三元复合驱注入剖面测井初探

三元复合驱技术是在聚合物驱油技术基础上开展的进一步提高原油采收率的高科技手段，三元混合液在注入水中加入了一定量的聚合物，碱和表面活性剂，可以提高驱油效率，扩大波及体积，其注入液的主要特点是具有非牛顿性及强腐蚀性，据此设计了一套注入剖面测井仪，且仪器和电缆的选用须适应这两个特点，选用磁性定位器，井温仪，压力仪，电磁流量计多参数组合测井可以较好地解释三元复合驱注入剖面的测井问题，多参数组合测井综合解释可以提供更多，更好的资料和信息，现场试验证明了其仪器及技术方案的可行性，对今后将会出现的分层配注井也提出了测井方案。     

高纯硼烷中杂质的低温气相色谱分析

用低温色谱法解决硼烷的分解问题，使硼烷中氢的分析成为可能，该法又能消除硼烷和四硼烷（B4H10)对氧、氮和甲烷峰测定的干扰，此方法的建立使硼烷的标准制定成为可能。     

应用德国PAR88挤出机生产PVC异型材的工艺研究

从控制PVC异型材挤出机的工艺参数的角度，分析并论述了挤出机工艺参数对PVC异型材低温落锤性能的影响。     

Measurement of Thermal Diffusivity at Low Temperatures Using an Optical Reflectivity Technique

An experimental arrangement has been developed for measuring the transient temperature responses and the thermal diffusivities of foil materials in the range of 10 to 300K by using the optical reflectivity technique. The cryogenic system with optical windows is designed to provide temperatures from 10 to 300 K. The front surface of a foil specimen is heated by a pulsed Nd:YAG laser. In situ measurement of the reflectivity of a continuous-wave He–Ne laser at the rear surface is conducted on the microsecond time scale. Using the temperature dependence of reflectivity, the transient temperature response is deduced. The thermal diffusivity is obtained by fitting Parker's formulae to the experimental data on temperature rise. Stainless-steel foils are chosen as samples and are studied in the region from 10 to 300 K. The accuracy is examined by comparing the present results with the theoretical temperature responses and thermal diffusivity data from the literature. Good agreement is observed.     

钢筋混凝土圆形水池裂缝分析与处理

本文针对某钢筋混凝土圆形水池在使用过程中出现的裂缝进行计算和分析，讨论了温度对水池的影响，特别是考虑储水区与非储水区存在温差的条件对水池池壁裂缝的影响，并提出处理方案。     

测定钠中杂质的手动阻塞计的研究

文章介绍了测定钠中杂质浓度的手动阻塞计的原理、装置和实验结果。为了减少测量误差,我们研究了影响准确测定阻塞温度的因素,并且找到了减少测量误差的办法。在同样的杂质饱和温度下,该阻塞计测得的高、低阻塞温度所对应的杂质浓度差是很接近的。对氧其差值为1.03ppm;对氢为0.0763ppm。     

SO2转化温度异常情况分析

结合凤山实业总公司硫酸车间 SO2 转化系统的具体工艺流程 ,分析近几年转化系统出现温度不正常的原因 ,提出解决方法     

High temperature controlled atmosphere experiments for catalysts in a transmission electron microscope

A new transmission electron microscopy (TEM) specimen preparation procedure for high temperature experiments using a controlled atmosphere specimen holder (HTCASH) has been developed. It is designed for studying the microstructure of catalyst specimens before and after treatments in various gases. The procedure involved (1) finding a new formula for the embedding material, (2) devising a new method of making specimen supports, and (3) developing a method for removing the embedding material after the specimen has been microtomed. These techniques were then brought together to produce the ideal specimens for the HTCASH experiments. As an extra benefit, this procedure is also suitable for preparing specimens for ultrahigh resolution imaging experiments. The application of the new procedure in HTCASH experiments is illustrated through a high temperature reduction of a Co/SiO₂-923 catalyst.     

白钨矿浮选731捕收剂低温乳化试验研究

介绍了731捕收剂在低温条件下试验的情况。试验研究结果表明，采用A和B药剂以5：6的比例混合组成的复合乳化剂对731进行乳化，低温时乳化体系稳定性好，浮选过程中降低乳化731的用量，同时提高了选择性，降低了浮选成本，实现了低温环境下白钨矿正常浮选作业，达到选矿技术攻关指标。     

Corrosion behaviour of low-Si alloyed steels in neutral reducing conditions at 90 °C

Electrochemical investigations on low-Si alloyed steels with Si content ranging from 0.25 to 3.2 wt.% were carried out in a 0.1 M NaCl borate-buffered solution (pH 8.4) in reducing conditions at 90 °C. Silicon as an alloying element was proved to degrade at first the steel ability to passivate. For longer immersion times, protective effects developed more efficiently on the steel containing 3.2 wt.% silicon. Passive layers electrochemically formed in the transpassive domain on the steel containing 3.2% Si were shown to be significantly different from those grown at rest potential.