Low Electrical Percolation Threshold of Silver and Copper Nanowires in Polystyrene Composites

Silver and copper nanowires have been synthesized using a scalable method of AC electrodeposition into porous aluminum oxide templates, which produces gram quantities of metal nanowires ca. 25 nm in diameter and up to 5 and 10 μm in length for Ag and Cu, respectively. The nanowires have been used to prepare polystyrene nanocomposites by solution processing. Electrical resistivity measurements performed on polymer nanocomposites containing different volume fractions of metal indicate that low percolation thresholds of nanowires are attained between compositions of 0.25 and 0.75 vol %.     

Evolution of grain structure in thin film reactions

In this paper, we examine, both experimentally and theoretically, the kinetics of formation and microstructure of product phases in thin film reactions, using the Nb/Al and Ti/Al systems as our prototypes. The results of calorimetry and microscopy studies are interpreted using simple kinetic and morphology models. In particular, the kinetic models employed here focus on the nucleation and growth components of the phase formation process and the morphology models provide a starting point for the classification of product grain structures. An erratum to this article is available at .     

Nonlinear electrical transport in K-TCNQ at low temperatures

A remarkable nonlinearity has been observed for electric transport in K-TCNQ (potassium tetracyanoquinodimethane) quasi-one-dimensional conductor. The negative differential resistance region appears afterV _m (turn over voltage), beyond which voltage goes down with increase of current. A possible mechanism is discussed in terms of dynamics of charged solitons and domain walls in one-dimensional molecular stacks of these types of crystals.     

β″－Al_2O_3陶瓷的强化和韧化

研究了稳定ＺｒＯ＿２和部份稳定ＺｒＯ＿２对β″－Ａｌ＿２Ｏ＿３陶瓷的强化和韧化作用，观察了不同种类、不同含量的ＺｒＯ＿２对β″－Ａｌ＿２Ｏ＿３陶瓷的显微结构、力学性能和电导率的影响，探讨了β″－Ａｌ＿２Ｏ＿３的韧化机理。     

TiAl基合金表面改性对高温抗氧化性的影响

研究了渗碳处理ＴｉＡｌ基合金试样的高温氧化行为，发现渗碳处理可以在ＴｉＡｌ基合金试样表层形成致密的多层结构的渗碳层，并发生表层Ａｌ、Ｔｉ重新分配。致密的渗碳层具有良好的高温抗氧化性和高温热稳定性，同时，Ｔｉ、Ａｌ重新分配形成的富Ａｌ最外层也能进一步提高合金的抗氧化性。     

WC对Cu/WC_P复合材料性能及组织的影响

通过ＷＣ含量对ＷＣ／Ｃｕ复合材料性能的影响，确定了冷压－烧结法制备Ｃｕ／ＷＣ材料的适宜ＷＣ含量为１０ｖｏｌ％左右。并就ＷＣ对该材料组织和再结晶行为的影响进行了有益的探讨。     

Stabilization of inter-area and/or oscillatory modes in large-scale power system by voltage impedance power system (VIPS) apparatus based on decentralized control scheme

New technologies such as power electronics have made it possible to change continuously the impedance of a power system not only to control power flow but also to enhance stability. A power system incorporating a variable impedance apparatus such as a variable series capacitor (VSrC) and high-speed phase shifter (HSPS) is called VIPS (Variable Impedance Power System) by the authors. This paper proposes a novel control method of VIPS apparatus such as VSrC and HSPS installed at an interconnecting point for stabilizing inter-area unstable and/or oscillatory modes. The proposed design method of the control system is a kind of hierarchical decentralized control method of a large-scale power system based on a Lyapunov function. Under the proposed control scheme, each subsystem can be stabilized independently by local controllers such as AVR, speed governor and PSS, and then the whole interconnected system can be stabilized by VIPS apparatus taking into account interactions between subsystems. The effectiveness and robustness of the VIPS apparatus control are shown by numerical examples with model systems including a large-scale power system.     

Mechanical degradation of coating systems in high temperature cyclic oxidation

Cyclic oxidation tests were performed on a large variety of commercially available overlay coatings. The results of cyclic oxidation tests confirmed that the composition of the coating as well as the processing method of the coating can affect the life of the system. Coating life was determined by the time to coating penetration and initiation of substrate attack. As this work was part of a effort to evaluate the relative protectiveness of available coating systems for Industrial Gas Turbine applications at relatively high temperature, an extensive testing programme was undertaken. The different coatings were tested to visual failure. The results presented in this paper concentrate on the surface instability of the coating. Apart from usual oxidation of the coating an additional degradation mechanism was observed. A mechanical effect caused by the instability of the coating as a result of the difference in the thermal coefficient of expansion and mechanical properties between the substrate and coating. This effect, the so-called “rumpling” effect, resulted in a significant reduction in time to penetration and was in some systems the life controlling factor.     

Corrosion fatigue short crack growth behaviour in a high strength steel

The influence of an aggressive environment (0.6 M, aerated NaCl solution) on short fatigue crack initiation and growth behaviour has been studied. The study involved three major test series, namely: air fatigue, corrosion fatigue, and intermittent air fatigue/corrosion fatigue. The above tests carried out under fully reversed torsional loading conditions at a frequency of 5 Hz, showed that it was the non-metallic inclusions which took part in crack initiation resulting from debonding at metal matrix/inclusion interface and pitting of inclusions in both air and corrosove environments, respectively. Short fatigue crack growth results in these two environments obtained by using plastic replication technique, indicated a large effect of microstructure i.e. prior austenite grain boundaries. The stage/stages at which the environmental contribution was dominant has been discussed by considering the results achieved from intermittent tests. However, the mechanisms involved in corrosion fatigue short crack growth have also been described in the light of results obtained from futher investigations carried out by conducting corrosion fatigue tests under applied cathodic potential conditions and tests on hydrogen pre-charged specimens under air fatigue and uniaxial tension conditions.     

变形温度和变形程度对Ti－31合金性能和组织的影响

通过高温和室温拉伸试验，研究了变形温度和变形程度对Ｔｉ－３１合金板材性能和组织的影响。结果表明，合金在７５０～８５０℃的温度下变形５％～２０％空冷后，其室温机械性能均能达到材料的技术指标要求。并发现了材料在９００℃的临界变形区。