Probing the early stages of polymerization of ethylene on a model chromium/silica catalyst by Fourier transform infrared spectroscopy

The nature of the interaction of monomer, and the early stages of growth of oligomers of ethylene on a rather more uniform surface of Cr/SiO₂ catalyst than hitherto studied has been investigated by differenceFTIR spectroscopy using C₂D₄ and C₂H₄ as reactants both with and without subsequent treatment of the catalyst with CO andTHF. The active catalyst was prepared by reaction of vapour phase CrO₂Cl₂ with the vicinal hydroxyls of the silica surface. Three distinct kinds of methylene groups were detected. Arguments are given for assigning the peaks at 2935 and 2860 cm^–1 to CH₂ groups directly bound to the active site and those at 2920 and 2850 to CH₂s in the growing chain well removed from the Cr. The peaks at 2160 and 2165 cm^–1 are attributed to CD₂ groups hydrogen bonded to surface hydroxyls.     

尖晶石型纳米钴蓝陶瓷颜料的制备

采用化学共沉淀法作为钴蓝颜料的制备方法,探讨了主要工艺因素对制备钴蓝颜料性能的影响,对制备的样品进行了测试与表征。结果表明:Co2+和Al3+物质的量比为1∶2.5时,制备的钴蓝样品颜色饱和度与明度最高,沉淀剂为尿素时制得的样品的粒度最小,粒度分布比较均匀。前驱体的洗涤过程采取水洗加醇洗的方法可有效减少样品的硬团聚现象,且前驱体的最佳煅烧温度为950℃左右。     

利用SiO2包膜技术提高群青蓝颜料耐酸性的研究

采用廉价的SiO2 对群青颜料进行致密包膜 ,使群青颜料耐酸性能得到提高 ,解决了群青在聚氯乙烯型材使用中产生的变色现象 ,拓宽了应用范围     

新型蓝绿发光材料ZnSe／BeTe超晶格的能带剪裁

由于器件的快速退化，101.5小时似乎成了Znse基蓝绿色半导体激光器难于逾越的寿命极限。分析退化机制，发现在强电流注入的半导体激光器中，热退化具有重要影响。研究表明，用作载流子限制层的宽带Ⅱ-Ⅵ族四元合金（如ZnMgSSe）只能对ZnSe中的电子有效地限制，无法对空穴很好地限制;而对BeTe，却只能对空穴进行有效的限制，无法对电子很好地限制。这导致ZnSe（或BeTe）活性层空穴（或电子）漏电发热，引起退化。本文提出以ZnSe／BeTe超晶格为蓝绿发光层，并用包络函数理论具体计算了阱宽、垒宽对载流子能级的不同影响，考察了ZnSe、BeTe厚度比和超晶格周期对带隙、载流子限制能力的调节。为研制新型长寿命蓝绿色半导体激光器提供了一条新的途径。     

直读光度法测定钼铁中的硅

试样经草酸、双氧水分解后，以盐酸羟胺破坏掉多余双氧水。以标准样品作参比，在硫酸－柠檬酸介质中，用钼酸铵显色，抗坏血酸还原，生成稳定的硅钼蓝。此方法可测定１．０％以下的硅，具有快速、准确、灵敏度高等优点。     

模块化蓝光光存储性能静态测试系统

蓝光光存储是信息存储领域发展的一个重要方向。测试系统是研究蓝光光存储材料的必备条件，为建立蓝光光存储研究平台，设计和搭建了一套模块化蓝光光存储性能静态测试系统。激光工作波长为406．7nm。系统采用调制解调技术降低系统噪声，提高测量粘度：采用光点移动模式降低对样品尺寸的要求；采用纳米平台提高记录点的反复定位性能。实验结果证明测试系统性能良好，可以满足蓝光光存储性能静态测试要求。     

图像半色调化算法研究综述

半色调化算法是图像打印输出的关键技术之一。介绍了简单阈值比较算法、使用随机数的半色调化算法、误差扩散算法、点扩散算法、按序抖动算法和抖动算法等一系列半色调化算法,并揭示了这些算法之间的联系。为了高效率地对图像做半色调化操作,商用光栅图像处理器一般使用抖动算法。抖动算法生成的半色调化图像的质量取决于所采用的抖动矩阵。基于几何分割设计半色调化抖动矩阵的方法可以在满足堆栈限制的前提下优化半色调化图像的质量。使用随机数的半色调化算法可以消除图像半色调化中产生的莫尔纹。随机半色调化算法的基础是将一定数量的随机点均匀地分布到一个正方形区域中。Asano提出了随机点均匀分布问题等价于圆形装填问题的命题,本文对该命题给出了初步的证明。最后,给出了一些有待进一步研究的图像半色调化课题。     

3D Prussian blue/Pt decorated carbon nanofibers based screen-printed microchips for the ultrasensitive hydroquinone biosensing

Nowadays,water pollution has become more serious,greatly affecting human life and healthy.Electrochemical biosensor,a novel and rapid detection technique,plays an important role in the real-time and trace detection of water pollutants.However,the stability and sensitivity of electrochemical biosensors remain a great challenge for practical detections in real samples to the strong interferences derived from complex components and coagulation effects.In this work,we reported a novel three-dimensional architecture of Prussian blue nanoparticles (PBNPs)/ Pt nanoparticles (PtNPs) composite film,using 3D interweaved carbon nanofibers as a supporting matrix,for the construction of screen-printed microchips-based biosensor.PtNPs with diameters of～2.5 nm was highly dispersed on the carbon nanofibers (CNFs) to build a 3D skeleton nanostructure through a solvothermal reduction.Subsequently,uniform PBNPs were in-situ self-assembled on this skeleton to construct a 3D architecture of PB/Pt-CNF composite film.Due to the synergistic effects derived from this special feature,the as-prepared hydro-quinone (HQ) biosensor chips can synchronously promote both surface area and conductivity to greatly enhance the electrocatalysis from enzymatic reaction.This biosensor has exhibited a high sensitivity of 220.28 μA·L·mmol-1·cm-2 with an ultrawide linear range from 2.5μmol·L-1 to 1.45 mmol·L-1 at a low potential of 0.15 V,as well as the satisfactory reproducibility and usage stability.Besides,its accuracy was also verified in the assays of real water samples.It is highly expected that the 3D PB/Pt-CNF based screen-printed microchips will have wide applications in dynamic monitoring and early warning of ana-lytes in the various practical fields.     

不同晶型纳米二氧化锰制备及对亚甲基蓝吸附性能

以高锰酸钾（KMnO₄）为氧化剂、硫酸亚铁铵[（NH₄）₂Fe（SO₄）₂]为还原剂,用水热氧化还原反应制备了层状δ-二氧化锰和隧道型α-二氧化锰纳米材料。用X射线衍射（XRD）、扫描电镜（SEM）和氮气吸-脱附技术对产物的晶型、形貌及孔结构进行了表征。实验结果表明,δ-二氧化锰呈花状微球形貌,具有介孔结构（平均孔径为3.4 nm）,BET比表面积为219 m²/g;α-二氧化锰呈纳米线束形貌,具有部分介孔结构（平均孔径为35.7 nm和154.6 nm）,BET比表面积为26 m²/g。研究了不同晶型纳米二氧化锰对亚甲基蓝的吸附性能。实验结果表明,在相同条件下α-二氧化锰的吸附性能优于δ-二氧化锰,且在碱性环境下吸附效果较好。当反应时间达到120 min时,α-二氧化锰和δ-二氧化锰对亚甲基蓝的去除率分别为84.4%和82.9%。     

兰炭和天然气在独立热源矿粉企业应用对比

随着国家环保治理的不断深入,很多拥有工业锅炉和窑炉的企业被要求煤改气。我公司作为一家使用独立烘干热源的矿粉企业,2018~2020年间,在当地政府环保部门的要求下完成了两台沸腾炉的煤改气工作。改造完成后,使用天然气作为燃料能够保证矿粉企业的稳定供热需求;在热能利用率上比使用兰炭更高,能够节能15%以上;同时在使用先进的燃烧技术和合理控制燃烧温度的情况下,在矿粉企业使用天然气作为燃料,可以满足河北省《水泥工业大气污染物超低排放标准》DB13/2167—2020排放要求。