttria‐Stabilized Zirconia Hollow‐Fiber Membrane Incorporated with Iron Oxide for Pb(II) Removal

Removal by absorptive ceramic membranes can simultaneously absorb and separate metal ions from water. Alumina/yttria‐stabilized zirconia (Al₂O₃/YSZ) hollow‐fiber membranes, fabricated using phase inversion and sintering process, were deposited with iron oxide by an in‐situ hydrothermal process. The results showed that α‐Fe₂O₃ was produced and incorporated across the membranes. A reduction in flux was recorded with the deposition of α‐Fe₂O_3. However, it improved the adsorption capacity for heavy metal adsorption. The adsorption‐separation test demonstrated that the optimized membrane is able to completely remove Pb(II) ions after two hours.     

Nanocrystalline transition metal oxides and their composites with reduced graphene oxide and carbon nanotubes for photocatalytic applications

Transition metal oxide nanoparticles (CuO, ZnO & Fe₂O₃) and mixed metal oxides CuO. ZnO.Fe₂O₃ were fabricated by facile co-precipitation approach for photocatalytic treatment of organic dyes. The structural features, phase purity, crystallite size and morphology of individual and mixed metal oxides were analysed by X-rays diffraction patterns (XRD) and scanning electron microscopic (SEM) analysis. Electrical behaviour of CuO, ZnO, Fe₂O₃ and mixed metal oxides CuO. ZnO.Fe₂O₃ was explored by current-voltage (I-V) measurements. Functional groups present in the synthesized metal oxides were investigated by Fourier transform infrared spectroscopy (FTIR) which ensures the existence of M-O functional groups in the samples. The optical bandgap analysis was carried out by UV–visible spectroscopic technique which revealed that the blend of three different transition metal oxides reduced the bandgap energy of mixed metal oxides. The reason behind this reduced bandgap energy is formation of new electronic state which arises due to the metal-oxygen interactions. Moreover, the nanocomposites of CuO.ZnO.Fe₂O₃ with reduced graphene oxide (rGO) and carbon nanotubes (CNTs) were prepared to study the effect of the carbonaceous materials on the rate of photodegradation. These carbonaceous nanomaterials have plethora properties which can bring advancement in sector of photocatalytic treatment of wastewater. The photocatalytic experiments were performed using methylene blue (MB) as standard dye for comparative study of metal oxides and their composites with rGO and CNTs. The percentage degradation of methylene blue (MB) by nanocomposite CuO.ZnO.Fe₂O₃/rGO is 87% which is prominent among all samples. This result ascribed the photocatalytic aspects of reduced graphene oxide along with mixed metal oxides.