On the curing of a vinylester-urethane hybrid resin

Curing kinetics of a vinylester-urethane hybrid (VEUH) resin consisting of vinylester resin (VE) diluted in styrene and novolac type polyisocyanate (NPI) have been studied by differential scanning calorimetry (DSC). As VEUH is crosslinked via free radical polymerisation between the vinyl functions of styrene and VE, and polyaddition reaction between the secondary -OH groups of VE and -NCO of NPI, it was necessary to study these reactions separately. This was achieved by studying the curing with and without incorporating the NPI. The curing reaction was monitored by measuring the heat of reaction under isothermal and dynamic temperature conditions. Models describing the curing were developed, which are in good agreement with the experiments. A comparison between the curing of the VEUH and the VE resin without NPI leads to the conclusion that the curing of the VEUH as accessed by DSC is dominated by the radical polymerisation of styrene with VE although the two reactions are not time separated.     

新型难燃输送带胶粘剂的研制

以改性氯丁橡胶为主料、多异氰酸酯为固化剂制成的新型难燃输送带胶粘剂,具有粘接强度高、耐热性好、干燥时间短、难燃等特点,在常温常压下粘接输送带接头,固化30min即可负荷运行。     

Development of sealing compositions with nanostructure iron-based fillers

The possibility of utilizing nanopowders of iron and Fe-Co-Ni produced bu a thermochemical method in the fabrication of sealing composition materials is investigated. It is established that such hermetic sealing composition materials function reliably under extremal conditions and guarantee elevated strength of adhesion to the surface of the metal and high corrosion and temperature stability. __________ Translated from Poroshkaya Metallurgiya, Nos. 3–4(448), pp. 112–117, March–April, 2006.     

MBS树脂改性PVC的研究

研究了不同类型及用量的MBS树脂对PVC抗冲击性、光学性能、拉伸性能及加工塑化性能的改性效果以及加工条件等因素的影响。结果表明 :在低用量条件下 ,随MBS树脂含量增加 ,MBS/PVC抗冲击性能有所提高 ,光学性能略有下降。此外 ,MBS/PVC制品的拉伸性能和加工性能受MBS树脂类型及用量影响不大。     

水乳型丙烯酸酯建筑防水胶的研制(Ⅱ)

摘 要 研究水乳型丙烯酸酯建筑防水胶与水泥的配比及共混性能、共混固化物胶膜的力学性能、耐冷热性能及老化性能。     

异丁烷与丁烯在炭化树脂负载PW_(12)催化剂上的烷基化

探讨了炭化树脂负载杂多酸PW1 2 催化剂制备的适宜条件 ,反应工艺条件对催化剂催化异丁烷与丁烯烷基化反应及产物分布的影响 ,分析了催化剂具有较高活性的原因 ,进行了催化剂稳定性实验。并与其它类固体酸催化剂进行了对比。     

耐高温绝缘GFRP管的真空辅助树脂传递成型工艺研究

阐述了耐高温绝缘GFRP管的成型工艺及原材料选择，并对影响成型工艺的主要因素作了理论分析及试验验证。研究表明，以TDE－85／DDS体系为为基体，以无碱无捻玻璃纤维方格布为增强材料，用VARTM工艺成型的石油勘探高性能平衡管完全满足技术要求。     

瓦楞纸板用抗水淀粉胶配方及性能研究

简要分析了玉米淀粉胶的组成及对其质量的影响，重点对粘合剂的防水性进行了研究，叙述了瓦楞纸板用抗水粘合剂的配制及工艺过程，并与常规方法制备的粘合剂进行了性能比较，测定了抗水时间，得出了瓦楞纸板用抗水粘合剂的最佳配制比例。     

硫脲型整合树脂在分析上的应用 Ⅰ.岩样中微量银的中子活化分析

前言银和其他贵金属元素一样,在地壳中比较稀少,按其自然丰度为第67号元素,平均含量仅0.07 ppm。由于地质样品成分非常复杂,为测定其微量银,必须进行严格的化学分离。但是迄今文献中报道的许多分离分法,步骤都相当冗长,一般采用氯化银反     

苯基荧光酮分光光度法测定聚烯烃树脂中的钛

应用苯基荧光酮 -聚乙烯醇 -Tween -80显色体系测定了聚烯烃树脂中的钛 ,建立了测定聚烯烃树脂中钛离子的灵敏、快速的分析方法。考察了测定条件 ,在测定过程中 ,以抗坏血酸还原作用消除了Fe3+ 、V5+ 等干扰。配合物最大吸收波长为 5 3 5nm ,其表观摩尔吸光系数ε =1 0× 10 5L/ (mol·cm) ,线性范围为 0～ 0 12 μg/ml。合成试样回收率为 97 3 %～ 10 1% ,相对标准偏差不大于 1 63 % ;加标回收率为 99 95 %～ 10 1 3 % ,该方法选择性高 ,准确性好 ,简便易行